1. Introduction
With its wide bandgap and intrinsic visible-blind absorption spectrum, AlxGa1-xN ternary alloy is the most promising material system for high-performance photodetectors operating in the ultraviolet (UV) spectrum Reference Razeghi and Rogalski[1]. Their cut-off wavelength (λc) can be tuned from 365 nm to 200 nm, which covers the solar-blind spectrum (λ<280 nm) Reference Schreiber, Dang, Smith, Pickenpaugh, Gehred and Litton[2]. Solar-blind detectors play important roles in a variety of military and civil applications including missile plume detection, flame/engine monitoring, chemical/biological agent sensing, and covert space-to-space communications Reference Carrano, Li, Grudowski, Dupuis and Campbell[3]. AlGaN-based solar-blind photodetectors with high responsivity Reference Walker, Jumar, Mi, Kung, Zhang and Razeghi[4] Reference Wong, Chowdhury, Collins, Yang, Denyszyn, Kim, Campbell and Dupuis[5], low dark current Reference Yang, Lambert, Li, Collins, Wong, Chowdhury, Dupuis and Campbell[6] Reference Kuryatkov, Temkin, Campbell and Dupuis[7], high solar rejection Reference Sandvik, Mi, Shahedipour, McClintock, Yasan, Kung and Razeghi[8] Reference Hirano, Pernot, Iwaya, Detchprohm, Amano and Akasaki[9], high bandwidth Reference Li, Lambert, Beck, Collins, Yang, Wong, Chowdhury, Dupuis and Campbell[10], and high detectivity Reference Collins, Chowdhury, Wong, Yang, Beck, Dupuis and Campbell[11] Reference Collins, Chowdhury, Wong, Yang, Beck, Dupuis and Campbell[12] performance were demonstrated using p-i-n, MSM and Schottky type detector structures.
Compared with p-i-n photodiodes, AlGaN Schottky photodiodes have several advantages. Growth of p+ AlGaN layers and formation p+ ohmic contacts with low contact resistance are two challenging issues for p-i-n photodiodes, while Schottky photodiodes do not face these problems. High-quality Schottky and n+ ohmic contacts can be achieved using widely known process techniques. Moreover, since the photocarriers are generated and efficiently collected within the depleted active layer, high-frequency operation of Schottky photodiodes is not affected by minority carrier diffusion Reference Wang and Bloom[13] Reference Parker, Say and Hansom[14] Reference Onat, Gokkavas, Ozbay, Ata, Towe and Unlu[15] Reference Biyikli, Kimukin, Aytur, Gokkavas, Unlu and Ozbay[16]. Successful solar-blind operation of AlGaN Schottky photodiodes were demonstrated by several research groups Reference Osinsky, Gangopadhyay, Lim, Anwar, Khan, Kuksenkov and Tempkin[17] Reference Rumyantsev, Pala, Shur, Gaska, Levinshtein, Adivarahan, Yang, Simin and Asif Khan[18]. However, the reported dark current and detectivity performances were poor with respect to AlGaN-based p-i-n and MSM type photodiodes. In terms of high-speed performance, GaN-based visible-blind photodiodes with 3-dB bandwidths in the GHz regime were successfully demonstrated Reference Carrano, Li, Brown, Grudowski, Eiting, Dupuis and Campbell[19] Reference Carrano, Li, Brown, Grudowski, Eiting, Dupuis and Campbell[20] Reference Biyikli, Kartaloglu, Aytur, Kimukin and Ozbay[21]. Reported AlGaN-based solar-blind detectors had lower bandwidths. A maximum high-speed performance of 100 MHz was reported with an AlGaN MSM photodiode structure Reference Li, Lambert, Beck, Collins, Yang, Wong, Chowdhury, Dupuis and Campbell[10]. For solar-blind AlGaN Schottky photodiodes the best detector bandwidth demonstrated was below the MHz level Reference Osinsky, Gangopadhyay, Lim, Anwar, Khan, Kuksenkov and Tempkin[17]. Recently we had demonstrated solar-blind AlGaN Schottky photodiodes with very low dark current and high detectivity Reference Biyikli, Aytur, Kimukin, Tut and Ozbay[22]. In this paper, we report on the design, fabrication, and characterization of high-performance solar-blind AlGaN Schottky photodiodes with high-speed performance close to the GHz level.
