Temperature Effect on the Quality of A1N thin Films

Published online by Cambridge University Press:  13 June 2014

Margarita P. Thompson
Affiliation:
CH&MSE Dept., Wayne State University, Detroit, MI 48202
Andrew R. Drews
Affiliation:
ECE Dept., Wayne State University, Detroit, MI 48202
Changhe Huang
Affiliation:
Physics Dept., Scientific Research Laboratories, Ford Motor Company, Dearborn, MI 48121
Gregory W. Auner
Affiliation:
Physics Dept., Scientific Research Laboratories, Ford Motor Company, Dearborn, MI 48121

Abstract

AlN thin films were deposited at various substrate temperatures via Plasma Source Molecular Beam Epitaxy. The films were grown on 6H-SiC (0001) substrates. Reflection High Energy Electron Diffraction and Atomic Force Microscopy showed a dramatic change in the surface morphology of the film grown at 640°C. This is attributed to a change in the growth mechanism from pseudomorphic at lower temperatures to three-dimensional at higher than 640°C temperatures. Photoreflectance measurements showed an absorption shift toward 200 nm as the deposition temperature increases which is attributed to the change in the growth mechanism at higher temperatures. X-Ray Diffraction was unable to conclusively determine the AlN (0002) peak due to a significant diffuse intensity from the SiC (0002) peak. A MIS structure was created by depositing Pt contacts on the film grown at 500°C. I-V measurements showed that the Pt/AlN contact is Schottky.

Type
Research Article
Copyright
Copyright © 1999 Materials Research Society

Introduction

AlN is a group III-V nitride wide bandgap semiconductor. Its bandgap, the largest among the III-V nitrides, gives AlN an array of interesting properties including: high degree of hardness, high thermal and chemical stability, and high thermal conductivity [Reference Strite and Morkoç1-Reference F. Davis3]. One major area where these properties can find application is in the construction of high-power, high- temperature devices which can operate in harsh conditions. Of particular interest is the possibility for using AlN as an insulator in SiC-based MIS structures [Reference Tin, Song and Isaacs-Smith4]. Such devices can operate at temperatures as high as 550°C while ordinary Si-based devices fail at around 120°C. At the same time AlN/SiC-based devices will be less susceptible to radiation damage.

However, prior to designing AlN-based devices, a number of materials issues need to be resolved. Two important problems are: i) finding a technique and optimal growth conditions for depositing stoichiometric AlN films of high purity and low defect density; ii) finding a substrate material which closely matches the lattice parameter and thermal expansion coefficient of AlN.

Here we report a systematic study of the effect of substrate temperature on the crystal quality of AlN thin films grown on 6H-SiC (0001) substrates via Plasma Source Molecular Beam Epitaxy (PSMBE). Our understanding of the growth mechanisms of AlN in the PSMBE system at various temperatures is presented.

Experiment

All AlN films were deposited on pieces from a single 6H-SiC (0001) wafer which was obtained from Advanced Technology Materials in 1994. The substrate was n-type with carrier concentration of 4.8x1018 cm−3. The films were deposited on the Si-face of the substrate. 6H-SiC was chosen as a substrate for AlN growth because of: (i) their close lattice parameter and thermal expansion coefficient match, and (ii) to study the properties of AlN/SiC MIS structures. Each substrate was ultrasonically degreased for 20 minutes in acetone and methanol in succession, followed by a one-minute etch in 10% (by volume) HF for removing any SiOx from the surface. Prior to deposition, each substrate was preheated in the PSMBE system above 850°C for one hour for degassing. Deposition of AlN films was accomplished using a unique technique developed in our laboratory called Plasma Source Molecular Beam Epitaxy (PSMBE). The PSMBE system has a new and innovative deposition source which includes a magnetically enhanced, r. f. powered hollow cathode, lined with high purity aluminum. A mixture of high purity argon and nitrogen is supplied to the hollow cathode, where a plasma consisting of high energy aluminum, argon, and nitrogen is formed. A flux containing predominantly Al+ and N+ ions of energies around 1 eV leaves the hollow cathode source. This flux is further accelerated by negative bias applied to the substrate. The PSMBE system is described in detail elsewhere[Reference Lenane, Ahmad, Naik, Kuo, Wu and Prelas5].

