Bi‐Pb‐Sr‐Ca‐Cu‐0 superconductors were prepared by the laser pedestal growth method. The high Tc phase was created only by post annealing. As the growing speed increased, the annealing time necessary to obtain a Tc above 100K decreased. When the low Tc phase was aligned with the growing direction, Tc was under 100K, but a Jc of 15B0A/cm2(77.3K, OT) was obtained. In this case, magnetic field dependence below 300 gauss was superior to that of Pb‐free materials.