Skip to main content Accessibility help

We use cookies to distinguish you from other users and to provide you with a better experience on our websites. Close this message to accept cookies or find out how to manage your cookie settings.

Close cookie message
×
  1. Home
  2. Search

Refine search

Refine search

Access:
Content type:
Publication date:
Apply   From and To filters
Subject: Show more
Journals Show more
Publishers: Show more
Societies Show more
Series: Show more
Collections: Show more

Actions for selected content:

Select all | Deselect all
  • View selected items
  • Export citations
  • Download PDF (zip)
  • Save to Kindle
  • Save to Dropbox
  • Save to Google Drive

Save Search

You can save your searches here and later view and run them again in "My saved searches".

Please provide a title, maximum of 40 characters.
Cancel
×

1 results

  • Deposition Rate Effect on Critical Thickness of BaTiO3 Epitaxial Thin Film Grown on SrTiO3 (001)

  • Masanori Kawai, Daisuke Kan, Seiichi Isojima, Hiroki Kurata, Seiji Isoda, Shigeru Kimura, Osami Sakata, Yuichi Shimakawa
  • Journal:
    MRS Online Proceedings Library Archive / Volume 1034 / 2007
    Published online by Cambridge University Press:
    01 February 2011, 1034-K10-04
    Print publication:
    2007

  • BaTiO3/SrTiO3(001) epitaxial thin films were prepared at various growth rates by pulsed laser deposition, and their heterostructures were evaluated by synchrotron x-ray diffraction measurements and cross-sectional scanning transmission electron microscopy observations. In a film grown at a low deposition rate (0.01 nm/s), misfit dislocations are found near the interface and a fully relaxed BaTiO3 thin film grows epitaxially on the substrate. On the other hand, a film grown at a high deposition rate (0.04 nm/s) consists of strained and relaxed BaTiO3 lattices. Our results showed that the critical thickness of BaTiO3/SrTiO3(001) epitaxial thin films can be controlled by the deposition rate and that the critical thickness increases with increasing the deposition rate, and by adjusting the deposition rate we were able to prepare epitaxial thin films consisting of fully strained BaTiO3, partially strained BaTiO3 or fully relaxed BaTiO3. We have also achieved the growth controlling of BaTiO3 thin films on SrTiO3(001) substrates with SrRuO3 bottom electrode layer.