AlN films were grown at 440°C, 500°C, 560°C, 640°C, and 800°C using a substrate bias voltage of -15 eV which is optimum for our PSMBE system. All films had a thickness of approximately 2000 Å as measured by a piezoelectric thickness monitor. The films were characterized in-situ by Reflection High Energy Electron Diffraction (RHEED) and ex-situ by Atomic Force Microscopy (AFM), X-Ray Diffraction (XRD), and optical reflectance. The AFM characterization was performed using a Digital Instruments Nanoscope III operating in contact mode with standard Si3N4 tips. The films were characterized by XRD in a Scintag X1 θ-θ diffractometer using Cu radiation. The samples were supported on a zero-background quartz plate and data were collected either in symmetric (Bragg-Brentano) scans or in rocking scans. For optical reflection measurements a Lambda 900 UV/Vis/NIR Spectrometer with range 180-3,000 nm was used. For electrical measurements, Pt electrodes were deposited in a dc- magnetron sputtering system on the sample grown at 500°C. Blanket electrodes were deposited on the bottom surface of the SiC substrates and top circular contacts with a diameter of 1 mm were deposited on the films surface through a hard mask. C-V characterization was performed using a HP4192A LF impedance analyzer at frequencies of 1 MHz. I-V measurements were performed on a HP4140B pico-ammeter with a dc-voltage source. A heated chuck was used to reach temperatures up to 300oC.

Results and Discussion

AFM revealed a number of scratches on the substrates surface. The depth of the more profound scratches was around 2 nm as determined by AFM. Following a degassing procedure lasting one hour at 850°C, RHEED studies of the 6H-SiC substrates gave patterns with streaks which is an indication of relatively smooth surfaces with terraces and steps.

As-grown AlN films did not display similar streaking, but rather oblong spots, indicative of facetted islands on the surface. The RHEED pattern from the film deposited at 640°C consists of round spots which shows that the surface is rough and the pattern is due to transmission through surface asperities rather than reflection from the surface. Figure 1 shows AFM images and RHEED patterns of the films grown at 500°C, 640°C, and 800°C. The film grown at 640°C has the greatest roughness and the largest substrate features among all the films. The films grown at temperatures lower than 640°C have small surface features very similar to the 500°C film. The film deposited at 800°C shows unusually shaped features. From the surface analysis one can conclude that at around 640°C a change in the growth mechanism occurs. At lower temperatures the depositing species do not have enough energy for lateral movement on the surface. The growth is pseudomorphic which results in smooth but strained films. At around 640°C the growth changes to three-dimensional and the film grows in columns. As the deposition temperature increases the films get smoother. This model is in agreement with our previous studies [Reference Lenane, Ahmad, Naik, Kuo, Wu and Prelas5, Reference Lekova, Auner, Jin, Naik and Naik6] on the temperature effect on the quality of AlN films deposited on silicon, sapphire, and Lely grown substrates.

Figure 1 AFM images and RHEED patterns of the films grown at 500°C, 640°C, and 800°C. The film deposited at 640°C has the greatest roughness and the largest surface features.

Symmetric XRD scans on all the samples displayed significant intensity from the SiC (0002) peak near 2θ=35.7° that severely overlaps the AlN (0002) peak, despite the intentional 3.5° off-cut of the substrates. Figure 2a represents a symmetric scan on the AlN film grown at 800°C.

Figure 2. a) A symmetric XRD scan on the film grown at 800°C and the standard AlN (-1100), (0002), and (-1101) peaks. b) Rocking scan about the 6H-SiC (0002) peak.

An increased intensity around AlN (0002) peak at around 2θ=36° can be observed. However, rocking scans about the SiC (0002) peak (Fig.2b) showed that the substrates are not single crystals, and typically contain a spread in orientation of about 4 degrees. Figure 2b shows a rocking curve about the 6H-SiC (0002) peak of another piece from the same wafer illustrating a miscut, larger than the specified one, as well as the wide orientation spread. In addition to the strong crystalline peaks seen in the rocking scans a significant fraction of the SiC (0002) intensity is diffuse. Due to this diffuse “halo” we are unable to conclusively determine whether we have observed the AlN (0002) peak. However, RHEED data indicates textured AlN growth.

Figure 3 shows photoreflectance measurements for all five films in the wavelength interval between 180 and 800 nm. All reflectance curves are characterized with one large peak in the interval 209-230 nm depending on the growth temperature. The films grown at temperatures lower than 640°C indicate a peak reflectivity of 37-40% in the range 209-216 nm with a decrease in reflectance at lower wavelengths probably due to absorption at the AlN bandgap. In high quality AlN, absorption should occur at around 200 nm which corresponds to an energy of 6.2 eV. The absorption of the films grown at lower temperatures is shifted to lower wavelengths due to a strained growth. At growth temperatures of 640°C and higher, the shift in absorption is observed towards 200 nm which, to our understanding, is due to a change in the growth mode which causes strain relaxation in the film. This conclusion is in agreement with the surface analysis data discussed above.

Figure 3. Photoreflectance measurements for all AlN films.

