Crystalline particles and grains embedded in Cu35Ti65 glass ribbons have been amorphized by isothermal cold rolling. The structural evolution has been studied by X-ray diffraction and TEM techniques. Initial particle morphologies are spherulitic and spherical, the latter with sizes ranging between 10 and 100 nm. The new amorphous phase seems to nucleate at crystalline-amorphous matrix interfaces. Initially there is a well defined interface between the new and the existing amorphous phases but it disappears as rolling progresses. Crystallites on a nanoscale still present in the final stages of particle amorphization have been observed by convergent beam electron diffraction. After sufficient deformation the consolidated ribbon becomes completely glassy. A morphological description of the transformation process in terms of crystal destabilization and solid-state particle melting is presented.