Study of CoxPt1−x nanoalloy formation mechanism via single-source precursors

  • E. Yu. Filatov (a1) (a2), A. V. Zadesenets (a1) (a2), S. V. Komogortsev (a3), P. E. Plyusnin (a1) (a2), A. A. Chepurov (a4) and S. V. Korenev (a1) (a2)...

Abstract

This paper is devoted to the study of formation mechanism of metal solid solutions during the thermolysis of single-source precursors in Co–Pt systems with a wide range of superstructural ordering. It is shown that the thermal decomposition of [Pt(NH3)4][Co(C2O4)2(H2O)2]·2H2O salt in helium is critically different from that under hydrogen atmospheres. Thermal degradation under the helium atmosphere is followed by a gradual reduction of platinum and cobalt, and at each thermolysis temperature only one phase is present. At 380 °C an equiatomic Co0.50Pt0.50 solid solution is formed (a = 3.749 (4) Å, Fm−3m space group, V/Z = 13.17 Å3, crystallite size: 5–7 nm). When the precursor is decomposed under a hydrogen atmosphere, the process proceeds mainly through the simultaneous reduction of the platinum and cobalt atoms, and at each temperature section two metal phases are present. The formation of the close to equiatomic Co0.50Pt0.50 solid solution (a = 3.782 (4) Å, Fm−3m space group, V/Z = 13.52 Å3, crystallite size: 7–9 nm) occurs at 450 °C. The calculations of crystallite sizes are confirmed by transmission electron microscopy data.

Copyright

Corresponding author

a)Author to whom correspondence should be addressed. E-mail: decan@niic.nsc.ru

References

Hide All
Asanova, T., Asanov, I., Zadesenets, A., Filatov, E., Plyusnin, P., Gerasimov, E., and Korenev, S. (2016). “Study on thermal decomposition of double complex salt [Pd(NH3)4][PtCl6],” J. Therm. Anal. Calorim. 123(2), 11831195.
Aulchenko, V. M., Evdokov, O. V., Kutovenko, V. D., Pirogov, B. Ya., Sharafutdinov, M. R., Titov, V. M., Tolochko, B. P., Vasiljev, A. V., Zhogin, I. L., and Zhulanov, V. V. (2009). “One-coordinate X-ray detector OD–3M,” Nucl. Instrum. Methods Phys. Res., Sect. A. 603, 7679.
Barry, M. C., Wei, Z., He, T., Filatov, A. S., and Dikarev, E. V. (2016). “Volatile single-source precursors for the low-temperature preparation of sodium-rare earth metal fluorides,” J. Am. Chem. Soc. 138(28), 88838887.
Chepurov, A. I., Sonin, V. M., Chepurov, A. A., Zhimulev, E. I., Tolochko, B. P., and Eliseev, V. S. (2011). “Interaction of diamond with ultrafine Fe powders prepared by different procedures,” Inorg. Mater. 47, 864868.
Furukawa, S., Ehara, K., and Komatsu, T. (2016). “Unique reaction mechanism of preferential oxidation of CO over intermetallic Pt3Co catalysts: surface-OH-mediated formation of a bicarbonate intermediate,” Catal. Sci. Technol. 6, 16421650.
Komogortsev, S. V., Chizhik, N. A., Filatov, E.Yu., Korenev, S. V., Shubin, Yu.V., Velikanov, D. A., Iskhakov, R. S., and Yurkin, G.Yu. (2012). “Magnetic properties and L10 phase formation in CoPt nanoparticles,” Solid State Phenom. 190, 159162.
Komogortsev, S. V., Iskhakov, R. S., Zimin, A. A., Filatov, E.Yu., Korenev, S. V., Shubin, Yu.V., Chizhik, N. A., Yurkin, G.Yu., and Eremin, E. V. (2016). “The exchange interaction effects on magnetic properties of the nanostructured CoPt particles,” J. Magn. Magn. Mater. 401, 236241.
Kraus, W., and Nolze, G. (2000). PowderCell 2.4, Program for the Representation and Manipulation of Crystal Structures and Calculation of the Resulting X-ray Powder Patterns (Federal Institute for Materials Research and Testing, Berlin).
Krumm, S. (1995). “An interactive windows program for profile fitting and size/strain analysis,” Mater. Sci. Forum 228–231, 183188.
Plyusnin, P. E., Makotchenko, E. V., Shubin, Y. V., Baidina, I. A., Korolkov, I. V., Sheludyakova, L. A., and Korenev, S. V. (2015). “Synthesis, crystal structures, and characterization of double complex salts [Au(en)2][Rh(NO2)6]·2H2O and [Au(en)2][Rh(NO2)6],” J. Mol. Struct. 1100, 174179.
Potemkin, D. I., Filatov, E. Yu., Zadesenets, A. V., Snytnikov, P. V., Shubin, Yu.V., and Sobyanin, V. A. (2012). “Preferential CO oxidation over bimetallic Pt–Co catalysts prepared via double complex salt decomposition,” Chem. Eng. J. 207–208, 683689.
Potemkin, D. I., Filatov, E. Yu., Zadesenets, A. V., and Sobyanin, V. A. (2017). “CO preferential oxidation on Pt0.5Co0.5 and Pt-CoOx model catalysts: catalytic performance and operando XRD studies,” Catal. Commun. 100, 232236.
Zadesenets, A., Filatov, E., Plyusnin, P., Baidina, I., Dalezky, V., Shubin, Yu., Korenev, S., and Bogomyakov, A. (2011). “Bimetallic single-source precursors [M(NH3)4][Co(C2O4)2(H2O)2]·2H2O (M = Pd, Pt) for the one run synthesis of CoPd and CoPt magnetic nanoalloys,” Polyhedron 30, 13051312.

Keywords

Study of CoxPt1−x nanoalloy formation mechanism via single-source precursors

  • E. Yu. Filatov (a1) (a2), A. V. Zadesenets (a1) (a2), S. V. Komogortsev (a3), P. E. Plyusnin (a1) (a2), A. A. Chepurov (a4) and S. V. Korenev (a1) (a2)...

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed