Stress Corrosion Cracking of Magnesium Die Casting Alloys

Published online by Cambridge University Press:  21 February 2011

William K. Miller
William K. Miller*
Affiliation:
General Motors Research Laboratories, Metallurgy Department, Tech Center, Warren, MI 48090–9055
Get access

Abstract

Contrary to limited published information on the subject, magnesium die casting alloys are shown to be susceptible to stress corrosion cracking (SCC), requiring only partial immersion in distilled water. Also described is evidence that this SCC results from a cathodic process, with perhaps hydrogen-assisted cracking and film rupture both playing roles.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 125: Symposium N – Materials Stability and Environmental Degradation , 1988 , 253
Copyright
Copyright © Materials Research Society 1988

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Miller, W.K. and Ryntz, E.F., SAE Trans. 92, 2.524–2.552 (1983).Google Scholar
2. Siebel, G., Jahrbuch 1937 der deutschen Luftfahrforschung, part I, 528–531 (1937).Google Scholar
3. Beck, A., The Technology of Magnesium and Its Alloys, (F.A. Hughes & Co. Ltd, London, 1940), pp. 294–297.Google Scholar
4. Sager, G.F., Brown, R.H. and Mears, R.B., Symposium on Stress Corrosion Cracking of Metals, (ASTM, Philadelphia, 1945), pp. 255–272.CrossRefGoogle Scholar
5. Loose, W.S., in The Corrosion Handbook, edited by Uhlig, H.H. (John Wiley & Sons, New York, 1948), p. 233.Google Scholar
6. Belyakov, V.D. and Ramanov, V.V., Sov. Mater. Sci. 7 (4), 400–402 (1971).CrossRefGoogle Scholar
7. Miller, W.K., presented at the 1988 TMS Annual Meeting, Phoenix, AZ, 1988 (to be published in proceedings of Advances in Magnesium Alloys and Composites Symposium).Google Scholar
8. Hollrigi-Rosta, F., Just, E., Kohler, J. and Melzer, H.J., Proceedings 37th Annual World Conference on Magnesium (International Magnesium Association, McLean, VA, 1980), pp.38–45.Google Scholar
9. Reichek, K.N., Clark, K.J. and Hillis, J.E., SAE Trans. 94, 3.318–3.329 (1985).Google Scholar
10. Hillis, J.E. and Reichek, K.N., SAE Trans. 96, 2.227–2.234 (1986).Google Scholar
11. LaQue, F.L., May, T.P. and Uhlig, H.H., Corrosion in Action (The International Nickel Company, Inc., 1955), pp 19–23.Google Scholar
12. Perryman, E.C.W., J. Inst. Met. 78, 621–642 (1951).Google Scholar
13. Chakrapani, D.G. and Pugh, E.N., Met. Trans. 7A, 173–178 (1976).CrossRefGoogle Scholar
14. Bursle, A.J. and Pugh, E.N., in Mechanisms of Environment Sensitive Cracking of Materials, edited by Swann, , Ford, and Westwood, (The Metals Society, London, 1977), pp. 471–481.Google Scholar
15. Viswanadham, R.K., Sun, T.S. and Green, J.A.S., Met. Trans. 11A, 85–89 (1980).CrossRefGoogle Scholar
16. Scamans, G.M., Alani, R. and Swann, P.R., Corros. Sci. 16, 443–460 (1976).CrossRefGoogle Scholar
17. Pugh, E.N., Green, J.A.S. and Slattery, P. W., in Proceedings of the Second International Conference on Fracture (Chapman and Hall, London, 1969), pp. 387–395.Google Scholar
18. Uhlig, H.H., in Stress Corrosion Cracking and Hydrogen Embrittlement of Iron Base Alloys, edited by Staehle, R.W. (NACE, Houston, 1977), pp. 174–177.Google Scholar
19. Pourbaix, M., in The Theory of Stress Corrosion Cracking in Alloys, edited by Scully, J.C. (NATO, Brussels, 1971), pp 442–448.Google Scholar
20. Wearmouth, W.R., Dean, G.P. and Parkins, R.N., Corros. 29, 251–258 (1973).CrossRefGoogle Scholar