Investigation of Blistering Phenomena in Hydrogen-Implanted GaN and AlN for Thin Film Layer Transfer Applications
Published online by Cambridge University Press: 01 February 2011
Abstract
High dose hydrogen implantation-induced blistering phenomena in GaN and AlN have been investigated for potential thin film layer transfer applications. GaN and AlN were implanted with 100 keV H2+ ions with various ion doses in the range of 5´1016 to 2.5´1017 cm−2. After implantation the samples were annealed at higher temperatures up to 800°C in order to observe the formation of surface blisters. In the case of GaN only those samples that were implanted with a dose of 1.3´1017 cm−2 or higher showed surface blistering after post-implantation annealing. For AlN the samples those were implanted with a dose of 1.0´1017 or 1.5´1017 cm−2 displayed surface blistering after post-implantation annealing. Cross-sectional transmission electron microscopy was utilized to observe the microscopic defects that eventually cause surface blistering. Large area microcracks, as revealed in the XTEM images, were clearly observed in the case of both GaN and AlN after post-implantation annealing. A comparison of the hydrogen implantation-induced blistering in GaN and AlN has also been presented.
- Type
- Research Article
- Information
- Copyright
- Copyright © Materials Research Society 2008
References
REFERENCES
- 1
- Cited by