Nickel-Alumina Composites: In Situ Synthesis by a Displacement Reaction, and Mechanical Properties

Published online by Cambridge University Press:  15 February 2011

Steven A. Jones
Affiliation:
Dept. of Chemistry, Cornell University, Ithaca, NY 14853
James M. Burlitch
Affiliation:
Dept. of Chemistry, Cornell University, Ithaca, NY 14853
Ersan Üstündag
Affiliation:
Dept. of Materials Science and Engineering, Cornell University, Ithaca, NY 14853
Jeannie Yoo
Affiliation:
Dept. of Materials Science and Engineering, Cornell University, Ithaca, NY 14853
Alan T. Zehnder
Affiliation:
Dept. of Theoretical and Applied Mechanics, Cornell University, Ithaca, NY 14853
Get access

Abstract

Nickel-alumina composites have the potential to be high performance materials. Alumina, with its excellent oxidation resistance, combined with a ductile phase such as nickel may provide a tough material with a lower density and higher Young's modulus, overall, a higher specific modulus than typical Superalloys. Dense, interpenetrating Ni-Al2O3 composites were synthesized using a displacement reaction between NiO and aluminum. The resulting composites were characterized in terms of their mechanical properties such as hardness, flexure strength, fracture toughness and elastic constants. The synthesis, characterization, and mechanical properties, as well as the effect of the interpenetrating microstructure on the toughening mechanisms and other properties will be discussed.

Type
Research Article
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Waterman, N. A. and Ashby, M. F.; 1991; CRC-Elsevier Materials Selector; Boca Raton.Google Scholar
[2] Tuan, W. H. and Brook, R. J., J. Eur. Ceram. Soc. 6, 31 (1990).Google Scholar
[3] Ekströrm, T., J. Euro. Ceram. Soc. 11, 487 (1993).Google Scholar
[4] Üstündag, E., Subramanian, R., Diekmann, R. and Sass, S. L., Acta Metall. Mater. 41, 2153 (1993).Google Scholar
[5] Breval, E., Deng, Z., Chiou, S. and Pantano, C. G., J. Mat. Sci 27, 1464 (1992).Google Scholar
[6] Üstündag, E., Ret, P., Subramanian, R., Dieckmann, R. and Sass, S. L., J.Mater. Sci. in press (1994).Google Scholar
[7] Rapp, R. A., Ezis, A. and Yurek, G. J., Metal. Trans. 4, 1283 (1973).Google Scholar
[8] Henager, C. H. Jr., Brimhall, J. L. and Hirth, J. P., Mat. Sci. Eng. A155, 109 (1992).Google Scholar
[9] Sperisen, T. and Mocellin, A., J. Mat. Sci. 27, 1121 (1992).Google Scholar
[10] Chernenko, E. V., Afanas'eva, L. F., Lebedeva, V. A. and Rozenband, V. I., Fiz. Goreniya Vzryva 24, 3 (1988).Google Scholar
[11] Henager, C. H. Jr., and Brimhall, J. L., Scripta Metal. et Mater. 29, 1597 (1993).Google Scholar
[12] Jones, S. A., and Burlitch, J. M., Mater. Let. 19, 233 (1994).Google Scholar
[13] Munz, D., Bubsey, R. T. and Shannon, J. L., J. Am. Ceram. Soc. 63, 300 (1980).Google Scholar
[14] Wu, S.-X. in Chevron-Notched Specimens, Testing. and Stress Analysis, edited by Underwood, J. H., Freiman, S. W. and Baratta, F. I. (ASTM STP 855 Philadelphia, PA, 1984).Google Scholar
[15] ASTM Syandard C 1161-90:, Flexural Strength of Advanced Ceramics at Ambient Temperature, Philadelphia, 1991).Google Scholar
[16] Kolhe, R., Üstündag, E., Hui, C.-Y. and Sass, S. L., unpublished results.Google Scholar