Skip to main content Accessibility help

We use cookies to distinguish you from other users and to provide you with a better experience on our websites. Close this message to accept cookies or find out how to manage your cookie settings.

Close cookie message
×
  1. Home
  2. Search

Refine search

Refine search

Access:
Content type:
Publication date:
Apply   From and To filters
Subject: Show more
Journals Show more
Publishers: Show more
Societies Show more
Series: Show more
Collections: Show more

Actions for selected content:

Select all | Deselect all
  • View selected items
  • Export citations
  • Download PDF (zip)
  • Save to Kindle
  • Save to Dropbox
  • Save to Google Drive

Save Search

You can save your searches here and later view and run them again in "My saved searches".

Please provide a title, maximum of 40 characters.
Cancel
×

1 results

  • Pulsed Laser Deposition of Silicon Nanostructures

  • P. Bruno, T. Salve, V. Russo, D. Dellasega, G. Filoni, C.S. Casari, C.E. Bottani, A. Li Bassi
  • Journal:
    MRS Online Proceedings Library Archive / Volume 1322 / 2011
    Published online by Cambridge University Press:
    21 September 2011, mrss11-1322-b05-34
    Print publication:
    2011

  • Silicon nanostructures embedded in an amorphous matrix have been synthesized by Pulsed Laser Deposition (PLD) at room temperature. The structural and optical properties of the materials were tailored by varying deposition parameters; attention has been devoted to the nanoscale morphology of the Si layers which has been varied from compact to open-porous by changing background gas (Ar) pressure (1-100 Pa). An adopted simple-minded strategy of a compact Si layer deposited on top of nanostructured layers showed to reduce quite successfully ex-situ oxidation. Raman spectroscopy suggests that as deposited samples are mainly constituted by amorphous silicon with nanocrystals (NCs) inclusions. The results indicate that the average size of the Si NCs varies in the range 2-6 nm. Photoluminescence (PL) responses are found to be strictly dependent on morphology and strengthen up the idea of the quantum confinement effect in the obtained nanostructured material. The results are interpreted in terms of particle size distribution, crystallinity and partial surface oxidation of the silicon nanostructures.