Fundamental Aspects of Friction and Wear Contacts in <100> Surfaces

Published online by Cambridge University Press:  17 March 2011

William W. Gerberich ,
Natalia I. Tymiak  and
Donald E. Kramer
William W. Gerberich
Affiliation:
Department of Chemical Engineering and Materials ScienceUniversity of Minnesota, Minneapolis, MN 55455
Natalia I. Tymiak
Affiliation:
Department of Chemical Engineering and Materials ScienceUniversity of Minnesota, Minneapolis, MN 55455
Donald E. Kramer
Affiliation:
Now at National Institute for Standards and Technology, Gaithersburg, MD 20899
Get access

Abstract

Unexpected friction and wear transitions occur in transition metals associated with dislocation emission, dislocation storage, and oxide break-through phenomena. Both normal nanoindentation and nanoscratch evaluations of conical diamond tips driven into tungsten {100} single crystal surfaces have been conducted. In terms of initiating plasticity undert the contact, this represents a high Peierl's barrier for dislocation motion in transition metals. Both quasi-equilibrium and kinetic aspects are reported along with current but speculative ideas on multiple friction and wear transitions. Preliminary results show that yielding under contacts can produce a 250 nm displacement excursion. Ramifications are seen in terms of friction coefficients which can double during the near-instantaneous yield excursion but then continue to triple from about 0.05 to 0.15 in the pile-up phase in front of the sliding contact. Implications of how nanotribological issues such as adhesion connect through this mesoscale activity to macroscopic friction and wear are discussed.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 649: Symposium Q – Fundamentals of Nanoindentation & Nanotribology II , 2000 , Q9.1
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Lim, S.C. and Ashby, M.F., Acta Metall., 35, 1 (1987).Google Scholar
2. Blau, P., Friction and Wear Transitions of Materials, (Noyes Publications, Park Ridge, N.J., 1989).Google Scholar
3. OPML Nanomechanics Links, http://web.mit.edu/cortiz/www/nanomechanics.htmlGoogle Scholar
4. Nanoscience: Probing Friction and Rheology on the Nanometer Scale, edMeyer, s. E., Gyalog, T., Overney, R.M. and Dransfeld, K., (World Scientific Publishers, 1999).Google Scholar
5. Kramer, D.E., Yoder, K.B. and Gerberich, W.W., in press, Philos. Mag. (2000).Google Scholar
6. Kramer, D.E., PhD Thesis, University of Minnesota (2000).Google Scholar
7. Chung, Y.-W., Surface Science Investigations in Tribology, eds. Chung, Y.-W., Homda, A.M. and Streat, G.B., ACS Symposium Series 485, 1 (1992).Google Scholar
8. Morris, J.C. and Callahan, D.L., J. Mater. Res., 9, 2907 (1994).Google Scholar
9. Rugar, D. and Hansma, P., Physics Today, 43, No. 10, 23 (1990).Google Scholar
10. Hendriks, C.P., PhD Thesis, Technische Universteit Eindhoven (2000).Google Scholar
11. Bhushan, B. and Koinkar, V.N., J. Appl. Phys., 75, 5741 (1994).Google Scholar
12. Bhushan, B. and Kulkarni, A.V., Thin Solid Films, 278, 49 (1996).Google Scholar
13. Landman, U., Luedtke, W.D., Burhham, N.A. and Colton, R.J., R.J., , Science, 248, 454 (1990).Google Scholar
14. Belak, J. and Stowers, I.F., in Fundamentals of Friction: Macroscopic and Microscopic Processes, eds. singer, I.L. and Pollock, H.M., (Kluwer Academic, The Netherlands, 1992) p. 511.Google Scholar
15. Mikulla, R.P., Hammerberg, J.E., Lomdahl, P.S. and Holian, B.L., Mater. Res. Soc., 522, 385 (1998).Google Scholar
16. Phillips, R., Rodney, D., Shenoy, V., Tadmor, E. and Ortiz, M., Modelling Simul. Mater. Sci. Engng., 7, 769 (1999).Google Scholar
17. Eds. Singer, I.L. and Pollock, H.M., Fundamentals of Friction: Macroscopic and Microscopic Processes (Kluwer Academic, The Netherlands, 1992).Google Scholar
18. Johnson, K.L., in in Fundamentals of Friction: Macroscopic and Microscopic Processes, eds. singer, I.L. and Pollock, H.M., (Kluwer Academic, The Netherlands, 1992) p. 574.Google Scholar
19. Dowson, D., in in Fundamentals of Friction: Macroscopic and Microscopic Processes, eds. singer, I.L. and Pollock, H.M., (Kluwer Academic, The Netherlands, 1992) p. 586.Google Scholar
20. Horstemeyer, M., private communication, Sandia Livermore National Labs (2000).Google Scholar
21. Schwarz, K.W., J. Appl. Phys., 85, 108 (1999).Google Scholar
22. Archard, J.F., Proc. Royal Soc., London, A243, 190 (1959).Google Scholar
23. Giannakopoulos, A.E. and Suresh, S., Acta Mater., 46, No. 1, 177 (1998).Google Scholar
24. Giannakopoulos, A.E., Lindley, T.C. and Suresh, S., Acta Mater., 46, No. 9, 2955 (1998).Google Scholar
25. Gerberich, W.W., Harvey, S.E., Kramer, D.E. and Hoehn, J.W., Acta Mater., 46, No. 14, 5007 (1998).Google Scholar
26. Hainsworth, S.V., Bull, S.J. and Page, T.F., Mater. Res. Soc. Proc., 522, 433 (1998) p. 433.Google Scholar
27. Barceinas-Sanchez, S. and Rainforth, N.M., Acta Mater., 46, No. 8, 6475 (1998).Google Scholar
28. Gerberich, W.W., Venkataraman, S.K., Huang, H., Harvey, S.E. and Kohlstedt, D.L., Acta Metall. Mater., 43, No. 4, 1569 (1995).Google Scholar
29. Tymiak, N.I., Downs, S. and Gerberich, W.W., in preparation (2001).Google Scholar
30. Kapoor, A. and Johnson, K.L., Int. J. Mech. Sci., 34, No. 3, 223 (1992).Google Scholar
31. Kapoor, A., Wear, 233–235, 182 (1999).Google Scholar