Temperature Dependence of Residual Stresses and Stress Relaxation in Blanket Films of Various Thicknesses

Published online by Cambridge University Press:  21 February 2011

A. P. Clarke ,
G. Langelaan  and
S. Saimoto
A. P. Clarke
Affiliation:
Now at Chalk River Laboratories, AECL Research, Chalk River Ontario, KOJ 1J0
G. Langelaan
Affiliation:
Department of Materials and Metall. Eng., Queen’s University, Kingston, Ontario, K7L 3N6
S. Saimoto
Affiliation:
Department of Materials and Metall. Eng., Queen’s University, Kingston, Ontario, K7L 3N6
Get access

Abstract

A rapid method to measure residual strains using x-rays during continuous temperature ramping has been developed whereby resolution of ±5xl0-5 can be attained with 2θ scans of about one minute using low index reflections. The method was used to make residual stress measurements during temperature cycling at heating rates of 2 to 15°C/min with interrupted stress relaxations at 235°C and 130°C on pure Al blanket films of 0.24μm, 0.58μm and 1.01 μm thicknesses. The results are consistent with the notion that surface sources are activated by the back stress of misfit dislocations.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 356: Symposium B2 – Thin Films: Stresses and Mechanical Properties V , 1994 , 609
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Clarke, A.P., Saimoto, S., & Ho, P., Stress Induced Phenomena in Metallization ed. by Ho, P.S., Li, C-Y, Totta, P., AIP Press, New York (1994) 125–136.Google Scholar
2. Clarke, A.P. Ph.D. Thesis, Queen’s University, 1993.Google Scholar
3. Nix, W.P., Met Trans. (1989) 20A, 2217–2245.Google Scholar
4. Freund, L.B, MRS Bulletin, July 1992, 52–60.Google Scholar
5. Freund, L.B., Scripta Metall et Mater, (1992) 27, 669–674.Google Scholar
6. Noyan, I.C. & Cohen, J.B., Residual Stress Measurements by Diffraction and Interpretation, (Springer-Verlag, New York, 1987).Google Scholar
7. Jones, R.E. & Basehore, M.L., Applied Physics letters, 50 (1987) 725.Google Scholar
8. Hellwege, K.H., editor, Landolt Bornstein Vol HI. (Springer-Verlag, New York, 1987).Google Scholar
9. Mondolfo, L.F.. Aluminum Alloys: Structure and Properties. (Butterworth Co., Toronto, 1976).Google Scholar
10. Paszkiet, C.A., Ph.D. Thesis, Cornell University, 1992.Google Scholar
11. Doerner, M.F., Gardner, D.S. & Nix, W.D., J. Mater. Res. 1 (1986) 845–851.Google Scholar
12. Korhonen, M.A., Paszkiet, C.A., R.D. Black & C-Y Li Scripta Metall et Mater., 24 (1997) 2297–2302.Google Scholar
13. Ho, P.S., Yeo, I-S, Anderson, S.G.H. & Hu, C.K.,, Stress Induced Phenomena in Metallization, ed. by Ho, P.S., Li, C-Y, Totta, P., AIP Press New York (1994) 62–69.Google Scholar
14. Romanov, A.E. & Aifantis, E.C., Scripta Metall et Mater. 30 (1994) 1581–1586.Google Scholar