Phase Stability and High Temperature Tensile Properties of W doped gamma-TiAl

Published online by Cambridge University Press:  21 March 2011

Keizo Hashimoto ,
Hirohiko Hirata  and
Youji Mizuhara
Keizo Hashimoto
Affiliation:
Dept. of Materials Science & Eng. Teikyo University, Utsunomiya, 320–8551, JAPAN
Hirohiko Hirata
Affiliation:
Dept. of Materials Science & Eng. Teikyo University, Utsunomiya, 320–8551, JAPAN
Youji Mizuhara
Affiliation:
Advanced Technology Research Labs. Nippon Steel Corp., Hikari, 743–8510, JAPAN
Get access

Abstract

Tungsten (W) doped γ-TiAl is one of promising alloys among many other proposed TiAl base alloys, for the purpose of structural applications at elevated temperatures. Ingots of W doped γ-TiAl were produced by plasma arc melting, followed by homogenizing heat treatment and isothermal forging to control their microstructures. The phase stability of W doped γ-TiAl has been studied quantitatively, using the specimens quenched from 1273 K. Equilibrium compositions of consisting phases were analyzed by means of EDS analysis in a TEM. An isothermal cross section of the Ti-Al-W ternary phase diagram at 1273K has been proposed based on the experimental observations. Small amounts of W addition (< 1at%) to Ti-48at%Al cause a phase shift from α2+γ to α2+β+γ, which suggests that W is the strongest β stabilizer among transition metals, such as Cr and Mo. Mechanical property measurements of W doped γ-TiAl show that the high temperature tensile strength has been improved by the W addition. Relationships between the microstructures and the mechanical properties of W doped γ-TiAl have been discussed.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 646 , 2000 , N7.8.1
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Lipsitt, H.A., Shechtman, D. and Schafrik, R.E., Met. Trans., 6A, (1975) 1991 10.1007/BF03161822Google Scholar
2. Blackburn, M.J. and Smith, M.P., US Patent 4,294,615 (1981)Google Scholar
3. Kawabata, T., Tamura, T. and Izumi, O., MRS Symp. Proc. 133, (1989) 329 10.1557/PROC-133-329Google Scholar
4. Kim, Y-W., JOM 41, No.7, (1989) 2410.1007/BF03220267Google Scholar
5. Huang, S.C., US Patent 4,879,092 (1989)Google Scholar
6. Austin, C.M. and Kelly, T.J., Structural Intermetallics. Eds. by Darolia, R. et al. (Seven Springs) TMS (1993) 143 Google Scholar
7. Hashimoto, K., Hanamura, T. and Mizuhara, Y., The 7th Symp. on High-Performance Materials for Severe Environments. Nov. (1996) 69 Google Scholar
8. Hashimoto, K., Hanamura, T. and Mizuhara, Y., The 8th Symp. on High-Performance Materials for Severe Environments. Sep. (1997) 81 Google Scholar
9. Lundstrom, D. and Karlsson, B., Structural Intermetallics. Eds. by Nathal, M.V. et al. TMS (1997) 461 Google Scholar
10. Lupinc, V. et al, Structural Intermetallics. Eds. by Nathal, M.V. et al. TMS (1997) 515 Google Scholar
11. Kim, Y-W and Dimiduk, D.M., Structural Intermetallics. Eds. by Nathal, M.V. et al. TMS (1997) 531 Google Scholar
12. Hashimoto, K., Kimura, M. and Mizuhara, Y., Intermetallics 6 (1998) 667 Google Scholar