To save content items to your account,
please confirm that you agree to abide by our usage policies.
If this is the first time you use this feature, you will be asked to authorise Cambridge Core to connect with your account.
Find out more about saving content to .
To save content items to your Kindle, first ensure email@example.com
is added to your Approved Personal Document E-mail List under your Personal Document Settings
on the Manage Your Content and Devices page of your Amazon account. Then enter the ‘name’ part
of your Kindle email address below.
Find out more about saving to your Kindle.
Note you can select to save to either the @free.kindle.com or @kindle.com variations.
‘@free.kindle.com’ emails are free but can only be saved to your device when it is connected to wi-fi.
‘@kindle.com’ emails can be delivered even when you are not connected to wi-fi, but note that service fees apply.
Cementitious material is the most commonly used encapsulation medium for low and intermediate level radioactive waste. This paper focuses on the aqueous durability of a Materials Testing Reactor (MTR) cementitious wasteform – a possible candidate for the proposed intermediate level waste management facility in Australia. A series of medium term (up to 92 months) durability tests, without leachate replacement, were conducted on samples of this wasteform.
The wasteform was made from cement, ground granulated blast furnace slag and a simulated waste liquor. The compressive strength (39 MPa) was typical of MTR cement wasteforms and well above that required for handling or storage. The wasteform was an inhomogeneous mixture containing calcite, a calcium silicate hydrate phase, hydrotalcite and unreacted slag particles. After leaching for 92 months the crystallinity of the calcium silicate hydrate phase increased.
The majority of the releases of Ca, Si, Al, Sr, S, Na and K was reached within 4 days of leaching, with the maxima ie. the highest concentrations in the leachates, occurring at 3 months for Ca, Al, Sr, S, Na and K, and at 1 month for Si. For the longer leach periods (6 months and 3 months respectively) there was a slight reduction in concentration in the leachates, and these levels were similar to those for the longest period of 92 months, suggesting steady-state conditions prevailing after 3 to 6 months of leaching. The highest releases of matrix elements were for Na (37%), K (40%) and S (16%). Releases for elements such as Ca, Na, Al and Sr were similar in magnitude to those reported by the UKAEA in earlier MTR studies.
After leaching for 92 months there was an alteration layer about 80 ∞m deep where calcium has been depleted. Na, K and Sr showed signs of diffusion towards the outer part of the cement samples.