Diffusion and Defect Structure in Nitrogen Implanted Silicon
Published online by Cambridge University Press: 21 March 2011
Nitrogen diffusion and defect structure were investigated after medium to high dose nitrogen implantation and anneal. 11 keV N2+ was implanted into silicon at doses ranging from 2×1014 to 2×1015 cm−2. The samples were annealed with an RTA system from 750°C to 900°C in a nitrogen atmosphere or at 1000°C in an oxidizing ambient. Nitrogen profiles were obtained by SIMS, and cross-section TEM was done on selected samples. TOF-SIMS was carried out in the oxidized samples. For lower doses, most of the nitrogen diffuses out of silicon into the silicon/oxide interface as expected. For the highest dose, a significant portion of the nitrogen still remains in silicon even after the highest thermal budget. This is attributed to the finite capacity of the silicon/oxide interface to trap nitrogen. When the interface gets saturated by nitrogen atoms, nitrogen in silicon can not escape into the interface. Implant doses above 7×1014 create continuous amorphous layers from the surface. For the 2×1015 case, there is residual amorphous silicon at the surface even after a 750°C 2 min anneal. After the 900°C 2 min anneal, the silicon fully recrystallizes leaving behind stacking faults at the surface and residual end of range damage.
- Research Article
- MRS Online Proceedings Library (OPL) , Volume 669: Symposium J – Si Front-End Processing–Physics and Technology of Dopant-Defect Interactions III , 2001 , J6.4
- Copyright © Materials Research Society 2001