2. Experimental Details
2.1 Epitaxial Structure Design
The epitaxial structure of the AlGaN Schottky detector wafer was designed to achieve low cut-off wavelength (λc < 280 nm), high visible rejection, and low dark current. Figure 1 shows the details of the photodiode structure. The AlxGa1-xN/GaN epitaxial layers of our hetero-junction Schottky PD wafer were grown by MOCVD on a 2-inch single-side polished (0001) sapphire substrate. The 0.8 μm thick undoped AlGaN layer with 38% Al concentration was the active absorption region of the detector. The ohmic contacts were formed within the n+ GaN layer. The 0.2 μm thick n+ Al0.38Ga0.62N layer was designed as a diffusion barrier for the holes generated in the n+ GaN layer to increase the visible rejection of the detector.
Figure 1. Epitaxial layer structure of solar-blind AlGaN Schottky photodiode wafer.
2.2 Device Fabrication
Fabrication process of the AlGaN Schottky photodiodes was accomplished in a class-100 clean-room facility using a microwave compatible five mask-level standard semiconductor process Reference Ozbay, Islam, Onat, Gokkavas, Aytur, Tuttle, Towe, Henderson and Unlu[23] Reference Kimukin, Ozbay, Biyikli, Kartaloglu, Aytur, Unlu and Tuttle[24]. Fabrication started with the formation of n+ ohmic contacts. The ohmic contact regions were etched down to the n+ GaN ohmic layer using dry etch. Reactive ion etching (RIE) process was utilized under 20 sccm CCl2F2 plasma at 100 W RF power. Then a ∼100 nm thick Ti/Al contact metal was deposited using thermal evaporation. The metal was lifted off in acetone solution and the samples were annealed at 700 °C for 30 s afterwards. Then the device mesas with 30-200 μm diameters were defined using RIE with the same process parameters. Mesa isolation of the devices was completed with a ∼1.8 μm deep etch, down to the undoped GaN layer. This was followed by the evaporation of ∼100 Å thick Au film as the Schottky contact metal. Afterwards, a ∼100 nm thick Si3N4 layer was deposited using plasma enhanced chemical vapor deposition to passivate the sample surface and protect the thin Schottky contactfilms. In the final step, interconnect pads were formed by a ∼0.7 μm thick Ti/Au metallization. A schematic cross-section figure of the completed AlGaN Schottky photodiode is shown in Figure 2.
Figure 2. Cross-section schematic of the fabricated AlGaN Schottky photodiode.
2.3 Device Characterization
After device fabrication, current-voltage (I-V), spectral responsivity, noise, and high-speed characterizations were carried out. All measurements were made on-wafer, using a microwave probe station. To observe the electrical diode characteristics and the leakage current, we first performed the I-V measurements. The I-V setup consisted of a Hewlett Packard HP4142B DC parametric measurement instrument, DC probes with triax output and low-noise triax cables. DC current was measured as voltage was applied to the devices.
Spectral responsivity measurements were done using a 175 W xenon light-source, 1/4 m Digikrom DK240 monochromator, multi-mode UV fiber, DC voltage source, SR830 DSP lock-in amplifier and a Newport model 1830-C calibrated optical power-meter. Xenon lamp output was fed into the monochromator. The monochromator output was chopped and coupled to the fiber using a UV-enhanced focusing lens. The detectors were illuminated by the optical output coming out from the fiber which was calibrated using the calibrated photodetector. The detectors were biased with a DC voltage source upto 50 V, and the resulting photocurrent was measured using the lock-in amplifier.
Low-frequency (< 100 KHz) noise characteristics of the solar-blind Schottky detectors were measured with a SR785 dynamic signal analyzer, which measured the fast Fourier transform spectrum of the detector noise. The detectors were reverse biased with a DC voltage source.
Temporal high-frequency measurements were done at the solar-blind wavelength of 267 nm. Ultrafast UV pulses were generated using a laser set-up with two nonlinear crystals. A Coherent Mira 900F model femtosecond mode-locked Ti:sapphire laser was used to generate the pump beam at 800 nm. The pump pulses were produced with 76 MHz repetition rate and 140 fs pulse duration. These pulses were frequency doubled to generate a second harmonic beam at 400 nm using a 0.5 mm thick type-I β-BaB2O4 (BBO) crystal. The second harmonic beam and the remaining part of the pump beam were frequency summed to generate a third harmonic output beam at 267 nm using another type-I BBO crystal with thickness of 0.3 mm. The resulting 267 nm pulses had pulsewidths below 1 ps and were focused on-to the devices using UV-enhanced mirrors and lenses. The detectors were biased using a DC voltage source and a 40 GHz bias-tee. Using 50 GHz microwave probe and cables, the electrical pulses were transferred to a 50 GHz sampling oscilloscope where the temporal pulse responses were observed.
