Interaction of Dislocations with Impurities and its Influence on the Mechanical Properties of Silicon Crystals

Published online by Cambridge University Press:  15 February 2011

Koji Sumino
Koji Sumino*
Affiliation:
The Research Institute for Iron, Steel and Other Metals, Tohoku University, 2–1–1 Katahira, Sendai 980, Japan
Get access

Abstract

A review is presented of the work on the influence of impurities on the dynamic behavior of dislocations in silicon crystals and also on the resulting effects in the mechanical strength performed by the author's group. Special emphasis is laid on the effects of light element impurities such as oxygen, nitrogen and carbon. Although all of these impurities do not affect the velocities of dislocations moving under relatively high stresses, oxygen and nitrogen atoms are found to lock slowly moving dislocations and dislocations at rest very effectively. Such locking of dislocations results in the decreases in the activities of generation and multiplication centers for dislocations, leading to the strengthening of the crystals. The high strength of silicon crystals brought about by the impurities is lost when the crystals are subjected to the heat treatments which allow the precipitation of the impurities on a macroscopic scale. This softening is shown to be caused by dislocations punched out from precipitates and by the exhaustion of the impurities dissolved in the matrix crystal.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 14: Symposium B – Defects in Semiconductors II , 1982 , 307
Copyright
Copyright © Materials Research Society 1982

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Alexander, H. and Haasen, P., Solid State Physics 22, 28 (1968).Google Scholar
2. Kojima, K. and Sumino, K., Crystal Lattice Defects 2, 147 (1971).Google Scholar
3. Sumino, K. and Kojima, K., Crystal Lattice Defects 2, 159 (1971).Google Scholar
4. Sumino, K., Kodaka, S., and Kojima, K., Mater. Sci. Engng. 13, 263 (1974).Google Scholar
5. Sumino, K., Mater. Sci. Engng. 13, 269 (1974).Google Scholar
6. Yonenaga, I. and Sumino, K., Phys. Stat. Sol. (a) 50, 685 (1978).CrossRefGoogle Scholar
7. Suezawa, M. Sumino, K. and Yonenaga, I., Phys. Stat. Sol. (a) 51, 217 (1979).Google Scholar
8. Sumino, K. and Harada, H., Phil. Mag. A 44, 1319 (1981).Google Scholar
9. Sato, M. and Sumino, K., Proc. Fifth Int. Conf. on High Voltage Electron Microscopy, Imura, Kyoto T. and Hashimoto, H. eds. (1977) pp. 459.Google Scholar
10. Sumino, K. and Sato, M., Kristall u. Technik 14, 1343 (1979).Google Scholar
11. Sato, M. and Sumino, K., Phys. Stat. Sol. (a) 55, 297 (1979).Google Scholar
12. Hu, S. M. and Patrick, W. J., J. Appl. Phys. 46, 1869 (1975).Google Scholar
13. Hu, S. M., Appl. Phys. Lett. 31, 53 (1977).Google Scholar
14. Sumino, K., Harada, H. and Yonenaga, I., Jpn. J. Appl. Phys. 19, L49 (1980).Google Scholar
15. Suzuki, T., Isawa, N., Okubo, Y. and Hoshi, K., Semiconductor Silicon 1981,Huff, H. R. et al. eds.(1981) pp. 90.Google Scholar
16. Abe, T., Kikuchi, K., Shirai, S., and Muraoka, S., Semiconductor Silicon 1981,Huff, H. R. et al. eds. (1981) pp. 54.Google Scholar
17. Imai, M. and Sumino, K., Phil. Mag. A, in the press.Google Scholar
18. Erofeev, V. N., Nikitenko, V. I. and Osvenskii, V. B., Phys. Stat. Sol. 35, 79(1969).Google Scholar
19. Kulkarni, S. B. and Williams, W. S., J. Appl. Phys. 47, 4318 (1976).Google Scholar
20. Patel, J. R. Testardi, L. R. and Freeland, P. E., Phys. Rev. B 13, 3548(1976).Google Scholar
21. George, A. and Champier, G., Phys. Stat. Sol. (a) 53, 529,(1979).Google Scholar
22. Sumino, K. and Imai, M., to be published.Google Scholar
23. Haas, C., J. Phys. Chem. Solids 15, 108 (1960).Google Scholar
24. Weber, H. Schroter, W. and Haasen, P., Helv. Phys. Acta 41, 1255 (1968).Google Scholar
25. Grazhulis, V. A., Kveder, V. V. and Yu., V., Mukhina, Phys. Stat. Sol. (a) 43,407 (1977).Google Scholar
26. Ono, H. and Sumino, K., Jpn. J. Appl. Phys. 19, L629 (1980).Google Scholar
27. Yonenaga, I., Sumino, K. and Hoshi, K., to be published.Google Scholar
28. Sumino, K., Yonenaga, I. and Abe, T., to be published.Google Scholar
29. Sumino, K. and Yonenaga, I., Jpn. J. Appl. Phys. 20, L685 (1981).CrossRefGoogle Scholar
30. Sumino, K. Yonenaga, I., Harada, H. and Imai, M., Proc. Int. Conf. on Dislocation Modelling of Physical Systems, Gainesville, Ashby, M. F. et al. eds.(1981) pp. 212.Google Scholar
31. Patel, J. R., Discuss. Faraday Soc. 38, 201 (1964).Google Scholar
32. Yonenaga, I. and Sumino, K., Jpn. J. Appl. Phys. 21, 47 (1982).Google Scholar
33. Yasutake, K., Umeo, M. and Kawabe, H., Phys. Stat. Sol. (a) 69, 333(1982).Google Scholar