Native tungsten (IMA2011-004), W, is officially described as a new mineral from gold placers in the Bol'shaya Pol'ya river valley, Prepolar Urals, Russia, associated with yttriaite-(Y) and from quartz veins in the Mt Neroyka rock-crystal field, Ust–Puiva, Tyumenskaya Oblast', Russia. Tungsten forms polycrystalline grains and masses, and rarely cubo-octahedra. It is silver white to steel grey in colour, with metallic lustre and grey streak. The calculated density is 19.226 g/cm3. The Vickers hardness (VHN25) is 571.45 kg/mm2. In plane polarised light, tungsten is white with a pale-yellow tint and optically isotropic. Electron microprobe analyses of Bol'shaya Pol'ya river valley material provided W 99.27, Mo 0.06, Mn 0.04, Fe 0.01, total 99.38 wt.%. The five strongest powder X-ray diffraction lines are [dobs Å(I)(hkl)]: 2.2422(100)(110), 1.5835(25)(200), 1.2929(48)(211), 1.0010(23)(310) and 0.8457(24)(321). Tungsten is cubic, Im$\bar{3}$m, a = 3.1648(4) Å, V = 31.69(4) Å3 and Z = 2. Some additional occurrences of native tungsten and technogenic tungsten found in Nature are also described.

Hagstromite, Pb8Cu2+(Te6+O6)2(CO3)Cl4, (IMA2019-093) is a new tellurate mineral from Otto Mountain near Baker, California, USA. It occurs on quartz in association with cerussite, fuettererite and thorneite. It is a secondary oxidation zone mineral and is presumed to have formed by oxidation of earlier formed tellurides, chalcopyrite and galena. Hagstromite occurs as light yellow–green blades, up to ~100 μm long. Crystals are transparent with adamantine to silky lustre. The mineral is brittle with two cleavages providing splintery fracture; the Mohs hardness is probably between 2 and 3. The calculated density is 7.062 g cm–3. Hagstromite is optically biaxial (+), with calculated indices of refraction for α = 2.045, β = 2.066 and γ = 2.102; 2Vmeas = 76(1)°; and optical orientation X = b, Y = a and Z = c. The Raman spectrum of hagstromite exhibits similarities with those of agaite and thorneite and confirms the presence of CO32–. The electron microprobe analyses provided the empirical formula Pb8.07Cu2+0.98Te6+1.96C1.17Cl3.83O15.34. Hagstromite is orthorhombic, space group Ibam, with a = 23.688(17), b = 9.026(8), c = 10.461(8) Å, V = 2237(3) Å3 and Z = 4. The crystal structure of hagstromite (R1 = 0.0659 for 284 I > 2σI reflections) contains a novel Cu2+Te6+2O12 chain assembled of corner-sharing Cu2+O4 squares and Te6+O6 octahedra. The O atoms in the chains form bonds with Pb2+ cations, which in turn bond to Cl– and CO32– anions, thereby creating a framework structure.

Davidbrownite-(NH4), (NH4,K)5(V4+O)2(C2O4)[PO2.75(OH)1.25]4·3H2O, is a new mineral species from the Rowley mine, Maricopa County, Arizona, USA. It occurs in an unusual bat-guano-related, post-mining assemblage of phases that include a variety of vanadates, phosphates, oxalates and chlorides, some containing NH4+. Other secondary minerals found in association with davidbrownite-(NH4) are antipinite, fluorite, mimetite, mottramite, quartz, rowleyite, salammoniac, struvite, vanadinite, willemite and wulfenite. Crystals of davidbrownite-(NH4) are light green–blue needles or narrow blades up to ~0.2 mm long. The streak is white, the lustre is vitreous, Mohs hardness is ca. 2, tenacity is brittle and fracture is splintery. There are two good cleavages in the [010] zone, probably {100} and {001}. The measured density is 2.12(2) g cm–3. Davidbrownite-(NH4) is optically biaxial (+) with α = 1.540(2), β = 1.550(5) and γ = 1.582(2) (white light); 2V = 58.5(5)°; moderate r > v dispersion; and orientation Z = b and Y ≈ a. Pleochroism: X = pale blue, Y = nearly colourless, Z = light blue; and Y < X < Z. Electron microprobe analysis gave the empirical formula [(NH4)3.11K1.73Na0.09]Σ4.93[(V4+1.92Mg0.01Al0.02)Σ1.95O2](C2O4) [(P3.94As0.12)Σ4.06O10.94(OH)5.06]·3H2O, with the C and H content provided by the crystal structure. Raman and infrared spectroscopy confirmed the presence of NH4 and C2O4. Davidbrownite-(NH4) is monoclinic, P21/c, with a = 10.356(6), b = 8.923(5), c = 13.486(7) Å, β = 92.618(9)°, V = 1244.9(12) Å3 and Z = 2. The crystal structure of davidbrownite-(NH4) (R1 = 0.0524 for 2062 Io > 2σI reflections) consists of a chain structural unit with the formula {(V4+O)2(C2O4)[PO2.75(OH)1.25]4}5–, and a disordered interstitial complex containing five large monovalent cations (NH4+ and K+) and three H2O groups pfu. Strong hydrogen bonds form links within and between the chains.

A crystal of painite discovered in 1979 in a parcel of rough gem spinel from Burma represents the third known crystal of the species. This crystal is similar to the type crystal in most respects. Chemical analyses of both the new crystal and the type crystal confirmed the essential constituents reported by Moore and Araki (1976) and showed in addition the presence of trace amounts of Fe, Cr, V, Ti, Na, and Hf. Optical absorption spectra suggest that the red colour of painite is caused principally by Cr3+ and V3+.

Żabińskiite, ideally Ca(Al0.5Ta0.5)(SiO4)O, was found in a Variscan granitic pegmatite at Piława Górna, Lower Silesia, SW Poland. The mineral occurs along with (Al,Ta,Nb)- and (Al,F)-bearing titanites, a pyrochlore-supergroupmineral and a K-mica in compositionally inhomogeneous aggregates, ∼120 μm × 70 μm in size, in a fractured crystal of zircon intergrown with polycrase-(Y) and euxenite-(Y). Żabińskiite is transparent, brittle, brownish, with a white streak, vitreous lustre and a Mohs hardness of ∼5. The calculated density for the refined crystal is equal to 3.897 g cm–3, but depends strongly on composition. The mineral is non-pleochroic, biaxial (–), with mean refractive indices ≥1.89. The (Al,Ta,Nb)-richest żabińskiite crystal,(Ca0.980Na0.015)∑=0.995(Al0.340Fe3+0.029Ti0.298V0.001Zr0.001Sn0.005Ta0.251Nb0.081)∑=1.005[(Si0.988Al0.012)O4.946F0.047(OH)0.007)∑=5.000];60.7 mol.% Ca[Al0.5(Ta,Nb)0.5](SiO4)O; is close in composition to previously described synthetic material. Żabińskiite is triclinic (space group symmetry A1) and has unit-cell parameters a = 7.031(2) Å, b = 8.692(2) Å,c = 6.561(2) Å, α = 89.712(11)°, β = 113.830(13)°, γ = 90.352(12)° and V = 366.77 (11) Å3. It is isostructural with triclinic titanite and bond-topologically identical with titanite and other minerals of the titanite group.Żabińskiite crystallized along with (Al,Ta,Nb)-bearing titanites at increasing Ti and Nb, and decreasing Ta activities, almost coevally with polycrase-(Y) and euxenite-(Y) from Ca-contaminated fluxed melts or early hydrothermal fluids.

Kyawthuite, Bi3+Sb5+O4, is a new gem mineral found as a waterworn crystal in alluvium at Chaung-gyi-ah-le-ywa in the Chaung-gyi valley, near Mogok, Burma (Myanmar). Its description is based upon a single sample, which was faceted into a 1.61-carat gem.The composition suggests that the mineral formed in a pegmatite. Kyawthuite is monoclinic, space group I2/c, with unit cell dimensions a = 5.4624(4), b = 4.88519(17), c = 11.8520(8) Å, β = 101.195(7)°, V = 310.25(3) Å3and Z = 4. The colour is reddish orange and the streak is white. It is transparent with adamantine lustre. The Mohs hardness is 5½. Kyawthuite is brittle with a conchoidal fracture and three cleavages: {001} perfect, {110} and {110} good. The measured density is 8.256(5) g cm–3and the calculated density is 8.127 g cm–3. The mineral is optically biaxial with 2V = 90(2)°. The predicted indices of refraction are α = 2.194, β = 2.268, γ = 2.350. Pleochroism is imperceptible and the optical orientation is X = b; Y≈ c; Z ≈ a. Electron microprobe analyses, provided the empirical formula (Bi0.823+Sb0.183+)∑1.00(Sb0.995+Ta0.015+)∑1.00O4. The Raman spectrumis similar to that of synthetic Bi3+Sb5+O4. The infrared spectrum shows a trace amount of OH/H2O. The eight strongest powder X-ray diffraction lines are [dobs in Å(I)(hkl)]: 3.266(100)(112), 2.900(66)(112), 2.678(24)(200), 2.437(22)(020,114), 1.8663(21)(024), 1.8026(43)(116,220,204), 1.6264(23)(224,116) and 1.5288(28)(312,132). In the crystal structure of kyawthuite (R1 = 0.0269 for 593 reflections with Fo > 4σF), Sb5+O6 octahedrashare corners to form chequerboard-like sheets parallel to {001}. Atoms of Bi3+, located above and below the open squares in the sheets, form bonds to the O atoms in the sheets, thereby linking adjacent sheets into a framework. The Bi3+ atom is in lopsided 8 coordination,typical of a cation with stereoactive lone electron pairs. Kyawthuite is isostructural with synthetic β-Sb2O4 and clinocervantite (natural β-Sb2O4).

Andychristyite, PbCu2+Te6+O5(H2O), is a new tellurate mineral from Otto Mountain near Baker, California, USA. It occurs in vugs in quartz in association with timroseite. It is interpreted as having formed from the partial oxidation of primary sulfides and tellurides during or following brecciation of quartz veins. Andychristyite is triclinic, space group P1̄, with unit-cell dimensions a = 5.322(3), b= 7.098(4), c = 7.511 (4) Å, α = 83.486(7), β = 76.279(5), γ = 70.742(5)°, V = 260.0(2) Å3 and Z = 2. It forms as small tabular crystals up to ∼50 μm across, in sub-parallel aggregates. The colour is bluish green and the streak is very pale bluish green. Crystals are transparent with adamantine lustre. The Mohs hardness is estimated at between 2 and 3. Andychristyite is brittle with an irregular fracture and one perfect cleavage on {001}. The calculated density based on the empirical formula is 6.304 g/cm3. The mineral is optically biaxial, with large 2V, strong dispersion, and moderate very pale blue-green to medium blue-green pleochroism. The electron microprobe analyses (average of five) provided: PbO 43.21, CuO 15.38, TeO3 35.29, H2O 3.49 (structure), total 97.37 wt.%. The empirical formula (based on 6 O apfu) is: Pb0.98Cu2+0.98Te6+1.02O6H 1.96. The Raman spectrum exhibits prominent features consistent with the mineral being a tellurate, as well as an OH stretching feature confirming a hydrous component. The eight strongest powder X-ray diffraction lines are [dobs in Å(I)(hkl)]: 6.71(16)(010), 4.76(17)(110), 3.274(100)(120,102,012), 2.641(27)(102, 211, 112), 2.434(23)(multiple), 1.6736(17)(multiple), 1.5882(21)(multiple) and 1.5133(15)(multiple). The crystal structure of andychristyite (R1 = 0.0165 for 1511 reflections with Fo > 4σF) consists of stair-step-like hcp polyhedral layers of Te6+O6 and Cu2+O6 octahedra parallel to {001}, which are linked in the [001] direction by bonds to interlayer Pb atoms. The structures of eckhardite, bairdite, timroseite and paratimroseite also contain stair-step-like hcp polyhedral layers.

Low voltage field emission SEM (i.e., operated at several hundred volts to 5 kV), offering advantages in surface imaging due to reduced beam penetration,1 was found to be particularly useful in the investigation of uncoated, fine, geological materials down to the nano-scale. Here are four examples to highlight projects being conducted in our FESEM facility.

Kaolinite is one of the most important industrial minerals. Information about its surface properties and cation exchange capacity are important in both ore processing and applications of the clay mineral.2 Low voltage (LV) secondary electron (SE) imaging (Fig. la) reveals detailed (001) surface features of kaolinite, which are not obtainable with high voltage SEM (Fig. lb) and TEM. Kaolinite is highly sensitive to beam damage and can show obvious degradation after just a few seconds under the TEM beam. However, microtomed TEM samples maybe easily examined under LV SEM to show their thickness perpendicular to (001) and cross section features. Such information allows easy access to direct surface area determination of clay minerals.

Green glauconite-like minerals from Weipa, Australia, which were previously known as glauconite, were determined to be unusual Fe-rich vermicuhte and Fe-rich smectite. This study revealed the structural and chemical nature of these unique phyllosilicates with HRTEM, AEM, SEM and XRD analysis.

The Fe-rich phyllosilicates comprising up to about 15 wt% of the rock occur with various amounts of quartz, mica, feldspar, low-Fe smectite, kaolinite, pyrite and siderite at about 30 meters depth in unweathered marine sediments of the Rolling Downs Formation at Weipa. The proportions of Fe-rich vermiculite and smectite decrease upward and become undetectable in the upper saprolite zone at about 23 m depth.

Two major morphologies of the Fe-rich phyllosilicates were observed. One is of tabular or granular detrital-shaped form (Fig.la); the other is platy or film-like, coating grains and occurring in matrix and fissures (Fig.lb).

One-, two- and three-layer polytypes are common in muscovite (sheet silicate). Based on high-resolution transmission electron microscopy (HRTEM) and analytical electron microscopy (AEM) examinations, we report in the discovery of complex 5-layer and 7- layer polytypes in natural muscovite for the first time (Fig. 1) and the implications of polytype transitions.

Three main structures are found in muscovite crystals in a sample from Oreana, Nevada, which are 1M, 2M1, and a disordered structure often containing short-range ordered stacking sequences. On the scale of a few micrometers, muscovite occurs as ordered crystals, disordered crystals, and crystals with regions of ordered and disordered layer stacking.

Short-range ordered 5- or 7-layer repeats are found in some disordered structures where single 4-, 6-, 9- or 10-layer intergrowths occur occasionally with 2- and 3-layer repeats. Such complex polytypes have not been observed before in either natural or synthetic muscovite, although 5- and 7-layer structures are commonly present in trioctahedral micas (i.e., biotite) (Baronnet, 1992).