Thermal Stability Of Electrodeposited Nanocrystalline Ni-45%Fe Alloys

Published online by Cambridge University Press:  10 February 2011

F. Czerwinski
Affiliation:
Department of Metallurgical Engineering, McGill University, Montreal, PQ H3A 2A7, Canada
H. Li
Affiliation:
Department of Metallurgical Engineering, McGill University, Montreal, PQ H3A 2A7, Canada
F. Megret
Affiliation:
Department of Metallurgical Engineering, McGill University, Montreal, PQ H3A 2A7, Canada
J. A. Szpunar
Affiliation:
Department of Metallurgical Engineering, McGill University, Montreal, PQ H3A 2A7, Canada
D. G. Clark
Affiliation:
Department of Materials and Metallurgical Engineering, Queen's University, Kingston, Ont., K7L 3N6, Canada
U. Erb
Affiliation:
Department of Materials and Metallurgical Engineering, Queen's University, Kingston, Ont., K7L 3N6, Canada
Get access

Abstract

Electrolytically deposited nanocrystalline Ni-45%Fe alloys, composed of γ (f.c.c.) phase, were annealed at 573 and 673 K for time periods up to 20 h in an inert atmosphere of argon. The evolutions of crystallographic texture, grain size, and microhardness were analyzed as a function of annealing parameters. The initial grains, approximately 5 nm in size increased after annealing up to 10–20 nm, however, the growth kinetics and the final grain size depended on the temperature. A correlation was found between the grain size and alloy microhardness. The phase composition was unstable and during annealing the α(b.c.c) phase was detected to precipitate from the γ matrix. The texture of γ phase, consisted of two fibre components of <111> and <200>, and evolved at high temperatures. Although the detailed changes depended on the annealing temperature, in general, the <111> component became stronger at the expense of the <200> component.

Type
Research Article
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Gleiter, H., Progr. Mater. Sci., 33, 223 (1989).Google Scholar
2. El-Sherik, A.M. and Erb, U.., J. Mater. Sci., 30, 5743 (1995).Google Scholar
3. Cheung, C., Djuanda, F., Erb, U., and Palumbo, G., to be published.Google Scholar
4. Brenner, A., Electrodeposition of Alloys, Academic Press, New York (1963).Google Scholar
5. Cullity, B.D., Elements of X-ray Diffraction, Addison-Wesley, Reading (1978).Google Scholar
6. Schurman, E. and Brauckmann, J., Arch. Eisenhüttenwes., 48, 3 (1977).Google Scholar
7. Iwase, K. and Nasu, N., Bull. Chem. Soc. Japan, 7, 305 (1932).Google Scholar
8. Marshak, F. and Stepanow, D., Z. Elektroch., 41, 599 (1935).Google Scholar
9. Aotani, K., J. Japan Inst. Met., B14, 55 (1950).Google Scholar