3. Measurement Results and Discussion
The fabricated AlGaN Schottky detectors exhibited low dark currents and high breakdown voltages. Figure 3 shows the I-V curve of a 150×150 μm2 device with >50 V breakdown voltage. Excellent low-leakage performance was achieved with a dark current below 400 fA under reverse bias voltages as high as 25 V. The dark current fluctuated between 150-400 fA in the 0-25 V reverse bias range (see inset figure). These leakage values correspond to dark current density values of 0.7-1.8 nA/cm2. The differential resistance (R = dV/dI) of these devices was calculated and their dark impedance was in excess of 1013 Ω in the 0-25 V range. These measurement results correspond to the best I-V performance reported for solar-blind AlGaN Schottky photodiodes. To indicate the performance variation, Figure 4 shows the I-V characteristics of a 200 μm diameter photodiode fabricated on a different wafer piece. Few pA dark current at 5 V reverse bias and a breakdown around 20 V was observed. I-V measurement under UV illumination at 256 nm showed a clear UV photoresponse when compared with the detector dark current (see inset figure).
Figure 3. I-V characteristics of a 150×150 µm2 solar-blind Schottky photodiode. Inset shows the measured curve in logarithmic scale.
Figure 4. I-V measurement curve of a 200 μm diameter Schottky detector. Inset shows dark current versus UV photocurrent at 256 nm.
Spectral photoresponse measurements of the AlGaN Schottky photodiodes were carried out in the 250-350 nm spectral range. A bias-dependent spectral responsivity with true solar-blind characteristic was observed. Figure 5 shows the measured spectral responsivity of a photodiode with ∼20 V breakdown voltage. The peak responsivity increased with applied reverse bias. The photovoltaic peak responsivity of 36 mA/W increased upto 78 mA/W under 15 V reverse bias. At higher reverse biases, photocurrent fluctuations increased and signs of photoconductive gain were observed as the detector operated near the breakdown regime. Peak wavelength of 250 nm did not change with bias. The peak responsivity value corresponds to a peak quantum efficiency of 39% at 250 nm. The corresponding spectral quantum efficiency curves are plotted in Figure 6. True solar-blind characteristic was achieved with cut-off wavelengths smaller than 280 nm. The cut-off wavelength changed from 262 nm to 266 nm for no bias and 15 V reverse bias respectively. The device responsivity dropped sharply around 270 nm. A UV/VIS rejection of 3 orders of magnitude was already obtained around 280 nm. For λ> 280 nm, the responsivity decay continued with a lower rate and a 4 order of magnitude rejection was achieved before 350 nm. The maximum visible rejection at 350 nm was recorded as 2.4×104 while the detectors were operating in the photovoltaic mode. As applied reverse bias increased, the rejection showed a descending behavior. The measured λc and UV/VIS rejection values correspond to the lowest λc and highest visible rejection reported for solar-blind AlGaN Schottky photodiodes. Table 1 summarizes the spectral responsivity measurement results.
Figure 5. Spectral responsivity of the AlGaN Schottky photodiodes. A peak responsvity of 78 mA/W at 250 nm was obtained under 15 V reverse bias.
Figure 6. Bias-dependent spectral quantum efficiency curves of the solar-blind Schottky detector. A peak efficiency of 39% at 250 nm with a solar-blind cut-off at 266 nm was measured at 15 V.
Table 1 Spectral photoresponse measurement results obtained for solar-blind AlGaN Schottky photodiodes.
Detector noise characteristics were measured in the 0.1 Hz - 100 KHz frequency range. Solar-blind AlGaN Schottky photodiodes with low dark current exhibited spectral noise density values below the noise floor of the measurement setup. Noise floor of our setup was around 3×10−29 A2/Hz for frequencies higher than 1 KHz, and increased for lower frequency values. Therefore we were not able to measure the noise density values of our low-leakage devices. To understand the dominant noise mechanism and its bias dependence, we measured a device with high leakage (few μA dark current at 5 V, breakdown at ∼14 V). The detectors displayed 1/f-noise characteristic with noise densities proportional to reverse bias. Figure 7 shows the dark current noise power density values measured at 1 Hz as a function of applied reverse bias voltage. With increasing bias from 0 V to 10 V, the noise density increased by more than 4 orders of magnitude.
Figure 7. Dark current noise power density of an 80 μm diameter high leakage Schottky photodiode at 1 Hz as a function of reverse bias.
Time-domain high-speed characterization of the fabricated solar-blind Schottky photodiodes resulted in very fast pulse responses with high 3-dB bandwidths. The detector pulse response was bias dependent. Faster pulses were obtained for higher reverse bias values as the thick n- AlGaN absorption layer was fully depleted under high reverse bias voltages. As the bias tee limit was 16 V, we were not able to increase the bias voltage above this limit. The fastest pulse response was measured with an 80 μm diameter device (Figure 8). Under 15 V reverse bias, it produced a pulse response with a very fast rise time of 12 ps, and a full-width-at-half-maximum (FWHM) of 216 ps. Using FFT, the corresponding 3-dB bandwidth of the detector was calculated as 870 MHz. Pulse responses with narrower pulse-widths were also measured, but their calculated 3-dB bandwidth was lower due to longer decay parts. Figure 9 shows such a response of a 30 μm diameter solar-blind detector with 13 ps rise time, 74 ps FWHM, and 300 MHz 3-dB bandwidth.
Figure 8. Best pulse response measured with an 80 μm diameter device. Inset shows the FFT of temporal data. The AlGaN Schottky photodiode performed a 3-dB bandwidth of 870 MHz.
Figure 9. Pulse response of a 30 μm diameter solar-blind detector with 74 ps FWHM and 300 MHz 3-dB bandwidth. Inset shows the zoomed plot of the pulse response.
To analyze this unexpected longer decay time for a smaller diode area, curve fitting with exponential decay functions were applied to the measured pulse responses shown in Figure 8 and Figure 9. A simple first order exponential fit with a single time constant could not be achieved. Instead, both responses were fitted well with second order exponential decay functions, i.e. with a sum of two exponential decay functions with two different time constants. The fit for 80 μm diameter device response had time constants of 157 ps and 2.85 ns, while the 30 μm diameter device response fit exhibited time constants of 120 ps and 5.45 ns. These time constants agree with our bandwidth calculations: The response with the shorter FWHM but lower 3-dB bandwidth (30 μm diameter diode) had a shorter initial decay time constant along with a longer subsequent decay time constant. The reverse conditions were valid for the other device response giving rise to a longer FWHM but higher 3-dB bandwidth. The physical reason for the multi-exponential relaxation mechanism was not clear. Evenmore, the initial decay time constants were much longer than the RC time constants of 4 ps and 27 ps for 30 μm and 80 μm device respectively. These results convinced us that mechanisms other than RC and transit time limitations were responsible for the decay part of the high-speed response of these solar-blind detectors. We postulate that the long and multi-exponential decay times are related to issues such as carrier trapping effect in AlGaN layers, carrier diffusion component originating from low field regions close to the center of the mesa, and growth/process related effects. A detailed study on the relaxation mechanisms of solar-blind AlGaN PDs will be made in the near future.
Although there were exceptions, as discussed above, in general, an inverse proportionality between device area and detector bandwidth was observed. FFT curves of 4 pulse responses from detectors with different device areas are plotted in Figure 10. 3-dB bandwidths of 220, 280, 510, and 780 MHz were obtained for devices with 200, 150, 100, and 60 μm diameter respectively. These results correspond to the best high-speed performance reported for any type of solar-blind photodetectors.
Figure 10. FFT curves of pulse responses from Schottky detectors with different device areas. 3-dB bandwidths of 220, 280, 510, and 780 MHz were obtained with decreasing device area.
4. Summary and Conclusions
High-performance solar-blind AlGaN Schottky photodiodes have been successfully designed, fabricated and tested. The solar-blind Schottky detectors displayed dark current densities as low as 7×10−10 A/cm2 under reverse biases as high as 25 V. A bias dependent spectral responsivity was observed with a maximum peak responsivity of 78 mA/W at 250 nm. The corresponding peak quantum efficiency obtained from these devices was 39%. True solar-blind detection was demonstrated with a sharp cut-off at 266 nm. The AlGaN Schottky photodiodes exhibited over 4 orders of magnitude visible rejection within 100 nm, with a maximum rejection of 2.4×104 at zero bias. Low frequency noise was 1/f limited with noise power densities below the measurement setup noise floor of 3×10−29 A2/Hz. Time-domain high-frequency measurements resulted in very short rise times and 3-dB bandwidths as high as 870 MHz were achieved. The recorded values for dark current, cut-off wavelength, visible rejection, and high-speed measurements correspond to the best detector performance results reported for solar-blind AlGaN Schottky photodiodes.
Acknowledgments
This work was supported by NATO Grant No. SfP971970, Turkish Department of Defense Grant No. KOBRA-002, and FUSAM-03.