Magnetization and Interactions of Single Domain Sm2Co17 Particles Embedded in CaO Matrix

Published online by Cambridge University Press:  21 February 2011

Wenge Liu  and
Paul G. Mccormick
Wenge Liu
Affiliation:
Special Research Center for Advanced Mineral and Materials ProcessingThe University of Western Australia, Perth, Australia
Paul G. Mccormick
Affiliation:
Special Research Center for Advanced Mineral and Materials ProcessingThe University of Western Australia, Perth, Australia
Get access

Abstract

Investigation of the interactions in two magnetic composite systems composed of ∼8 vol% isolated Sm2Co17 nanoparticles of different size ranges in a CaO matrix has been made by comparing the isothermal remanent magnetization curves (IRM) with the dc demagnetization curves (DCD) using Wohlfarth remanence relation. The presence of a weak demagnetizing field was evidenced in the sample with smaller magnetic particles (7-90nm), indicating the magnetostatic interaction between the magnetic particles was dominant in this sample. The large positive deviation from Wolhfarth relation in the sample with larger particles (10-250nm) suggests the presence of multigrain particles in which neighboring grains interact strongly with each other. The hysteresis curves of the two composite systems were measured at temperatures between 5 and 350K. A nearly linear temperature dependence of the coercivity was observed in both samples up to 350 K. From these results it is shown that although the sizes of the Sm2Co17 particles are well below the critical size for single domain particle, there is no evidence that the magnetization reversals in these particles are coherent rotation.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 577: Symposium H – Advanced Hard and Soft Magnetic Materials , 1999 , 229
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Pardave-Horvath, M. and Takacs, L., Scripta Metall. Mater., 33, 1731 (1995).Google Scholar
2. Majetich, S.A., Scott, J. H., Kirkpatrick, E.M., Chowdary, K., Gallgher, K., McHentry, M.E., Nanostructured Mater., 9, 291 (1997).Google Scholar
3. Panagiotopoulos, I., Meng-Burany, X., and Handjipanayis, G.C., J. Magn. Magn. Mater., 172, 225 (1997).Google Scholar
4. Schalek, R.L., Leslie-Pelecky, D.L., Knight, J., Sellmyer, D.L., and Axtell, S.C., IEEE Trans. Mag., 31, 3772 (1995).Google Scholar
5. Chien, C.L. in Science and Technology of Nanostructured Magnetic Materials, edited by Hadjipanayis, G.C. and Prinz, G.A., Plenum Press, New York, 1991, 477.Google Scholar
6. Ding, J., Miao, W.F., McCormick, P.G., and Street, R., Appl. Phys. Lett., 67, 3804 (1995).Google Scholar
7. Ding, J., Tsuzuki, T., McCormick, P.G., and Street, R., J. Am. Ceram. Soc., 79, 2956 (1996).Google Scholar
8. Wohlfarth, E.P., J. Appl. Phys., 29, 595 (1958).Google Scholar
9. Gaunt, P., Hadjipanayis, G., and Ng, D., J. Magn. Magn. Mater., 54–57, 841 (1986).Google Scholar
10. Kelly, P.E., O'Grady, K., Mayo, P.I., and Chantrell, R.W., IEEE Trans. Mag., 25, 3881 (1989).Google Scholar
11. Liu, W. and McCormick, P.G., J. Magn. Magn. Mater., 195, 279 (1999).Google Scholar
12. Chen, D.X., Brug, J.A., and Goldfarb, R.B., IEEE Trans. Mag., 27, 3601 (1991).Google Scholar
13. Folks, L., Street, R., and Woodward, R., J. Appl. Phys., 75, 6271 (1994).Google Scholar
14. Ding, J., Smith, P.A.I., McCormick, P.G., and Street, R., J. Magn. Magn. Mater., 161, 303 (1996).Google Scholar