Skip to main content Accessibility help

We use cookies to distinguish you from other users and to provide you with a better experience on our websites. Close this message to accept cookies or find out how to manage your cookie settings.

Close cookie message
×
  1. Home
  2. Search

Refine search

Refine search

Access:
Content type:
Publication date:
Apply   From and To filters
Subject: Show more
Journals Show more
Publishers: Show more
Societies Show more
Series: Show more
Collections: Show more

Actions for selected content:

Select all | Deselect all
  • View selected items
  • Export citations
  • Download PDF (zip)
  • Save to Kindle
  • Save to Dropbox
  • Save to Google Drive

Save Search

You can save your searches here and later view and run them again in "My saved searches".

Please provide a title, maximum of 40 characters.
Cancel
×

1 results

  • CVD Growth of Graphene on Three Types of Epitaxial Metal Films on Sapphire Substrate

  • Katsuya Nozawa, Nozomu Matsukawa, Kenji Toyoda, Shigeo Yoshii
  • Journal:
    MRS Online Proceedings Library Archive / Volume 1284 / 2011
    Published online by Cambridge University Press:
    23 March 2011, mrsf10-1284-c01-11
    Print publication:
    2011

  • Graphene growth by chemical vapor deposition (CVD) was studied on three types of epitaxial metal films with different crystal structures on sapphire. Nickel (face-centered-cubic: fcc), Ru (hexagonal-closed-pack: hcp), and Co (fcc at temperature for graphene growth and hcp at R.T.) were deposited on c-face sapphire substrates and annealed in a furnace for solid phase epitaxial growth. Graphene layers were grown by CVD with methane gas on the epitaxial metal film. The graphene layer uniformity was consistent with the structural simplicity of the metal film. The Ru sample had a single domain in the metal film and the highest graphene uniformity. The Co sample had a very complex crystal structure in the metal film and the poorest uniformity in graphene. The Ni sample had two types of stacking domains in the metal film and the graphene layer was uniform on each domain, but inhomogeneity was observed at domain boundaries.