Retention Behaviours Of Carbon In Sol-Gel Derived ZrO2 Studied By Fourier Transform Infrared Spectroscopy

Published online by Cambridge University Press:  21 February 2011

H.C. Zeng
H.C. Zeng*
Affiliation:
Department of Chemical Engineering, Faculty of Engineering, National University of Singapore, 10 Kent Ridge Crescent, Singapore 0511
Get access

Abstract

The carbon retention patterns based on evolution of FT-IR spectra at different calcination temperatures for ZrO2 gels derived from Zr-n-propoxide-acetylacetone-water-isopropanol system are examined in detail. For most captured carbon species, carbon can be depleted at relatively low temperature of about 400°C. However, for lattice-included species, especially those incorporated into lattice during phase transition, a temperature around 900°C is needed to eliminate carbon in the gels. It is found that water treatment alone does not provide new routes for carbon retention in as-prepared ZrO2 gels. When gels are pre-treated with Ni2+ and water, new forms of carbon containing species can be observed. This is attributed to an inter-diffusion of Ni2+ and ZrO2 matrix and the catalytic effect of resultant solid solution NiO-ZrO2 on the retained carbon.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 346: Symposium N – Better Ceramics Through Chemistry VI , 1994 , 715
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1 Ramamurthi, S.D., Xu, Z., and Payne, D.A., J. Am. Ceram. Soc. 73 (1990) 2760.Google Scholar
2 Millberg, L.S., J. of Metals, August 1987 p.9.Google Scholar
3 Maschio, R.D., Filipponi, M., Soraru, G.D., Carturan, G. and Felice, G.M.D., Ceram. Bull. 71 (1992) 204.Google Scholar
4 Yang, L. and Cheng, J.J., J. Non-Cryst. Solids 112 (1989) 442.Google Scholar
5 Vesteghem, H., Lecomte, A., and Dauger, A., J. Non-Cryst. Solids 147&148 (1992) 503.Google Scholar
6 Dislich, H. and Hinz, P., J. Non-Cryst. Solids 48 (1982) 11.Google Scholar
7 Debsikdar, J.C., J. Non-Cryst. Solids 86 (1986) 231.Google Scholar
8 Monros, G., Carda, J., Tena, M.A., Escribano, P., Sales, M. and Alarcon, J., J. Non-Cryst. Solids 147&148 (1992) 588.Google Scholar
9 Chaumont, D., Craievich, A., and Zarzycki, J., J. Non-Cryst. Solids 147&148 (1992) 41.Google Scholar
10 Johnson, D.W., Am. Ceram. Soc. Bull. 64 (1985) 1597.Google Scholar
11 Debsikdar, J.C., J. Non-Cryst. Solids 91 (1987) 262.Google Scholar
12 Colomban, Ph. and Bruneton, E., J. Non-Cryst. Solids 147&148 (1992) 201.Google Scholar
13 Guinebretiere, R., Dauger, A., Lecomte, A. and Vesteghem, H., J. Non-Cryst. Solids 147/148 (1992) 542.Google Scholar
14 Atik, M. and Aegerter, M.A., J. Non-Cryst. Solids 147&148 (1992) 813.Google Scholar
15 Monros, G., Carda, J., Tena, M.A., Escribano, P., Sales, M. and Alarcon, J., J. Non-Cryst. Solids 147/148 (1992) 588.Google Scholar
16 Bruce, L.A. and Mathews, J.F., Appl. Catal. 8 (1983) 349.Google Scholar
17 Mercera, P.D.L., van Ommen, J.G., Doesburg, E.B.M., Burggraaf, A.J., and Ross, J.R.H., Appl. Catal. 71 (1991) 363.Google Scholar