Minority Carrier Lifetime Measurement in Germanium on Silicon Heterostructures for Optoelectronic Applications

Published online by Cambridge University Press:  01 February 2011

Josephine J. Sheng
Affiliation:
jjsheng@sandia.gov, Sandia National Laboratories and University of New Mexico, Albuquerque, P.O.Box 5800, MS 1077, Albuquerque, NM, 87185-1077, United States
Malcolm S. Carroll
Affiliation:
mscarro@sandia.gov, United States
Get access

Abstract

Demand for low cost and high density near infrared (NIR) detection has motivated the development and use of germanium on silicon (Ge/Si) heterostructures to extend the optoelectronic application of Si technology. Ge/Si structures are currently being considered for NIR p/n detectors that can be integrated with Si CMOS [1]. Various research demonstrations of integrated Ge/Si diodes with CMOS have been made including using sputtered poly-Ge to form Ge/Si photodiodes after the CMOS transistors were complete. Poly-crystalline germanium (poly-Ge) may be formed by various methods including the use of plasma enhanced chemical vapor deposition. In this work, the formation of poly-Ge/Si heterostructures by inductively coupled plasma enhanced chemical vapor deposition (ICP-CVD) is examined as an alternative method to integrate poly-Ge into a CMOS process flow. In this work, 25 nm poly-Ge on Si heterostructures are formed by either recrystallization of ICP-CVD hydrogenated amorphous germanium (α-Ge:H) or direct deposition of ICP-CVD poly-Ge. A rapid measure of the suitability for detectors of the different poly-Ge films is the minority carrier recombination lifetime, which can affect dark current, quantum efficiency and overall detector detectivity. Recombination lifetimes were measured, therefore, in α-Ge:H that was recrystallized using rapid thermal annealing between 400 – 1050 °C in nitrogen ambient. Lifetimes were measured using a non-contact inductively coupled photo-conductance setup and an effective surface recombination velocity is subsequently extracted for each Ge/Si heterostructure that describes the integrated recombination in the Ge layer and at the Ge/Si interface, which separates the Ge contribution from recombination in the bulk silicon and at the silicon surface. The effective recombination velocities for the 25 nm Ge layers are found to be ∼103−104 cm/s.

Type
Research Article
Copyright
Copyright © Materials Research Society 2006

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Masini, C., Calace, L., Assanto, G., Luan, H-C., Kimerling, L. C., IEEE Trans. Elec. Dev., 48, 1092 (2001)Google Scholar
[2] Famà, S., Colace, L., Masini, G., Assanto, G., Luan, H.-C., Appl. Phys. Lett., 81, 586 (2002)Google Scholar
[3] Masini, G., Cencelli, V., Colace, L., De Nortaristefani, F., Assanto, G., Appl. Phys. Lett., 80, 3268 (2002)Google Scholar
[5] Submitted MRS Spring 2006 Google Scholar
[6] Sinton, R.A., Testing Solar Cell Wafers After Phosphorus Diffusion, April 27, 2004 Google Scholar
[7] Kane, D.E., Swanson, R.M., Proc. 18th IEEE Photovoltaic Specialist Conf., 5781 (1985)Google Scholar
[8] Sinton, R.A., Cuevas, A., Appl. Phys. Lett., 69, 2510 (1996)Google Scholar
[9] Yablonovitch, E., Allara, D.L., Chang, C.C., Gmitter, T., Bright, T.B., Phys. Rev. Lett., 57, 249 (1986)Google Scholar
[10] Gräf, D., Grundner, M., Schulz, R., Mühlhoff, L., J. Appl. Phys., 68, 5155 (1990)Google Scholar
[11] Stockhausen, A., Kampen, T.V., Mönch, W., Appl. Surf. Sci., 56–5, 795 (1992)Google Scholar
[12] Carroll, M. S., King, C. A., Thin Solid Films, 473, 173 (2005)Google Scholar
[13] Bandaru, P. R., Sahni, S., Yablonovitch, E., Liu, J., Kim, H.-Jun, Xie, Y.-H., Material Science and Engineering B, 113, 7984 (2004)Google Scholar