Towards a Virtual Laboratory for Grain Boundaries and Dislocations

Published online by Cambridge University Press:  31 January 2011

Sebastián Echeverri Restrepo  and
Barend J. Thijsse
Sebastián Echeverri Restrepo
Affiliation:
s.echeverrirestrepo@tudelft.nlsebastianecheverrir@gmail.com, Delft University of Technology, Department of Materials Science and Engineering, Delft, Netherlands
Barend J. Thijsse
Affiliation:
b.j.thijsse@tudelft.nl, Delft University of Technology, Department of Materials Science and Engineering, Delft, Netherlands
Get access

Abstract

In order to perform a systematic study of the interaction between grain boundaries (GBs) and dislocations using molecular dynamics (MD), several tools need to be available. A combination of computational geometry and MD was used to build the foundations of what we call a virtual laboratory. First, an algorithm to generate GBs on face-centered cubic bicrystals was developed. Two crystals with different orientations are placed together. Then, by applying “microscopic” rigid body translations along the GB plane to one of the crystals and removing overlapping atoms, a set of initial configurations is sampled and a minimum energy configuration is found. Second, to classify the geometry of the GBs a local symmetry type (LST) describing the angular environment of each atom is calculated. It is found that for a given relaxed GB the number of atoms with different LSTs is not very large and that it is possible to find unique geometrical patterns in each GB. For instance, the LSTs of two GBs having the same “macroscopic” configuration but different “microscopic” degrees of freedom can be dissimilar: the configurations with higher GB energy tend to have a higher number of atoms with different LSTs. Third, edge dislocations are introduced into the bicrystals. We see that full edge dislocations split into Shockley partials. Finally, by loading the bicrystals with tensile stresses the edge dislocations are put into motion. Various examples of dislocation-GB interactions in Cu are presented.

Keywords

dislocationsgrain boundariessimulation
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1224: Symposia FF/GG – Mechanical Behavior at Small Scales — Experiments and Modeling , 2009 , 1224-GG05-03
Copyright
Copyright © Materials Research Society 2010

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Wolf, D. and Yip, S.. Materials interfaces: atomic atomic-level structure and properties. Chapman and Hall (1992).Google Scholar
2 Foiles, S. M., Olmsted, D., and Holm, E. A.. Using atomistic simulations to inform mesoscale simulations of microstructural evolution. Proceedings of the Fourth International Conference on Multiscale Materials Modeling, 362 (2008).Google Scholar
3 Spearot, D. E.. Atomist Atomistic Calculations of Nanoscale Interface Behavior in FCC Metals. PhD thesis, Georgia Institute of Technology (2005).Google Scholar
4 Rittner, J. D. and Seidman, D. N.. Phys. Rev. B, 54, 6999 (1996).Google Scholar
5 Swygenhoven, H. Van and Caro, A.. Appl. Phys. Lett., 71, 1652 (1997).Google Scholar
6 Derlet, P. M. and Swygenhoven, H. Van Phys. Rev. B, 67, 014202 (2003).Google Scholar
7 Alfthan, S. von Kaski, K. and Sutton, A. P., Phys. Rev. B, 74, 134101 (2006).Google Scholar
8 Thijsse, B. J.. Camelion. Virtual Materials Laboratory, Department of Materials Science and Engineering, Delft Univ Universit ersity of Technology, The Netherlands.Google Scholar
9 Spearot, D. E., Capolungo, L., Qu, J., and Cherkaoui, M.. Comput. Mater. Sci., 42, 57 (2008).Google Scholar
10 Mishin, Y., Farkas, D., Mehl, M. J., and Papaconstantopoulos, D. A.. Interatomic potentials for Al and Ni from experimental data and ab initio calculations. In Mat. Re Res. Soc. Symp. Proc., 538, 535 (1999).Google Scholar
11 Mishin, Y., Mehl, M. J., Papaconstantopoulos, D. A., Voter, A. F. and Kress, J. D., Phys. Rev. B, 63, 224106 (2001).Google Scholar
12 Steinhardt, P. J., Nelson, D. R. and Ronchetti, M.. Phys. Rev. B, 28, 784 (1983).Google Scholar
13 Lazic, I., Klaver, P. and Thijsse, B. J.. Phys. Rev. B, 81, 045410 (2010).Google Scholar
14 Lechner, W. and Dellago, C.. J. Chem. Phys., 129, 114707, (2008).Google Scholar
15 Li, J., Modelling Simul. Mater. Sci. Eng., 11, 173 (2003).Google Scholar
16 Hull, D. and Bacon, D. J.. Introduction to dislocati dislocations. Butter ons. Butterworth Heinemann, fourth worth edition (2002).Google Scholar
17 Frøseth, A. G., Derlet, P. M., and Swygenhoven, H. Van, Act. Mat., 52, 5863, (2004).Google Scholar
18 Byun, T. S., Act. Mat., 51, 3063 (2003).Google Scholar