A study of pest oxidation in polycrystalline MoSi2

Published online by Cambridge University Press:  31 January 2011

C.G. McKamey ,
P.F. Tortorelli ,
J.H. DeVan  and
C.A. Carmichael
C.G. McKamey
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6115
P.F. Tortorelli
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6115
J.H. DeVan
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6115
C.A. Carmichael
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6115
Get access

Abstract

MoSi2 is a promising high-temperature material with low density (6.3 g/cm3), high melting point (2020 °C), and good oxidation resistance at temperatures to about 1900 °C. However, in the intermediate temperature range between 400 and 600 °C, it is susceptible to a “pest” reaction which causes catastrophic disintegration by a combination of oxidation and fracture. In this study, we have used polycrystalline MoSi2, produced by arc-casting of the pure elements and by cold and hot pressing of alloy powders, to characterize the pest reaction and to determine the roles of composition, grain or phase boundaries, and physical defects on the oxidation and fracture of specimens exposed to air at 500 °C. It was found that pest disintegration occurs through transport of oxygen into the interior of the specimen along pre-existing cracks and/or pores, where it reacts to form MoO3 and SiO2. The internal stress produced during the formation of MoO3 results in disintegration to powder. Near the stoichiometric ratio, the susceptibility to pest disintegration increases with increasing molybdenum content and with decreasing density. Silicon-rich alloys were able to form protective SiO2 and showed no indication of disintegration, even at densities as low as 60%.

Type
Articles
Information
Journal of Materials Research , Volume 7 , Issue 10 , October 1992 , pp. 2747 - 2755
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Fleischer, R.L., J. Metals 37 (12), 16 (1985).Google Scholar
2Meschter, P.J. and Schwartz, D.S., J. Metals 41 (11), 52 (1989).Google Scholar
3Vasudevan, A. K. and Petrovic, J.J., to be published in proceedings of High Temperature Structural Silicides Workshop, held Gaithersburg, MD, Nov. 1991.Google Scholar
4Schlichting, K., High Temp.-High Press. 10, 241 (1978).Google Scholar
5Carter, D. H., Petrovic, J. J., Honnell, R. E., and Gibbs, W. S., Ceram. Eng. Sci. Proc. 10 (9-10), 1121 (1989).Google Scholar
6Petrovic, J. J., Honnell, R. E., and Vasudévan, A. K., in Intermetallic Matrix Composites, edited by Anton, D. L., Martin, P. L., Miracle, D. B, and McMeeking, R. (Mater. Res. Soc. Symp. Proc. 194, Pittsburgh, PA, 1990), p. 123.Google Scholar
7Carter, D. H. and Martin, P. L., in Intermetallic Matrix Compos ites, edited by Anton, D.L., Martin, P.L., Miracle, D.B., and McMeeking, R. (Mater. Res. Soc. Symp. Proc. 194, Pittsburgh, PA, 1990), p. 131.Google Scholar
8Lu, T. C., Evans, A. G., Hecht, R. J., and Mehrabian, R., Acta Metall. Mater. 39 (8), 1853 (1991).Google Scholar
9Yang, J-M., Kai, W., and Jeng, S.M., Scripta Metall. 23, 1953 (1989).Google Scholar
10Maloy, S., Heuer, A. H., Lewandowski, J., and Petrovic, J., J. Am. Ceram. Soc. 74 (10), 2704 (1991).CrossRefGoogle Scholar
11Lee, E.W., Cook, J., Khan, A., Mahapatra, R., and Waldman, J., JOM 43 (3), 54 (1991).CrossRefGoogle Scholar
12Chang, Y.A., J. Mater. Sci. 4, 641 (1969).CrossRefGoogle Scholar
13Meschter, P.J., in High-Temperature Ordered Intermetallic Alloys IV, edited by Johnson, L. A., Pope, D. P., and Stiegler, J. O. (Mater. Res. Soc. Symp. Proc. 213, Pittsburgh, PA, 1991), p. 1027.Google Scholar
14Wirkus, C.D. and Wilder, D.R., J. Am. Ceram. Soc. 49, 173 (1966).CrossRefGoogle Scholar
15Falco, J. J. and Levy, M., J. Less-Common Met. 20, 291 (1970).CrossRefGoogle Scholar
16Fitzer, E., in Warmfeste und Korrosionsbestdndige Sinterwerkstoffe, Proceedings of 2nd Plansee Seminar, 1955, edited by Benesovsky, F. (Pergamon Press, Elmsford, NY, 1956), p. 56.Google Scholar
17Berkowitz-Mattuck, J.B., Rossetti, M., and Lee, D.W., Metall. Trans. 1, 479 (1970).CrossRefGoogle Scholar
18Bartlett, R. W., McCamont, J. W., and Gage, P. R., J. Am. Ceram. Soc. 48, 551 (1965).CrossRefGoogle Scholar
19Meier, G. H., to be published in proceedings of High Temperature Structural Silicides Workshop, held in Gaithersburg, MD, Nov. 1991.Google Scholar
20Schnabel, H., Ph.D. Dissertation, Universitiit Karlsruhe, 1965.Google Scholar
21Fitzer, E. and Matthias, K., High Temp. Sci. 3, 93 (1971).Google Scholar
22McKamey, C.G., Tortorelli, P.F., and Hirano, T., Oak Ridge National Laboratory, Oak Ridge, TN, and National Research Institute for Metals, Tokyo, Japan, unpublished results, 1991.Google Scholar
23Hilliard, J.E. and Cahn, J. W., Trans. AIME 221, 344 (1961).Google Scholar
24Chou, T. C. and Nieh, T. G., to be published, 1992.Google Scholar
25Tuominen, S.M. and Dahl, J.M., J. Less-Common Met. 81, 249 (1981).CrossRefGoogle Scholar
26McKamey, C. G. and Tortorelli, P. F., Oak Ridge National Laboratory, Oak Ridge, TN, unpublished results, 1991.Google Scholar