Skip to main content Accessibility help

We use cookies to distinguish you from other users and to provide you with a better experience on our websites. Close this message to accept cookies or find out how to manage your cookie settings.

Close cookie message
×
  1. Home
  2. Search

Refine search

Refine search

Access:
Content type:
Publication date:
Apply   From and To filters
Subject: Show more
Journals Show more
Publishers: Show more
Societies Show more
Series: Show more
Collections: Show more

Actions for selected content:

Select all | Deselect all
  • View selected items
  • Export citations
  • Download PDF (zip)
  • Save to Kindle
  • Save to Dropbox
  • Save to Google Drive

Save Search

You can save your searches here and later view and run them again in "My saved searches".

Please provide a title, maximum of 40 characters.
Cancel
×

1 results

  • Pressure Studies for 1111 and 11 Type Iron-based Superconductors

  • Hiroki Takahashi, Hironari Okada, Hiroyuki Takahashi, Yoichi Kamihara, Satoru Matsuishi, Masahiro Hirano, Hideo Hosono, Yoshikazu Mizuguchi, Yoshihiko Takano
  • Journal:
    MRS Online Proceedings Library Archive / Volume 1254 / 2010
    Published online by Cambridge University Press:
    01 February 2011, 1254-L02-02
    Print publication:
    2010

  • In the recent development of the studies in iron-based superconductors, high-pressure experiments have been played an important role. Large enhancement of Tc with applying pressure and pressure-induced superconductivity were reported in LaFeAsO1-xFx. In this work, electrical, magnetic and structural measurements on 1111 type Ca(Fe1-xCox)AsF and 11 type Fe(Se1-xTex)0.92 under high pressure have been performed. For Ca(Fe1-xCox)AsF, the substitution of Co suppressed the magnetic and structural transitions and raised superconductivity. Pressure-induced superconductivity was observed for x = 0.0 and 0.05. The highest Tc was obtained in parent compound under high pressure, in contrast to LaFeAsO1-xFx. These results suggest that the substitution of Co increases carrier concentration and induces disorder in the FeAs superconducting layer. For FeTe0.92, pressure-induced superconductivity was not detected under high pressure up to 19 GPa, although the resistive anomaly due to the structural and magnetic phase transition was suppressed by applying pressure.