We use cookies to distinguish you from other users and to provide you with a better experience on our websites. Close this message to accept cookies or find out how to manage your cookie settings.
To save content items to your account,
please confirm that you agree to abide by our usage policies.
If this is the first time you use this feature, you will be asked to authorise Cambridge Core to connect with your account.
Find out more about saving content to .
To save content items to your Kindle, first ensure no-reply@cambridge.org
is added to your Approved Personal Document E-mail List under your Personal Document Settings
on the Manage Your Content and Devices page of your Amazon account. Then enter the ‘name’ part
of your Kindle email address below.
Find out more about saving to your Kindle.
Note you can select to save to either the @free.kindle.com or @kindle.com variations.
‘@free.kindle.com’ emails are free but can only be saved to your device when it is connected to wi-fi.
‘@kindle.com’ emails can be delivered even when you are not connected to wi-fi, but note that service fees apply.
A new process route for lateral growth of nearly defect free GaN structures via Pendeo-epitaxy is discussed. Lateral growth of GaN films suspended from {110} side walls of [0001] oriented GaN columns into and over adjacent etched wells has been achieved via MOVPE technique without the use of, or contact with, a supporting mask or substrate. Pendeo-epitaxy is proposed as the descriptive term for this growth technique. Selective growth was achieved using process parameters that promote lateral growth of the {110} planes of GaN and disallow nucleation of this phase on the exposed SiC substrate. Thus, the selectivity is provided by tailoring the shape of the underlying GaN layer itself consisting of a sequence of alternating trenches and columns, instead of selective growth through openings in SiO2 or SiNx mask, as in the conventional lateral epitaxial overgrowth (LEO).
Two modes of initiation of the pendeo-epitaxial GaN growth via MOVPE were observed: Mode A - promoting the lateral growth of the {110} side facets into the wells faster than the vertical growth of the (0001) top facets; and Mode B - enabling the top (0001) faces to grow initially faster followed by the pendeo-epitaxial growth over the wells from the newly formed {110} side facets. Four-to-five order decrease in the dislocation density was observed via transmission electron microscopy (TEM) in the pendeo-epitaxial GaN relative to that in the GaN columns. TEM observations revealed that in pendeo-epitaxial GaN films the dislocations do not propagate laterally from the GaN columns when the structure grows laterally from the sidewalls into and over the trenches. Scanning electron microscopy (SEM) studies revealed that the coalesced regions are either defect-free or sometimes exhibit voids. Above these voids the PEGaN layer is usually defect free.
A new process route for lateral growth of nearly defect free GaN structures via Pendeoepitaxy is discussed. Lateral growth of GaN films suspended from {1120} side walls of [0001] oriented GaN columns into and over adjacent etched wells has been achieved via MOVPE technique without the use of, or contact with, a supporting mask or substrate. Pendeo-epitaxy is proposed as the descriptive term for this growth technique. Selective growth was achieved using process parameters that promote lateral growth of the { 1120) planes of GaN and disallow nucleation of this phase on the exposed SiC substrate. Thus, the selectivity is provided by tailoring the shape of the underlying GaN layer itself consisting of a sequence of alternating trenches and columns, instead of selective growth through openings in SiO2 or SiNx mask, as in the conventional lateral epitaxial overgrowth (LEO).
Two modes of initiation of the pendeo-epitaxial GaN growth via MOVPE were observed: Mode A - promoting the lateral growth of the {1120} side facets into the wells faster than the vertical growth of the (0001) top facets; and Mode B - enabling the top (0001) faces to grow initially faster followed by the pendeo-epitaxial growth over the wells from the newly formed {1120} side facets. Four-to-five order decrease in the dislocation density was observed via transmission electron microscopy (TEM) in the pendeo-epitaxial GaN relative to that in the GaN columns. TEM observations revealed that in pendeo-epitaxial GaN films the dislocations do not propagate laterally from the GaN columns when the structure grows laterally from the sidewalls into and over the trenches. Scanning electron microscopy (SEM) studies revealed that the coalesced regions are either defect-free or sometimes exhibit voids. Above these voids the PEGaN layer is usually defect free.