Capacitance-voltage (C-V) and current-voltage (I-V) measurements were performed at room temperature and 300°C on the film grown at 500°C. Due to the shorting of the contacts on all of the other samples, C-V and I-V measurements could only be performed on the film grown at 500°C. We believe that the contact shorting in the other samples is caused by small crystallites on the substrate surface which were visible under optical microscope. This is an example of the critical impact of the substrate surface quality on the performance of device structures. C-V measurements are shown in Figure 4a. A small hysteresis loop was observed both at room temperature and 300°C, which is an indication of the presence of trapping centers. Another feature of the C-V curve is the presence of a shoulder at room temperature and 300°C. However, at 300°C this shoulder is shifted toward lower voltages. Figure 4a also shows that the C-V curve measured at 300°C is shifted in the negative bias direction compared to the curve obtained at room temperature. This observation is similar to that reported by Tin et al. [Reference Tin, Song and Isaacs-Smith4]. They attribute this shift to the activation of fixed positively charged states in the AlN layer at the film/substrate interface at elevated temperatures. The I-V characteristics at room temperature and 300°C are shown in Figure 4b. The sample has high leakage currents at both temperatures. Although the leakage current at 300°C is slightly higher it did not damage the sample. The I-V curves were repeatable even after multiple cycles of heating to 300°C and cooling back to room temperature. The high leakage current as well as the hysteresis loop in the C-V curves may be due to high defect density in the film grown at 500°C. RHEED, AFM and optical reflection measurements confirm that the defect density of this film is high. In addition, the SiC crystallites protrude through the film to within a very close distance to the contacts. Thus, the distance between a contact and the SiC substrate at the points of protrusion could be only a few hundred Å which may partly account for the high leakage current. The defect density in the samples grown at higher temperatures is expected to be smaller and we would expect better C-V and I-V characteristics.

Figure 4. a) Capacitance-Voltage and b) Current-Voltage curves for the AlN film deposited at 500°C.

Conclusions

A systematic study of the effect of deposition temperature on the AlN crystalline quality was performed. Surface analysis including RHEED and AFM showed that around 640°C the growth mode changes from pseudomorphic to three dimensional. Temperatures higher than 640°C tend to give smoother films. Due to a high diffuse intensity of the SiC (0002) peak, XRD scans could not conclusively determine that the higher intensity at 2θ=36° is due to the AlN (0002) peak. Photoreflectance measurements showed an absorption shift toward 200 nm as the deposition temperature of the films increased. Electrical measurements on the film deposited at 500°C°showed that the Pt/AlN contacts are Schottky. C-V measurements showed a small hysteresis loop both at room temperature and 300°C. The C-V curve at 300°C was shifted toward lower negative voltages.

Acknowledgments

The authors wish to acknowledge support for this research by the National Science Foundation (Grant No. DGE-9870720) and the Institute for Manufacturing Research at WSU. We would also like to acknowledge Dr. Guang-Zhao Mao, Jie Xu, and Quiang Zhao for their support and contribution in conducting the experiments.

Footnotes

MRS Internet J. Nitride Semicond. Res. 4S1, G3.7 (1999)

References

Strite, S. and Morkoç, H., J. Vac. Sci. Technol. B 10 (1992) 1237 Google Scholar
Edgar, J. H., J. Mater. Res. 7 (1992) 235 Google Scholar
F. Davis, Robert, Proceedings of the IEEE 79 (1991) 702 CrossRefGoogle Scholar
Tin, C. C., Song, Y., Isaacs-Smith, T., J. Electron. Mater. 26 (1997) 212 Google Scholar
, G. W., Lenane, T. D., Ahmad, F., Naik, R., Kuo, P. K., Wu, Z., “Epitaxial growth of AlN by plasma source molecular beam epitaxy”, Prelas, M. A. et al., “Wide Band Gap Electronic Materials329, (1995) Kluwer Academic Publishers, Printed in Netherlands Google Scholar
Lekova, M., Auner, G. W., Jin, F., Naik, R., Naik, V., Mat. Res. Soc. Symp. Proc. 449 (1997) 245 Google Scholar
Figure 0

Figure 1 AFM images and RHEED patterns of the films grown at 500°C, 640°C, and 800°C. The film deposited at 640°C has the greatest roughness and the largest surface features.

Figure 1

Figure 2. a) A symmetric XRD scan on the film grown at 800°C and the standard AlN (-1100), (0002), and (-1101) peaks. b) Rocking scan about the 6H-SiC (0002) peak.

Figure 2

Figure 3. Photoreflectance measurements for all AlN films.

Figure 3

Figure 4. a) Capacitance-Voltage and b) Current-Voltage curves for the AlN film deposited at 500°C.