Vitrification of High-Level Waste at the Savannah River Site

Published online by Cambridge University Press:  15 February 2011

Kevin M. Fox
Affiliation:
Environmental & Chemical Process Technology, Savannah River National Laboratory Aiken, SC 29808U.S.A.
David K. Peeler
Affiliation:
Environmental & Chemical Process Technology, Savannah River National Laboratory Aiken, SC 29808U.S.A.
Get access

Abstract

The objective of this study was to experimentally measure the properties and performance of a series of glasses with compositions that could represent high level waste Sludge Batch 5 (SB5) as vitrified at the Savannah River Site Defense Waste Processing Facility. These data were used to guide frit optimization efforts as the SB5 composition was finalized. Glass compositions for this study were developed by combining a series of SB5 composition projections with a group of candidate frits. The study glasses were fabricated using depleted uranium and their chemical compositions, crystalline contents and chemical durabilities were characterized. Trevorite was the only crystalline phase that was identified in a few of the study glasses after slow cooling, and is not of concern as spinels have been shown to have little impact on the durability of high level waste glasses. Chemical durability was quantified using the Product Consistency Test (PCT). All of the glasses had very acceptable durability performance. The results of this study indicate that a frit composition can be identified that will provide a processable and durable glass when combined with SB5.

Type
Research Article
Copyright
Copyright © Materials Research Society 2009

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Hay, M. S., Pareizs, J. M., Bannochie, C. J., Stone, M. E., Click, D. R. and McCabe, D. J., “Characterization and Aluminum Dissolution Demonstration with a 3 Liter Tank 51H Sample,” U.S. Department of Energy Report WSRC-STI-2007-00697, Revision 0, Washington Savannah River Company, Aiken, SC (2008).Google Scholar
2 Fox, K. M. and Edwards, T. B., “SB5 with the Estimated Impact of Low-Temperature Aluminum Dissolution: Preliminary Frits for Melt Rate Testing,” U.S. Department of Energy Report WSRC-STI-2008-00006, Revision 0, Washington Savannah River Company, Aiken, SC (2008).Google Scholar
3 Edwards, T. B., Brown, K. G. and Postles, R. L., “SME Acceptability Determination for DWPF Process Control,” U.S. Department of Energy Report WSRC-TR-95-00364, Revision 5, Washington Savannah River Company, Aiken, SC (2006).Google Scholar
4 Marra, S. L. and Jantzen, C. M., “Characterization of Projected DWPF Glass Heat Treated to Simulate Canister Centerline Cooling,” U.S. Department of Energy Report WSRC-TR-92-142, Revision 1, Westinghouse Savannah River Company, Aiken, SC (1993).Google Scholar
5 ASTM, “Standard Test Methods for Determining Chemical Durability of Nuclear Waste Glasses: The Product Consistency Test (PCT),” ASTM C-1285, (2002).Google Scholar
6 Jantzen, C. M., Bibler, N. E., Beam, D. C., Crawford, C. L. and Pickett, M. A., “Characterization of the Defense Waste Processing Facility (DWPF) Environmental Assessment (EA) Glass Standard Reference Material,” U.S. Department of Energy Report WSRC-TR-92-346, Revision 1, Westinghouse Savannah River Company, Aiken, SC (1993).Google Scholar
7 Bickford, D. F. and Jantzen, C. M., “Devitrification of Defense Nuclear Waste Glasses: Role of Melt Insolubles,” J. Non-Crystalline Solids, 84 [1-3] 299307 (1986).Google Scholar
8 Fox, K. M., Edwards, T. B., Best, D. R., Reamer, I. A. and Workman, R. J., “Frit Development for High Level Waste Sludge Batch 5: Compsitional Trends for Varying Aluminum Concentrations,” U.S. Department of Energy Report SRNS-STI-2008-00060, Revision 0, Savannah River Nuclear Solutions, Aiken, SC (2008).Google Scholar
9 Jantzen, C. M., Picket, J. B., Brown, K. G., Edwards, T. B. and Beam, D. C., “Process/Product Models for the Defense Waste Processing Facility (DWPF): Part I. Predicting Glass Durability from Composition Using a Thermodynamic Hydration Energy Reaction Model (THERMO),” U.S. Department of Energy Report WSRC-TR-93-672, Revision 1, Westinghouse Savannah River Company, Aiken, SC (1995).Google Scholar