Strong piezoelectric effects in unstrained GaN quantum wells

Published online by Cambridge University Press:  13 June 2014

R. Langer
Affiliation:
Département de Recherche Fondamentale sur la Matière Condensée, CEA/Grenoble, SP2M/PSC, 38054 Grenoble, Cedex 9, France
J. Simon
Affiliation:
Département de Recherche Fondamentale sur la Matière Condensée, CEA/Grenoble, SP2M/PSC, 38054 Grenoble, Cedex 9, France
O. Konovalov
Affiliation:
Département de Recherche Fondamentale sur la Matière Condensée, CEA/Grenoble, SP2M/PSC, 38054 Grenoble, Cedex 9, France
N.T. Pelekanos
Affiliation:
Département de Recherche Fondamentale sur la Matière Condensée, CEA/Grenoble, SP2M/PSC, 38054 Grenoble, Cedex 9, France
R. André
Affiliation:
Laboratoire de Spectrométrie Physique, CNRS, Université J. Fourier, 38402 Saint Martin d’Hères, France
A. Barski
Affiliation:
Département de Recherche Fondamentale sur la Matière Condensée, CEA/Grenoble, SP2M/PSC, 38054 Grenoble, Cedex 9, France
M. Godlewski
Affiliation:
Institute of Physics, Polish Academy of Sciences, 02-668 Warsaw, Al. Lotnikow 32/46 Poland

Abstract

Optical properties of GaN/AlGaN single quantum well (SQW) and multi quantum well (MQW) structures grown by nitrogen plasma assisted MBE on MOCVD-grown GaN/sapphire have been characterised by low temperature photoluminescence. Photoluminescence (PL) peaks corresponding to emission from very narrow (10 Å wide) SQWs are blue shifted with respect to the bulk GaN emissions but reveal strong red shift for wider SQWs (40 and 60 Å wide). Structural properties of SQW and MQW structures have been characterised by X-ray reciprocal lattice mapping in order to determine the strain conditions and composition of ternary AlGaN alloys. The results clearly demonstrate that in all structures under investigation the ternary (barrier) alloys are fully strained to underlying MOCVD-grown GaN/sapphire substrates. Despite of the fact that GaN quantum wells (QW) are unstrained, photoluminescence experiments clearly reveal the presence of extremely strong electric fields in the QW regions, which can be attributed to the interplay of the piezoelectric-type polarisation in the well and barrier layers due to Fermi level alignment.

Type
Research Article
Copyright
Copyright © 1999 Materials Research Society

Introduction

GaN/AlGaN QWs are subject of intense investigations due to their potential for electronic and opto-electronic applications. Many recent publications report on the properties of GaN/AlN and GaN/AlGaN heterostructures, superlattices and/or multi QW structures [Reference Im, Kollmer, Off, Sohmer, Scholz and Hangleiter1,Reference Korakakis, Ludwig and Moustakas2,Reference Zeng, Lin, Jiang, Salvador, Popovici, Tang, Kim and Morkoc3,Reference Johnson, Shizuo Fujita, Rowland, Bowers, Hughes, He, El-Masry, Cook, Schetzina, Ren and Edmond4]. Recently, a strong piezoelectric field has been found in GaN/AlGaN heterostructures with strained QW regions which was attributed to strain induced phenomena [Reference Im, Kollmer, Off, Sohmer, Scholz and Hangleiter1]. We report here the results on GaN/AlGaN SQW and MQW structures grown by Radio Frequency Molecular Beam Epitaxy (RFMBE) on MOCVD-grown GaN/sapphire. In order to demonstrate that the strong electric field is present in unstrained quantum wells, the total thickness of AlGaN barriers in all our samples was kept below the critical thickness and hence the AlGaN layers are strained. Our structures are pseudomorphic with the GaN/sapphire substrate and the GaN QW’s are strain free.

Experimental

The GaN/AlGaN SQW structures studied have a single GaN QW of 10 and 40 Å thickness embedded between 1000 Å thick AlGaN barriers. The Al fraction in the barriers was about 17-20 %, as determined independently from PL and X-rays experiments. MQW structures of 20, 40 and 60 Å thick GaN wells have been grown for two different Aluminium concentrations in GaAlN barriers respectively of 10 and 20 %. The sample growth was performed in a RIBER MBE 2300 chamber. Standard Knudsen cells were used for Gallium and Aluminium evaporation and the active nitrogen was generated by a commercial (ADDON) radio frequency (RF) cell. Growth was performed at a relatively low substrate temperature of 650°C. The composition of the GaAlN films was adjusted by varying the beam equivalent pressure of the Gallium and Aluminium fluxes. The thickness of the layers was controlled by RHEED oscillations. MBE growth was performed on 1.5 µm thick GaN layers grown by MOCVD on sapphire. The oxide on this MOCVD grown GaN surface can easily be removed by acid etching (regal water) and short heating (∼ 650°C) prior to growth. A well-defined RHEED pattern and intense RHEED oscillations show that the treated MOCVD surface is smooth on an atomic scale. To completely get rid of the eventual influence from a surface oxide or from a contamination layer, we interpose a few 1000 Å thick GaN layer.

PL time resolved measurements were performed at 2K with pulsed excitation (of ns length) above QW band gap energy and photon counting system with multi-channel analyser for PL detection.

Results and discussion

Low temperature (2 K) PL spectra, shown in Figure 1, are dominated by 3.47 eV band gap emission of the underlying 1.5 μm thick MOCVD-grown epilayer and of MBE-grown (few times 1000 Å thick) buffer layer. PL emission of ternary AlGaN barrier layers is also seen on the high-energy side of the emission spectra. In addition to barrier and substrate emissions, a SQW emission is also resolved with its LO-phonon replica. Assuming QW confinement effects only, SQW PL should show a blue-shift with respect to the GaN substrate emission, which should increase with a decreasing QW width. However, as shown in Figure 1, only the PL of 10 Å wide SQW is blue-shifted by about 150 meV. For 40 Å thick SQW’s a pronounced red-shift of the PL lines is observed from the expected PL position. This red-shift of the PL can be explained by a strong internal electric field present in the structure [Reference Langer, Simon, Konovalov, Pelekanos, Barski and Leszczynski5], as will be discussed later. In order to determine the influence of Aluminium concentration in barriers on the PL line positions, two samples with different Aluminium concentrations have been grown. The first sample consisted of 20, 40 and 60 Å thick quantum wells separated by 100 Å GaAlN barriers with the Aluminium concentration of 10 %. The second sample has the same structure but the Aluminium concentration was increased to 20 %. Low temperature PL spectra of our MQW structures are shown in Figure 2. Only the emission from 20 Å thick well in the low Aluminium content sample is blue-shifted with respect to the GaN substrate emission. All emissions from 40 and 60 Å thick wells are detected below the GaN emission. This phenomenon is clear evidence for a strong electric field present in our structures, which increases with the Aluminium concentration in barriers.

Fig1: Low temperature photoluminescence of 10 Å and 40 Å thick GaN quantum wells in AlGaN barriers with an aluminium concentration of 17.2% and 20.6% respectively.

Fig2: Low temperature photoluminescence of two samples with 20 Å, 40 Å and 60 Å thick GaN quantum wells and 100 Å thick AlGaN barriers with an aluminium concentration of 17.2% and 20.6% respectively.

In order to determine the origin of this field the strain present in our samples has to be investigated. Strain could be precisely determined by X-rays reciprocal lattice mapping. Results of such experiments are shown in Figure 3 for the 40 Å thick SQW. X-rays mapping around the (-2 0 2) Bragg peak of the GaN substrate is shown. These measurements clearly demonstrate that the AlGaN alloy has the same in-plane lattice parameter (represented by the (h, k) axis in reciprocal units of Al2O3) as the GaN substrate. Both 1000 Å thick GaAlN barriers are thus fully strained to GaN. Similar conclusions can be drawn from reciprocal space mappings for all other QW’s structures under investigation.

Fig3 (a): X-ray cartography of GaN single quantum well 40 A thick embedded in 1000 Å thick AlGaN barriers around (-2 0 2) Bragg peak of GaN substrate. The AlGaN barriers have the same in-plane lattice parameter than the GaN substrate. This is shown very precisely on the in plane scans (b) where the in-plane lattice parameter is represented by the H-axis in reciprocal lattice units of GaN

For totally pseudomorphic samples, one can precisely determine the Aluminium fraction in GaAlN barriers. From the in-plane lattice parameter and from the lattice parameter along the growth axis, using Vegard’s law for the lattice parameter and a linear interpolation between Poisson ratios for GaN [Reference Kisielowski, Krüger, Ruvimov, Suski, Ager, Jones, Lilienthal-Weber, Rubin, Bremser and Davis6] and AlN [Reference McNeil, Grimsditch, French and Am7], we determine the Al fraction in all our samples, which agrees with our estimations from PL studies.

