Photochemical Vapor Deposition of Amorphous Silicon Using Mercury Photosensitization of Disilane

Published online by Cambridge University Press:  21 February 2011

Yasuo Tarui
Affiliation:
Faculty of Technology, Tokyo University of Agriculture and Technology, Koganei, Tokyo, Japan
Katsumi Aota
Affiliation:
Faculty of Technology, Tokyo University of Agriculture and Technology, Koganei, Tokyo, Japan
Takashi Sugiura
Affiliation:
Faculty of Technology, Tokyo University of Agriculture and Technology, Koganei, Tokyo, Japan
Tadashi Saitoh
Affiliation:
Central Research Laboratory, Hitachi, Ltd., Kokubunji, Tokyo, Japan
Get access

Abstract

High-rate deposition of amorphous silicon films using the mercury-photosensitized reaction of disilane gas is described. The deposition rate depends upon reactant pressure, light intensity, and concentration of mercury atoms. A maximum rate of 100 nm/min is attained at a 250°C substrate temperature and a disilane pressure of 200 Pa. This rate is about 3 times higher than that for monosilane gas.

Generally, the optical gap of the deposited films range from 1.7 to 1.8 eV, although the value decreases slightly with increasing substrate temperature. Photoconductivity under AM1 irradiation is 2×10−4 mho·cm−1 at a 250°C substrate temperature and the ratio of photoconductivity to dark is around 104. From the infrared data, amorphous silicon films are found to include only an SiH bond at substrate temperatures of 200° to 300°C. Hydrogen content is 10 to 13%. These data suggest that silicon films can be used in thin-film electronic device fabrication.

Type
Research Article
Copyright
Copyright © Materials Research Society 1984

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Ehrlich, D. J., Osgood, R. M. Jr., and Deutsch, T. F., IEEE J. of Quantum Electronics QE-16, 1233 (1980).Google Scholar
2. Peters, J., Technical Digest of IEDM, p. 240 (1981).Google Scholar
3. Kumagawa, M., Sunami, H., Terasaki, T., and Nishizawa, J., Jpn. J. Appl. Phys. 7, 1332 (1968).CrossRefGoogle Scholar
4. Itoh, H., Hatanaka, M., Mizuguchi, K., Miyake, K., and Abe, H., Proc. 4th Symp. Dry Process (The IEEJ, Tokyo, 1982).Google Scholar
5. Saitoh, T., Matsubara, S., Muramatsu, S., and Migitaka, M., Proc. 14th Conf. Solid State Devices, Tokyo, 1982, Jpn. J. Appl. Phys. 22 (1983), Supplement 22–1, p. 617.CrossRefGoogle Scholar
6. Saitoh, T., Muramatsu, S., Shimada, T., and Migitaka, M., Appl. Phys. Lett. 42, 678 (1983).Google Scholar
7. Tarui, Y., Sorimachi, K., Fujii, K., Aota, K., and Saitoh, T., to be published in J. Non-Crystalline Solids.Google Scholar
8. Saitoh, T., Shimada, T., Migitaka, M., and Tarui, Y., to be published in.Google Scholar
9. Emeleus, H. J. and Stewart, K., Trans. Faraday Soc. 32, 1577 (1936).CrossRefGoogle Scholar
10. Mishima, Y., Hirose, M., Osaka, Y., Nagamine, K., Ashida, Y., Kitagawa, N., and Isogaya, K., Jpn. J. Apl. Phys. 22, L46 (1983).CrossRefGoogle Scholar
11. Okabe, H., “Photochemistry of Small Molecules,” John Wiley & Sons, Inc. (1978).Google Scholar
12. Perkins, G. G. A. and Lampe, F. W., J. Am. Chem. Soc. 102 (11) 3764 (1980).Google Scholar