Quantum dots of InAs/GaSb type II superlattice for infrared sensing
Published online by Cambridge University Press: 21 March 2011
Abstract
Throughout the past years, significant progress has been made in Type II (InAs/GaSb) photovoltaic detectors in both LWIR and VLWIR ranges. BLIP performance at 60K for 16μm photovoltaic type II detectors has been successfully demonstrated for the first time. The detectors had a 50% cut-off wavelength of 18.8 μm and a peak current responsivity of 4 A/W at 80K. A peak detectivity of 4.5×1010cm·Hz1/2/W was achieved at 80K at a reverse bias of 110mV. Detectors of cutoff wavelength up to 25μm have been demonstrated at 77K. The great performance of single element detectors appeals us to lower dimensional structures for both higher temperature performance and possible wavelength tunability. Simple calculations show that quantum effects will become significant when the lateral confinement is within tens of nanometers. The variation of applied gate voltage will move the electron and hole energy levels unevenly. The cutoff wavelength of the superlattice will vary accordingly. Auger recombination will also decrease and higher temperature operation becomes possible. In this talk, the latest results will be discussed.
- Type
- Research Article
- Information
- Copyright
- Copyright © Materials Research Society 2002