Neutron Diffraction Studies on Recrystallization of Solution Derived Lead Zirconate Titanates

Published online by Cambridge University Press:  22 February 2011

B. Morosin ,
A. C. Lawson ,
G.H. Kwei ,
J. A. Voigt  and
B. A. Tuttle
B. Morosin
Affiliation:
Sandia National Laboratories,Albuquerque, NM 87185-0345
A. C. Lawson
Affiliation:
Los Alamos National Laboratory, Los Alamos, NM 87545
G.H. Kwei
Affiliation:
Lawrence Livermore National Laboratory, Livermore, CA 94550
J. A. Voigt
Affiliation:
Sandia National Laboratories,Albuquerque, NM 87185-0345
B. A. Tuttle
Affiliation:
Sandia National Laboratories,Albuquerque, NM 87185-0345
Get access

Abstract

We performed neutron powder diffraction on solution-derived lead zirconate titanates (PZT). Three compositions, PZT 45/55, PZT 20/80 and PbTiO3, were investigated. The materials were annealed so that the perovskite phase had just begun to grow from the precursor phase. In our materials this precursor phase is the pyrochlore rather than fluorite phase. The results show that in the pyrochlore phase, the (Ti,Zr) and the Pb are ordered in their crystallographic sites while the O are essentially disordered in both of the two usual pyrochlore anion sites.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 376: Symposium BB – Neutron Scattering in Materials Science , 1994 , 609
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1 see H 7.2 and H 7.3 San Francisco 1994 MRS and 12-5.9 Boston 1994 MRS meetings.Google Scholar
2 Wilkinson, A. P., Speck, J. S., Cheetham, A. K., Natarajan, S. and Thomas, J. M., Chem. Mater. 6, 75 (1994).Google Scholar
3 Yamaguchi, O., Fukuoka, T., and Kawakami, Y., J. Mater. Science Lett. 9, 958 (1990).Google Scholar
4 Kwok, C. K. and Desu, S. B., Appl. Phys. Lett. 60, 1430 (1992).Google Scholar
5 Voigt, J. A., Tuttle, B.A., Headley, T.J., Eatough, M.O., Lamppa, D.L., and Goodnow, D., Mat. Res. Soc. Symp. Proc. 310, 15 (1993).Google Scholar
6 Schwartz, R.W., Bunker, B.C., Dimos, D., Assink, R.A., Tallant, D.R., Weinstock, I., and Haaland, D.M. in Proc of 3rd Int. Symp. on Integrated Ferroelectrics 535 (1991).Google Scholar
7 Yi, G., Wu, Z., and Sayer, M., J. Appl.Phys. 64 2717 (1988).Google Scholar
8 Larson, A. C. and VonDreele, R. B., Los Alamos Natl Lab Report No. LAUR 86-748 (1986).Google Scholar
9 Budd, K., Dey, S., and Payne, D.A., Proc. Br. Ceram. Soc. 36, 107 (1986).Google Scholar
10 Lakeman, C. and Payne, D.A., Proc. Ninth IEEE Sym. on Applications of Ferroelectrics, Penn State Univ. Aug 10-14, (to be published).Google Scholar