Skip to main content Accessibility help

We use cookies to distinguish you from other users and to provide you with a better experience on our websites. Close this message to accept cookies or find out how to manage your cookie settings.

Close cookie message
×
  1. Home
  2. Search

Refine search

Refine search

Access:
Content type:
Publication date:
Apply   From and To filters
Subject: Show more
Journals Show more
Publishers: Show more
Societies Show more
Series: Show more
Collections: Show more

Actions for selected content:

Select all | Deselect all
  • View selected items
  • Export citations
  • Download PDF (zip)
  • Save to Kindle
  • Save to Dropbox
  • Save to Google Drive

Save Search

You can save your searches here and later view and run them again in "My saved searches".

Please provide a title, maximum of 40 characters.
Cancel
×

1 results

  • Laser solid forming assisted by friction stir processing for preparation of Ni–16Cr–8Fe alloys: Crack repairing and grain refinement

  • Pengda Niu, Ruidi Li, Tiechui Yuan, Minbo Wang, Siyao Xie, Hong Wu
  • Journal:
    Journal of Materials Research / Volume 33 / Issue 20 / 29 October 2018
    Published online by Cambridge University Press:
    27 June 2018, pp. 3521-3529
    Print publication:
    29 October 2018

  • Although laser solid forming (LSF) has a wide range of applications in material manufacturing, the technique has been severely limited due to the solidification cracks during rapid laser melting/solidification. In this paper, an LSF technology assisted by friction stir processing (FSP) is proposed to eliminate the LSF crack through the FSP thermomechanical coupling effect, with the Ni–16Cr–8Fe alloy as a representative material. By FSP-assisted LSF, the cracks at the top surface of the Ni–16Cr–8Fe alloy layer were eliminated. Meanwhile, the severe plastic deformation layers can be observed and gradient grains with tens of nanometers to tens of micrometers from the top surface to the inner. The LSF-printed dendrite microstructure was transformed into nanocrystals or nanotwins in the deformation zone with twining as the main deformation mechanism. The grain refinement results in the increase of hardness about 30%.