Despite of the fact that GaN QW’s are not strained in our samples, we observed a dramatic dependence of QW PL on a QW width and on Aluminium concentration in barriers. This can be related to strong piezoelectric effects introducing strong internal electric fields to the structure. This hypothesis is further confirmed by PL kinetics measurements. For 40 and 60 Å wide SQW the PL intensity decay is highly non exponential and in μs range. In fact such slow PL kinetics resembles that of the yellow emission band and dramatically varies from the PL kinetics of excitons from GaN substrate. Those excitons show PL decay times in the range of 100 ps. Slow PL kinetics in GaN/AlGaN QW system can be explained by a strong reduction of radiative recombination probability caused by electric field induced spatial separation of electrons and holes in a wide QW. Strong piezoelectric effects also explain why SQW emission is relatively weak when compared to the substrate emission. As was mentioned above, the internal electric field strongly reduces radiative recombination rates of QW’s.

In conclusion, the present studies demonstrate strong piezoelectric effects in GaN/AlGaN QW structures with strained AlGaN barrier layers but with strain free GaN QW’s. We believe that this is related to the large piezoelectric constants predicted for GaN and GaAlN [Reference Bernardini, Fiorentini and Vanderbilt8].

References

Im, J. S., Kollmer, H., Off, J., Sohmer, A., Scholz, F., Hangleiter, A., Phys. Rev. B 57, R9435 (1998).Google Scholar
Korakakis, D., Ludwig, K. F., Moustakas, T. D., Appl. Phys. Lett. 72, 1004 (1998).CrossRefGoogle Scholar
Zeng, K. C., Lin, J. Y., Jiang, H. X., Salvador, A., Popovici, G., Tang, H., Kim, W., Morkoc, H., Appl. Phys. Lett. 71, 1368 (1997).CrossRefGoogle Scholar
Johnson, M. A. L., Shizuo Fujita, W. H., Rowland, K. A., Bowers, W. C., Hughes, Y. W., He, N. A., El-Masry, J.W., Cook, J. F., Schetzina, J., Ren, J. A., Edmond, , J. Vac. Sci. Technol. B 14, 2349-2353 (1996).CrossRefGoogle Scholar
Langer, R., Simon, J., Konovalov, O., Pelekanos, N.T., Barski, A., Leszczynski, M., MRS Internet J. Nitride Semicond. Res. 3, 46 (1998).CrossRefGoogle Scholar
Kisielowski, C., Krüger, J., Ruvimov, S., Suski, T., Ager, J. W., Jones, E., Lilienthal-Weber, Z., Rubin, M., Bremser, M. D., Davis, R. F., Phys. Rev. B 54, 17745 (1996).CrossRefGoogle Scholar
McNeil, L.E., Grimsditch, M., French, R.H., Am, J.. Ceram. Soc. 76, 1132-1136 (1993).CrossRefGoogle Scholar
Bernardini, F., Fiorentini, V., Vanderbilt, D., Phys. Rev. B 56, R10024 (1997).CrossRefGoogle Scholar
Figure 0

Fig1: Low temperature photoluminescence of 10 Å and 40 Å thick GaN quantum wells in AlGaN barriers with an aluminium concentration of 17.2% and 20.6% respectively.

Figure 1

Fig2: Low temperature photoluminescence of two samples with 20 Å, 40 Å and 60 Å thick GaN quantum wells and 100 Å thick AlGaN barriers with an aluminium concentration of 17.2% and 20.6% respectively.

Figure 2

Fig3 (a): X-ray cartography of GaN single quantum well 40 A thick embedded in 1000 Å thick AlGaN barriers around (-2 0 2) Bragg peak of GaN substrate. The AlGaN barriers have the same in-plane lattice parameter than the GaN substrate. This is shown very precisely on the in plane scans (b) where the in-plane lattice parameter is represented by the H-axis in reciprocal lattice units of GaN