Leaching Behaviour of Zirconolite in 0.001M Citric Acid at 90°C Under Various Flow Regimes

  • Peter J. McGlinn (a1), Thierry Advocat (a2), Gilles Leturcq (a2), Terry I. McLeod (a1), Zaynab Aly (a1) and Patrick Yee (a1)...

Abstract

Nd-bearing zirconolite was leached at 90°C for 157 days in 0.001M citric acid under single-pass-flow-through conditions (modified MCC-4 protocol). Three different flow rates were used, ranging in an order of magnitude from 10 mL per day to 100 mL per day, to determine the effect of the rate of leachant replenishment on the durability of the zirconolite. Results of previous studies on the role of complexing agents on the leaching behaviour of single-phase zirconolite have been included in the discussion.

The pH of the citric acid solution was adjusted to 5 using KOH, mimicking that of the water in the parallel tests, to avoid the influence of pH on chemical durability of the zirconolite.

Simulated groundwater containing 0.001M citric acid at 90°C led to congruency in elemental releases and a diminution of release rate with time of about an order of magnitude, reaching virtual constancy after about 50 to 60 days to a level of about 10−5 g m−2 day−1. The most significant finding was that the elemental release rates of Nd, Ti and Zr (and Ca and Al where detected) were similar for all flow rates. Clearly, varying flow rate by up to an order of magnitude had no effect on elemental releases i.e. there is no solubility limit control on releases at 0.001M citric acid concentration.

An important finding of previous studies using identical leaching protocols with 0.001M citric acid, and inferred in our latest investigations reported here, was that there is no secondary layer development at the surface of the zirconolite to affect leach rates. In contrast, parallel tests carried out in deionised water instead of citric acid showed that hydroxides form in situ on the zirconolite surface, effectively forming hydrolysed zirconolite. This controls further dissolution of the zirconolite matrix due to the solubility limit being reached with respect to the hydrolysed phases rather than with zirconolite. Complexation by citrate ions prevents such control by hydrolysed species on zirconolite solubility.

Even under the more aggressive conditions imposed in these studies (0.001M citric acid), and regardless of flow rate of the leachant, elemental releases from zirconolite are very low for a candidate wasteform and demonstrate its attributes as a ceramic-based wasteform for the containment of actinides.

Copyright

References

Hide All
1. Vance, E.R., Begg, B.D., Day, R.A. and Ball, C.J., in Scientific Basis for Nuclear Waste Management, Mat. Res. Symp. Proc., Vol. 353 (1995).
2. Ebbinghaus, B., Konynenburg, R. Van, Vance, E. and Allender, J., in Waste Management proc. USA (1998).
3. Jostsons, A., Vance, E.R., Mercer, D.J. and Oversby, V.M., Scientific Basis for Nuclear Waste Management XVIII, Kyoto, Japan, October 23-27, 1994, pp. 775781 (2004).
4. Ringwood, A.E., Kesson, S.E., Reeve, K.D., Levins, D.M. and Ramm, E.J., “Synroc”, Radioactive Waste Forms for the Future, ed. Lutze, W. and Ewing, R.C. (Elsevier, 1988), pp 233334.
5. Leturcq, G., Advocat, T., Hart, K., Berger, G., Lacombe, J., and Bonnetier, A., American Mineralogist, 86, pp. 871880 (2001).
6. Leturcq, G., PhD thesis, University of Toulouse III, France, 207 p.(1998).
7. Leturcq, G., McGlinn, P.J., Barbé, C., Blackford, M.G. and Finnie, K.S., Applied Geochemistry, 20, Issue 5, pp. 899906 (2005).
8. Materials Characterization Center, Nuclear Waste Materials Handbook – Test Methods. DOE/TIC-11400 (1986).
9. McGlinn, P.J., McLeod, T., Leturcq, G., Aly, Z., Blackford, M.G., Zhang, Z., Li, H., Lumpkin, G.R., Scientific Basis for Nuclear Waste Management XXVII, Kalmar, Sweden, 15-19 June 2003, pp. 219224 (2004).
10. McGlinn, P.J., McLeod, T., Aly, Z., Zhang, Z., Advocat, T., Blackford, M.G., Li, H., Leturcq, G., In the Proceedings of ‘Atalante 2004 Intern. Conf. on Science for the Future Nuclear Fuel Cycles’, Nîmes, France, June 21-24, 2004. Paper P3-18.
11. Sillén, L.G. and Martell, A.E., Stability Constants of Metal-Ion Complexes, Special Publication, The Chemical Society, London, No. 17 (1964); No. 25 (1971).

Leaching Behaviour of Zirconolite in 0.001M Citric Acid at 90°C Under Various Flow Regimes

  • Peter J. McGlinn (a1), Thierry Advocat (a2), Gilles Leturcq (a2), Terry I. McLeod (a1), Zaynab Aly (a1) and Patrick Yee (a1)...

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed