Kinetics of Intrinsic and Dopant-Enhanced Solid Phase Epitaxy in Buried Amorphous Si Layers

Published online by Cambridge University Press:  03 September 2012

J. C. McCallum
J. C. McCallum*
Affiliation:
Microanalytical Research Centre, School of Physics, University of Melbourne, Parkville, Victoria 3052, Australia, jcm@physics.unimelb.edu.au
Get access

Abstract

The kinetics of intrinsic and dopant-enhanced solid phase epitaxy (SPE) have been measured in buried amorphous Si (a-Si) layers produced by ion implantation. Buried a-Si layers formed by self-ion implantation provide a suitable environment for studies of the intrinsic growth kinetics of amorphous Si, free from the rate-retarding effects of H. For the first time, dopant-enhanced SPE rates have been measured under these H-free conditions. Buried a- Si layers containing uniform As concentration profiles ranging from 1–16.1 × 1019 As.cm-3 were produced by multiple-energy ion implantation and time resolved reflectivi[ty was used to measure SPE rates over the temperature range 480–660°C. In contrast to earlier studies, the dopant-enhanced SPE rate is found to depend linearly on the As concentration over the entire concentration range measured. The SPE rate can be expressed in the form, v/vi(T) = 1 + N/[No exp(−Λ E/kT)], where vi(T) is the intrinsic SPE rate, N is the dopant concentration and No = 1.2 × 1021 cm-3, ΔE = 0.21 eV.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 438: Symposium A – Materials Modificaton and Synthesis by Ion Beam… , 1996 , 119
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] For a review, see Olson, G. L. and Roth, J. A., in Handbook of Crystal Growth 3, ed. Hurle, D. T. J., Elsevier, Amsterdam, 1994, pp. 255–312.Google Scholar
[2] Walser, R. M. and Jeon, Y. J., Mater. Res. Soc. Symp. Proc. 205, pp. 27–32 (1992) and references therein.Google Scholar
[3] Lu, G. Q., Nygren, E. and Aziz, M. J., J. Appl. Phys. 70, pp. 5323–5345 (1991).Google Scholar
[4] Wautelet, M., Semicond. Sci. Technol. 4, pp. 685–686 (1989).Google Scholar
[5] Roth, J. A., Olson, G. L., Jacobson, D. C. and Poate, J. M., Appl. Phys. Lett. 57, pp. 1340–1342 (1990).Google Scholar
[6] McCallum, J. C., Appl. Phys. Lett. 69, pp. 925–927 (1996).Google Scholar
[7] Jeon, Y. J., Becker, M. F. and Walser, R. M., Mater. Res. Soc. Symp. Proc. 157, pp. 745–750 (1990).Google Scholar