Rapidly Solidified Microstructures in a Ti-22 Wt% Fe Alloy

Published online by Cambridge University Press:  21 February 2011

W. A. Baeslack III ,
L. Weeter ,
S. Krishnamurthy ,
P. Smith  and
F. H. Froes
W. A. Baeslack III
Affiliation:
Department of Welding Engineering, The Ohio State University, Columbus, OH 43210
L. Weeter
Affiliation:
Department of Welding Engineering, The Ohio State University, Columbus, OH 43210
S. Krishnamurthy
Affiliation:
Materials Laboratory/Air Force Wright Aeronautical Laboratories, WPAFB OH 45433
P. Smith
Affiliation:
Materials Laboratory/Air Force Wright Aeronautical Laboratories, WPAFB OH 45433
F. H. Froes
Affiliation:
Materials Laboratory/Air Force Wright Aeronautical Laboratories, WPAFB OH 45433
Get access

Abstract

Rapidly-solidified microstructures were produced in aTi-22 wt% Fe alloy by laser surface melting, melt extraction, melt spinning and splat cooling. Increased cooling rates during solidification promoted increasingly finer beta grain sizes ranging from approximately 75 microns in a laser melt to 0.5 to 2.0 microns for splats. Beta grain morphologiesw ere generally equiaxed, although epitaxially-nucleated columnar grains were observed at the pool-substrate interface for laser melts. Fitting of the equiaxed beta grain size data to a λ0 = Boε−n0 power relationship for homogenous nucleation and isotropic growth resulted in Bo = 3 × 104 and no = 0.62. The refinement of dendrite structure with increasing cooling rate was also documented for laser melts. Dendrite spacing versus cooling rate data were fitted to a similar general power relationship and resulted in B1 = 45 and n1 = 0.34.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 28: Symposium F – Rapidly Solidified Metastable Materials , 1983 , 375
Copyright
Copyright © Materials Research Society 1984

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Maykuth, D. J., Ogden, H. R. and Jaffee, R. I., DMIC Rpt. 136A, 65 (1960).Google Scholar
2. Nurminen, J. I. and Brody, H. D., Titanium Science and Technology, Vol. 3, Jaffee, R. and Burte, H. ets. (Plenum Press, New York 1973) pp. 1893–1914.Google Scholar
3. Boswell, P. G. and Chadwick, G. A., Scripta Met. 11, 459 (1977)10.1016/0036-9748(77)90157-0Google Scholar
4. Jones, H., Rapid Solidification of Metals and Alloys, (The Institute of Metallurgists, London 1982).Google Scholar