Fracture Behavior of Vanadium/Vanadium Silicide In-Situ Composites

Published online by Cambridge University Press:  01 January 1992

M. J. Strum  and
G. A. Henshall
M. J. Strum
Affiliation:
Lawrence Livermore National Laboratory, P.O. Box 808, Livermore, CA 94550.
G. A. Henshall
Affiliation:
Lawrence Livermore National Laboratory, P.O. Box 808, Livermore, CA 94550.
Get access

Abstract

The fracture behavior of V-V3Si in-situ composite alloys has been evaluated for intermetallic phase fractions of 30, 50, and 70 volume percent. In addition, the mechanical properties of the ductile constituent in these composites have been evaluated from two alloys containing silicon at its solubility limit in vanadium at the eutectic temperature and at 1400°C. The fracture toughness was found to increase monotonically with increasing volume fraction of the ductile phase. Fractography has shown evidence of crack bridging by the vanadium solid solution phase and increased ductility within the composite relative to bulk measurements. The toughness results are compared with predictions based on an existing model of ductile-phase toughening using our measurements of component properties.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 288: Symposium L – High-Temperature Ordered Intermetallic Alloys V , 1992 , 1093
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Mendiratta, M. G., Lewandowski, J. J., and Dimiduk, D. M., Metall. Trans. 22A, 1573–1583 (1991).Google Scholar
2. Sigl, L. S., Mataga, P. A., Dalgleish, B. J., McMeeking, R. M., and Evans, A. G., Acta Metall. 36, 945–953 (1988).Google Scholar
3. , J. F. , Smith, Ed., Phase Diagrams of Binary Vanadium Alloys, ASM International, Metals Park, OH (1989).Google Scholar
4. Chang, K.-M., Bewlay, B.P., Sutliff, J.A. and Jackson, M.R., JOM 44, 59–63 (1992).Google Scholar
5. Evans, A.G., “Fracture Toughness: The Role of Indentation Techniques”, Fracture Mechanics Applied to Brittle Materials, ASTM STP 678, Freiman, S. W., Ed., American Society for Testing and Materials, pp. 112–135 (1979).Google Scholar
6. Strum, M.J. and Wagner, L.M., “Interstitial Embrittlement in Vanadium Laser Welds,” Proc. Intl. Conf. on Lasers, Duerte, F. J. and Herns, D. G., eds. STS Press, McLean, VA, pp. 474–478 (1992).Google Scholar
7. Ashby, M. F., Blunt, F. J. and Bannister, M., Acta Metall. 37, 1847–1857 (1989).Google Scholar
8. Ravichandran, K. S., Scr. Metall. Mater. 26, 1389–1393 (1992).Google Scholar
9. Ravichandran, K. S., Acta Metall. Mater. 40, 1009–1022 (1992).Google Scholar