Non-Equilibrium Formation Of Silicon Nitride During Both Ball Milling And Ion Bombardment

Published online by Cambridge University Press:  10 February 2011

Z. L. Li
Affiliation:
Department of Electronic Materials Engineering, RSPhysSE, Australian National University, Canberra, 0200, Australia.
J. S. Williams
Affiliation:
Department of Electronic Materials Engineering, RSPhysSE, Australian National University, Canberra, 0200, Australia.
D. J. Llewellyn
Affiliation:
Department of Electronic Materials Engineering, RSPhysSE, Australian National University, Canberra, 0200, Australia.
J. Wong-Leung
Affiliation:
Department of Electronic Materials Engineering, RSPhysSE, Australian National University, Canberra, 0200, Australia.
M. Giersig
Affiliation:
Hahn Meitner Institute, Berlin, Germany.
D. J. Chivers
Affiliation:
AEA Technology, Harwell, Didcot, Berks, UK.
Get access

Abstract

Phase evolution during ball milling of Si in NH3 gas and during subsequent annealing has been studied and compared with nitride formation during ion bombardment of Si. X-ray diffraction, differential thermal analysis, Rutherford backscattering and channeling, combustion analysis and transmission electron microscopy have been used as analytical techniques. Results have shown that an amorphous SixNy(Fe) phase forms during milling which transforms into α-Si3N4 and FeSi2 on annealing. During ion bombardment, slightly N-rich Si3N4 is formed but it is mostly crystalline at temperatures between 150 and 450°C.

Type
Research Article
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Calka, A. and Williams, J. S., Mater. Sci. Forum 88–89, p. 787 (1992).Google Scholar
[2] Chen, Y., Li, Z.L. and Williams, J.S., J. Mater. Sci. Lett. 14, p. 542 (1995).Google Scholar
[3] Li, Z.L., Williams, J.S. and Calka, A., J. Appl. Phys. 81, p. 8029 (1997).Google Scholar
[4] Williams, J.S., Petravic, M., Svensson, B.G. and Conway, M., J. Appl. Phys. 76(3), p1840 (1994).Google Scholar
[5] Kilner, J.A. et al. Nucl. Instrum. Meth. B15, p. 214 (1986).Google Scholar
[6] Jesurum, C.E., Hobbs, L.W., Pulim, V. and Berger, B., Symp. KK. Fall MRS (1997)Google Scholar