Interface Stability During Solid Phase Epitaxy Of Strained GexS1-x Films on Si (100)
Published online by Cambridge University Press: 15 February 2011
Abstract
Strained solid phase epitaxial (SPE) regrowth of amorphous GexSi1-x on Si (100) substrates was studied using time-resolved reflectivity (TRR). Films of CVD-grown Ge0.13Si0.87 on Si were amorphized by Si ion implantation, and subsequently regrown at temperatures between 550°C and 610°. Information on regrowth dynamics and interface roughness evolution was obtained by accurately modeling the complicated TRR data for GexSi1-x regrowth using a Moving, statistically roughening interface. The SPE regrowth rate slowed as the interface crossed into the GexSi1-x layer and the originally planar interface roughened, as confirmed by transmission electron Microscopy. A Minimum in the regrowth velocity was observed after regrowing approximately 60 nm into the GexSi1-x layer; the SPE rate subsequently increased to a final, thickness-dependent velocity that was still below that for pure Si. Upon entering the GexSi1-x layer, the interface roughened quickly to a 15–20 nm amplitude, increasing only slightly more during the remainder of regrowth. The degree of roughening and velocity reduction was found to be dependent on the anneal temperature. In contrast, samples with low Ge concentrations (< 3 at.%) prepared by ion implantation exhibited minimal interface roughening and essentially identical SPE velocities as pure Si.
- Type
- Research Article
- Information
- Copyright
- Copyright © Materials Research Society 1994
References
REFERENCES
- 1
- Cited by