Phase Composition and Leach Resistance of Actinide-Bearing Murataite Ceramics

  • Sergey Stefanovsky (a1), S.V. Yudintsev (a2), B.S. Nikonov (a3), A.V. Mokhov (a4), S.A. Perevalov (a5), O.I. Stefanovsky (a6) and A.G. Ptashkin (a7)...

Abstract

Phase composition of the murataite-based ceramics containing 10 wt.% ThO2, UO2, NpO2 or PuO2 and leaching of actinides using a MCC-1 procedure were studied. The ceramics were prepared by melting of oxide mixtures in Pt ampoules in air at ∼1500 °C. They are composed of predominant murataite-type phases and contain traces of extra phases (rutile, crichtonite, perovskite). At least two murataite-related phases with five- and eight-fold elementary fluorite unit cell (5C and 8C) were simultaneously observed. Minor phase 3C (murataite) in the ceramics doped with ThO2 and UO2 was also found. In the Th-bearing sample the 5C phase prevails over the 8C phase. In the U-bearing ceramic they co-exist in comparable amounts. The sample produced at 1500 °C contains crichtonite whereas the ceramic produced at lower temperature (1400 °C) contained rutile. Higher temperature favors further rutile reactions with formation of crichtonite. The Np- and Pu-doped ceramics are also composed of major the 5C and the 8C phases and minor rutile and crichtonite (in Pu-loaded sample only). Unlike the sample prepared under slightly re-ducing conditions (in glassy carbon crucible) the Pu-doped ceramic produced under neutral conditions (in Pt ampoule) doesn’t contain perovskite-type phase. Occurrence of perovskite in the first sample was sup-posed to be due to reduction of some Pu(IV) to Pu(III) during experiment. Leach rates (7-day MCC-1 test, 90 °C) of the actinide elements from all the ceramics studied are at the level of 10-6-10-7 g/(m2·day).

Copyright

References

Hide All
1. Ryerson, F.J., J. Amer. Ceram. Soc. 67 (1984) 7582.
2. Stefanovsky, S.V., Yudintsev, S.V., Nikonov, B.S., Omelianenko, B.I., Ptashkin, A.G., Mat. Res. Soc. Symp. Proc. 556 (1999) 121128.
3. Yudintsev, S.V., Stefanovsky, S.V., Nikonov, B.S., Omelianenko, B.I., Mat. Res. Soc. Symp. Proc. 663 (2001) 357365.
4. Portnov, A.M., Dubakina, L.S., Krivokoneva, G.K., Rep. AS USSR (Russ.) 261 (1981) 741744.
5. Ercit, T.S., Hawthorne, F.C., Canad. Miner. 33 (1995) 12231227.
6. Urusov, V.S., Organova, N.I., Karimova, O.V., Yudintsev, S.V., Stefanovsky, S.V., Russ. Acad. Sci. Rep. (Russ.: ДокладьІ PAH) 401 (2005) 226232.
7. Nuclear Waste Materials Handbook (Test Methods). Report DOE/TIC-11400 (1981).
8. Sobolev, I.A., Stefanovsky, S.V., Myasoedov, B.F., Kuliako, Y.M., Yudintsev, S.V., in: Plutonium Futures – The Science. Conf. Trans. Pillay, K.K.S. and Kim, K.C.(eds.), Santa Fe, July 10–13, 2000. (AIP Conf. Proc N532, 2000), pp. 122–124.
9. Zhang, Y., Hart, K.P., Begg, B.D., Keegan, E.A., Day, A.R., Brownscombe, A., Stewart, M.W.A., Mat. Res. Soc. Symp. Proc. 713 (2002) 389395.
10. Stefanovsky, S.V., Kirjanova, O.I., Yudintsev, S.V., Nikonov, B.S., Omelianenko, B.I., Phys. Chem. Mater. Treat. (Russ.) [3] (2001) 7280.

Keywords

Phase Composition and Leach Resistance of Actinide-Bearing Murataite Ceramics

  • Sergey Stefanovsky (a1), S.V. Yudintsev (a2), B.S. Nikonov (a3), A.V. Mokhov (a4), S.A. Perevalov (a5), O.I. Stefanovsky (a6) and A.G. Ptashkin (a7)...

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed