X-ray Absorption Fine Structure Studies of Speciation of Technetium in Borosilicate Glasses

Published online by Cambridge University Press:  01 February 2011

Wayne W. Lukens
Affiliation:
Chemical Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA 94720, USA.
David K. Shuh
Affiliation:
Chemical Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA 94720, USA.
Isabelle S. Muller
Affiliation:
Vitreous State Laboratory, The Catholic University of America, Washington, D.C. 20064, USA.
David A. McKeown
Affiliation:
Vitreous State Laboratory, The Catholic University of America, Washington, D.C. 20064, USA.
Get access

Abstract

A series of glass samples were prepared analogously to high level waste glass using either glass frit or glass precursors combined with a high level waste surrogate containing NaTcO4. Three different technetium species were observed in these glasses depending upon the synthesis conditions. If the glasses were prepared by reducing NaTcO4 to TcO2•2H2O with hydrazine or if a large amount of organic material was present, inclusions of TcO2 were observed. If no organic material was present, technetium was incorporated as TcO4. If only a small amount of organic material was present, isolated Tc(IV) sites were observed in the glass. The relative technetium retention of these glasses was estimated from the Tc K-edge height, and had no correlation with the oxidation state of the technetium. Pertechnetate was well retained in these glasses.

Type
Research Article
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Langowski, M.; Darab, J.; Smith, P.Volatility Literature of Chlorine, Iodine, Cesium, Strontium, Technetium and Rhenium; Technetium and Rhenium Volatility Testing,” PNNL-11052, Pacific Northwest National Laboratory, 1996.Google Scholar
2. Darab, J.; Smith, P. Chem. Mater. 1996, 8, 1004.Google Scholar
3. Antonini, M.; Merlini, A.; Thornley, R. J. Non-Cryst. Sol. 1985, 71, 219.Google Scholar
4. Bucher, J. J.; Allen, P. G.; Edelstein, N. M.; Shuh, D. K.; Madden, N. W.; Cork, C.; Luke, P.; Pehl, D.; Malone, D. Rev. Sci. Instrum. 1996, 67, 4.Google Scholar
5. Lukens, W. W.; Bucher, J. J.; Edelstein, N. M.; Shuh, D. K. Environ. Sci. Technol. 2002, 36, 1124.Google Scholar
6. Golcar, G. R.; Colton, N. G.; Darab, J. G.; Smith, H. D.Hanford Waste Tank Simulants Specification and Their Applicability for the Retrieval, Pretreatment, and Vitrification Process,” PNWD-2455, Pacific Northwest National Laboratory, 2000.Google Scholar
7. Freude, E.; Lutze, W.; Russel, C.; Schaeffer, H. Mat. Res. Soc. Symp. Proc. 1989, 127, 199.Google Scholar
8. Almahamid, I.; Bryan, J. C.; Bucher, J. J.; Burrell, A. K.; Edelstein, N. M.; Hudson, E. A.; Kaltsoyannis, N.; Lukens, W. W.; Shuh, D. K.; Nitsche, H.; Reich, T. Inorg. Chem. 1995, 34, 193.Google Scholar
9. Nelson, C.; Boyd, G.; Smith, W. J. Am. Chem. Soc. 1954, 76, 348.Google Scholar
10. Spitsyn, V.; Kuzina, A.; Oblova, A.; Shakh, G.; Gavrish, A.; Belyaeva, L. Russ. J. Inorg. Chem. 1978, 23, 484.Google Scholar