The electrode materials for VRFB should possess higher electric conductivity, corrosion resistance and hydrophilic properties in sulfuric acid. The characteristics of the electrode materials affect the stability and the energy efficiency of VRFB. Carbon materials are the best suited for VRFB applications. In this study, the calcined treatment, acid treatment and ozone treatment were used to modify the surface of carbon papers. The redox reaction of [VO]2+/[VO2]+ on the modified carbon papers was evaluated by cyclic voltammetry (CV). The surface compositions of carbon materials were analyzed by X-ray photoelectron spectrometry (XPS). The experimental results reveal that three oxidative methods enhance the redox reaction of [VO]2+/[VO2]+. The calcined treatments and acid treatments also enhanced hydrolysis reaction. The mole ratio of O/C apparently increased, but the binding energy of C1s and O1s were not chemically shifted in the acid treatment. The intensity of binding energy of O1s, between 532 eV and 534 eV, apparently increased in the ozone and calcined treatments. The Ox treated samples were more hydrophilic than the Oz treated samples. In the Ox treated samples, the decrease of Rct value indicates that was contributed from the redox reaction of [VO]2+/[VO2]+ and hydrolysis reaction. It does not completely benefit the energy efficiency of VRFB. The 5 x 5 cm2 modified carbon papers were used as electrode materials in the VRFB. The voltage efficiency, coulomb efficiency and energy efficiency reached 93 %, 90 % and 83 %, respectively, at a current density of 12 mA．cm-2 at 0.8-1.8 V.