EPR Studies of E-Beam and Gamma Irradiated ZnGeP2: A Nonlinear Optical Material for the Infrared

Published online by Cambridge University Press:  21 February 2011

M.H. Rakowsky ,
W.J. Lauderdale ,
R. A. Mantz ,
R. Pandey  and
P.J. Drevinsky
M.H. Rakowsky
Affiliation:
Frank J. Seiler Research Laboratory, USAF Academy, CO 80840–6272
W.J. Lauderdale
Affiliation:
Frank J. Seiler Research Laboratory, USAF Academy, CO 80840–6272
R. A. Mantz
Affiliation:
Phillips Laboratory, Edwards AFB, CA 93524–7680
R. Pandey
Affiliation:
Department of Physics, Michigan Technological University, Houghton, MI 49931
P.J. Drevinsky
Affiliation:
Phillips Laboratory, Hanscom AFB, MA 01731–2090
Get access

Abstract

Zinc germanium phosphide is a nonlinear optical material for efficient frequency conversion in the mid-IR spectral region. One challenge in the development of ZnGeP2 is to reduce the near band edge absorption in the 0.7 to 2.5 micron region. Several methods have been used to ascertain the origin of this absorbance. One method, electron paramagnetic resonance (EPR), has been used to characterize the paramagnetic native acceptor in ZnGeP2 by studying as-grown, thermally annealed, electron-beam irradiated, and gamma irradiated single crystals. Each of the these processing routines improves the optical transparency with a concurrent decrease in the concentration of paramagnetic centers and defect site symmetry as seen in the EPR spectra. High energy e-beam and gamma irradiation may cause compensation, movement, or creation of new defects. In addition, nuclear magnetic resonance (NMR) has been used to further characterize several samples of as-grown, annealed and polycrystalline ZnGeP2. Preliminary calculations of the defect energetics have been conducted using atomistic simulation techniques employing the shell model to describe the lattice. Interionic potentials between the constituent ions were obtained by performing quantum cluster calculations on ZnGeP2.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 354: Symposium A – Beam Solid Interactions for Materials Synthesis and Characterization , 1994 , 735
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Barnes, N. P., International Journal of Nonlinear Optical Physics 1, 639 (1991).Google Scholar
2 Shay, J. L. and Wernick, J. H., Ternary Chalcopyrite Semiconductors: Growth, Electronic Properties, and Applications (Pergamon Press, New York, 1975).Google Scholar
3 (a) Drevinsky, P. J., Schunemann, P. G., Pollak, T. M., Ohmer, M. C., “Gamma Ray Processing of ZnGeP2, a Non-Linear Optical Material for the Infrared”, this volume (b) P. J. Drevinsky, P. G. Schunemann, T. M. Pollak, M. C. Ohmer, W. C. Mitchel, N. C. Fernelius, “Electron Beam Processing of ZnGeP2, a Non-Linear Optical Material for the Infrared”, this volume.Google Scholar
4 Lind, M. D. and Grant, R. W., J. Chem. Phys. 58, 357 (1973).Google Scholar
5 Rakowsky, M. H., Kuhn, W. K., Lauderdale, W. J., Halliburton, L. E., Edwards, G. J., Scripsick, M. P., Schunemann, P. G., Pollak, T. M., Ohmer, M. C., Hopkins, F. K., Appl. Phys. Lett. 64, 1615(1994).Google Scholar
6 (a) Hobgood, H. M., Henningsen, T., Thomas, R. N., Hopkins, R. H., Ohmer, M. C., Mitchel, W. C., Fischer, D. W., Hegde, S. M., Hopkins, F. K., J. Appl. Phys. 73, 4030 (1993) (b) J. E. McCrae, Jr., M. R. Gregg, R. L. Hengehold, Y. K. Yeo, P. H. Ostdiek, M. C. Ohmer, S. M. Hegde, P. G. Schunemann, T. M. Pollak, Appl. Phys. Lett. 64, 3142 (1994).Google Scholar
7 Eckert, H., Prog, in NMR Spectroscopy 24, 159 (1992).Google Scholar
8 Rakowsky, M. H., Mantz, R. A., Otonari, Y. A., “3,P MAS NMR Study of Single-Crystal and Polycrystalline ZnGeP', submitted, Chem. Mater.Google Scholar
9 Electron beam irradiaton: Samples of ZnGeP2 were irradiated with 1 MeV electrons from the Phillips Laboratory Dynamitron accelerator. Typical fluences were 2 × 1018 electrons per cm2 as measured by a Faraday cup. The flux was approximately 1.4 × 1014 electrons per cm2 per sec. Samples were clipped to a specially fabricated hold which featured four jets fashioned from copper tubing through which liquid nitrogen slowly sprayed over the sample surface in order to prevent a large temperature rise during irradiation. The temperature was maintained at 0° C (or below) to minimize thermal annealing of radiation-induced defects during irradiation.Google Scholar
10 Gamma-ray irradiation: The Phillips Laboratory 60Co source provided the penetrating ionizing radiation to allow processing of relatively thick samples of ZnGeP2. The 40 kiloCurie source emits y rays with energies of 1.173 and 1.332 MeV. Samples were exposed to an average flux of 4.8 × 106 rads/hr for total doses varying from about 0.5 to 1 × 1018 electrons/cm2 (2.5 MeV equivalent). The temperature at the sample position within the source configuration was approximately 100° C. The source itself consisted of a circular array of 20 stainless steel tubes containing 60Co slugs and, when in use, was normally located in a shielded pit.Google Scholar
11 Schunemann, P. G. and Pollak, T. M., in OSA Proceedings on Advanced Solid-State Lasers, edited by Dube, George and Chase, Lloyd (Optical Society of America, Washington, D.C., 1991), Vol. 10, pp. 332–334.Google Scholar