Selective Depositions of Fe-Containing Oxide Films on Mixed Selfassembled Organic Monolayers using Microcontact Printing

  • Hyunjung Shin (a1), Hyejin Im (a2), Seungbum Hong (a3), Kyongmi Lee (a1), Geunbae Lim (a1), Jong Up Jeon (a1), Eung Soo Kim (a2) and Y. Eugene Pak (a1)...

Abstract

In situ patterning of crystalline iron oxide thin layers has been achieved via microcontact printing (μCP) and selective deposition. μCP was used to pattern two different surface moieties of selfassembled organic monolayers (SAMs) on Au/Cr/Si substrates. An elastomeric stamp (poly(dimethylsiloxane); PDMS) having a submicron-size patterned relief structure was used to transfer either hexadecanethiol (HDT) SAMs, which are to sustain deposition of iron oxide precipitates, or hydrophilic SAMs (e.g. dithiothreitol (DTT)). Selective deposition is realized through precipitation of iron oxide phases from aqueous solutions at ambient temperature (<100°C). Aqueous solutions of 0.05 M of iron nitrate (Fe(NO3)2•9H20) containing urea under nitric acid (pH < 2) were prepared for selective depositions. X-ray photoelectron spectroscopic (XPS) results showed that iron oxide precipitates were deposited onto hydrophilic SAMs, but not onto HDT surfaces. As-deposited films onto DTT-SAM surfaces at 80°C were crystalline α-Fe2O3 (hematite). Fe3O4 and γ-Fe2O3 films were synthesized via annealing of as-deposited α-Fe2O3. Scanning electron microscopy, x-ray diffractometry, vibrating sample magnetometry, and optical microscopy were used to characterize the films' microstructures and properties.

Copyright

References

Hide All
1. Koster, E., in Magnetic recording technology, Mee, C. Denise and Daniel, Eric D., eds. New York, McGraw-Hill, 1995, 3.37–3.49
2. Dhara, S., Rastogi, A. C., and Das, B. K., J. Appl. Phys., 74 (11) 7019–21 (1993)10.1063/1.355062
3. Isuii, O. and Senda, M., J. Appl. Phys., 77, 5828 (1995)10.1063/1.359162
4. Gao, Y., Kim, Y. J., and Chamber, S. A., J. Mater. Res., 13, 2003–14 (1998)10.1557/JMR.1998.0281
5. Lin, J. K., Sivertsen, J. M., and Judy, J. H., J. Appl. Phys., 57, 4000–02 (1985)10.1063/1.334889
6. Shin, H., Collins, R. J., Guire, M. R. De, Heuer, A. H., and Sukenik, C. N., J. Mater. Res., 10, 692 (1995)10.1557/JMR.1995.0692
7. Bunker, B. C., Rieke, P. C., Tarasevich, B. J., Campbell, A. A., Fryxell, G. F., Graff, G. L., Song, L., Liu, J., Virden, J. W., and McVey, G. L., Science, 264, 4855 (1994)10.1126/science.264.5155.48
8. Agarwal, M., Guire, M. R. De, and Heuer, A. H., J. Am. Ceram. Soc., 80, 2967–81 (1997)10.1111/j.1151-2916.1997.tb03222.x
9. Rieke, P. C., Marsh, B. D., Wood, L. L., Tarasevich, B. J., Liu, J., Song, L., and Fryxell, G. E., Langmuir, 11, 318326 (1995)10.1021/la00001a054
10. Tarasevich, B. J. rieke, P. C., and Liu, J., Chem. Mater., 8, 292300 (1996)10.1021/cm940391e
11. Xia, Y. and Whitesides, G. M., Angew. Chem. Int. Ed., 37, 550–75 (1998)10.1002/(SICI)1521-3773(19980316)37:5<550::AID-ANIE550>3.0.CO;2-G
12. Kumar, A., Biebuyck, H. A., and Whitesides, G. M., Langmuir, 10, 14981511 (1994)10.1021/la00017a030
13. Xia, Y., Zhao, X.-M., and Whitesides, G. M., Microelectronic Engineering, 32, 255–68 (1996)10.1016/0167-9317(95)00174-3
14. Wilbur, J. L., Kumar, A., Kim, E., and Whitesides, G. M., Adv. Mater., 6, 600 (1994)10.1002/adma.19940060719
15. Kumar, A., Abbot, N. L., Kim, E., Biebuyck, H. A., and Whitesides, G. M., Acc. Chem. Res., 28, 219226 (1995)10.1021/ar00053a003
16. Xia, Y., Kim, E., and Whitesides, G. M., J. Electrochem. Soc., 143, 1070–79 (1996)10.1149/1.1836585
17. Xia, Y. and Whitesides, G. M., Langmuir, 13, 2059–67 (1997)10.1021/la960936e
18. Agarwal, M., Guire, M. R. De, and Heuer, A. H., Appl. Phys. Lett., 71, 891 (1997)10.1063/1.119679
19. Collins, R. J., Shin, H., Guire, M. R. De, Heuer, A. H., and Sukenik, C. N., Appl. Phys. Lett., 69, 860 (1996)10.1063/1.117916
20. Gao, Y., Kim, Y. J., Chambers, S. A., and Bai, G., J. Vac. Sci. Technol. A 15, 332 (1997)10.1116/1.580488
21. Graat, P. C. J., and Somers, M. A. J., Appl. Surf. Sci., 100/101, 3640 (1996)10.1016/0169-4332(96)00252-8
22. Shin, H., Wang, Y., Sampathkumaran, U., Guire, M. R. De, Heuer, A. H., and Sukenik, C. N., J. Mater. Res., accepted for the publication (1999)
23. Shin, H., Agarwal, M., Guire, M. R. De, and Heuer, A. H., Acta Mater, 46, 801–15 (1998)10.1016/S1359-6454(97)00258-9

Selective Depositions of Fe-Containing Oxide Films on Mixed Selfassembled Organic Monolayers using Microcontact Printing

  • Hyunjung Shin (a1), Hyejin Im (a2), Seungbum Hong (a3), Kyongmi Lee (a1), Geunbae Lim (a1), Jong Up Jeon (a1), Eung Soo Kim (a2) and Y. Eugene Pak (a1)...

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed