High Strength Concrete and Mortars in High Temperature Environments

Published online by Cambridge University Press:  22 February 2011

Robert B. Williamson  and
Ahmed I. Rashed
Robert B. Williamson
Affiliation:
University of California, Department of Civil Engineering, Berkeley, CA 94720.
Ahmed I. Rashed
Affiliation:
University of California, Department of Civil Engineering, Berkeley, CA 94720.
Get access

Abstract

A number of new materials are presently being introduced for application in high temperature environments. Though some of these are old materials fabricated with new methods or processes, many are actually new. This paper focuses on the use of high strength concretes or mortars for application to high temperature environments, such as furnaces or boilers for coal gasification and similar processes requiring high pressure and temperature. This paper reports the results of an investigation on the high.temperature performance of mortar of different strengths incorporating 0%, 8% and 16% of condensed silica fume (CSF). The experiments described have been carried out to compare the performance of different strength level mortars with different CSF contents. Generally speaking, it was found that low strength mortar with CSF is less susceptible to strength loss after high temperature exposure than mortar without CSF. On the other hand, high strength mortar with CSF seems to be more sensitive to high temperature than high strength mortar without CSF since it retains only 65% of its room temperature strength after heating to 3200C as compared to regular high strength mortar which retains 95% of its room temperature strength.

Though there may be a possible practical problem in using high strength CSF concrete, this shown loss of strength in high strength CSF concrete upon heating may prove very important in giving us insight into the fundamental mechanisms of strengthening concrete with CSF. An explanation is hypothesized on the observed behavior of high strength CSF concrete, which will produce a theory for one of the ways in which CSF strengthens portland cement paste. It is theorized that the CSF touohens the portlandite in high strength paste, but after heating to 320 C, the CSF particles which have been converted to C-S-H have lost their ability to toughen the portlandite.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 42: Symposium L – Very High Strength Cement-Based Materials , 1984 , 295
Copyright
Copyright © Materials Research Society 1985

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1]. Grutzeck, M. W., Atkinson, S., and Roy, D. M., “Mechanism of Hydration of Condensed Silica Fume in Calcium Hydroxide Solutions.” ACI Publication SP 79–33, 643–652 (1983).Google Scholar
[2]. Gjorv, O., “Durability of Concrete Containing Condensed Silica Fume,” ACI Publication, SP 79–36, 695–702 (1983).Google Scholar
[3]. Hertz, K., “Heat Induced Explosion of Dense Concrete,” Lyngby, Technical University of Denmark, Institute of Building Design Report, No. 166, 1984.Google Scholar
[4]. Williamson, R. B., “Solidification of Portland Cement”, Progress in Materials Science, 15, 189–286 (1972).CrossRefGoogle Scholar
[5]. Williamson, R. B., Science, 164, 149–151 (1969).10.1126/science.164.3879.549Google Scholar
[6]. Schneider, U., “Verhalten von Beton bei hohen Temperaturen,” Deutscher Ausschuss fur Stahlbeton, Heft 337, 1982.Google Scholar