Heteroepitaxial growth of TaN on MgO(001) and TiN(001)/Si(001) by pulsed laser deposition

Published online by Cambridge University Press:  21 March 2011

H. Y. Cheung  and
K.H. Wong
H. Y. Cheung
Affiliation:
Department of Applied Physics and Materials Research Centre, The Hong Kong Polytechnic University, Hunghom, Kowloon, Hong Kong, People's, Republic of China
K.H. Wong
Affiliation:
Department of Applied Physics and Materials Research Centre, The Hong Kong Polytechnic University, Hunghom, Kowloon, Hong Kong, People's, Republic of China
Get access

Abstract

Epitaxial TaN(001) films have been successfully grown on MgO(001) single crystal and TiN(001) buffered Si(001) substrates by pulsed laser deposition method. Crystalline TaN layers of about 100 nm thick were deposited under a base pressure of 5 × 10−6 Torr and at substrate temperatures ranging from 500°C to 700°C. X-ray diffraction results suggested that stoichiometric TaN films with cube-on-cube <001>TaN∥<001>MgO heteroepitaxy are obtained in this temperature range. Plan-view and cross-sectional electron microscopy analysis revealed excellent structural quality and sharp interface boundary. TaN films grown on TiN(001) buffered Si(001), however, showed a mixture of TaNx (with x ≤ 1) components. Although the (001)-orientated TaN is always present prominently, the nitrogen deficient TaNx components are often co-existed in the films and show up as a broad peak in the X-ray diffraction profile. Stoichiometric and single phase TaN(001) films can only be obtained in a narrow temperature window at around 550oC and heteroepitaxial relation <001>TaN∥<001>TiN∥<001>Si has been demonstrated.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 672: Symposium O – Mechanisms of Surface and Microstructure Evolution in Deposited Films and Film Structures , 2001 , O10.9
Copyright
Copyright © Materials Research Society 2001

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. So, F. C. T., Kolawa, E., Zhao, X. A., Pan, E. T. S. and Nicolet, M. A., J. Appl. Phys. 64, 2787 (1988).Google Scholar
2. Sun, Xin, Kolawa, Elzbieta, Chen, Jen-Sue, Ried, Jason S. and Nicolet, Marc-A., Thin Solid Films, 236, 347 (1993).Google Scholar
3 Au, C. L., Anderson, W. A., Schmitz, D. A., Flassayer, J. C. and , Collins, J. Mater. Res. 5, 1224 (1990).Google Scholar
4. Oku, Takeo, Karva, Eiji, Uekubo, Masaki, Takahiro, Katsumi, Yamaguchi, Sadae, Murakami, Masanori, Appl. Surf. Sci. 99, 265 (1996).Google Scholar
5. Toth, L. E., Transition Metal Carbides and Nitrides, Academic Press, New York, (1971).Google Scholar
6. Abdin, S. and Val, C., Thin Solid Films, 57, 327 (1979).Google Scholar
7. Rivaud, L., Barnett, S. A., Greene, J. E. and Marciniec, E. T., J. Vac. Sci. Technol. A9, 2180 (1991).Google Scholar
8. Mehrotra, B. and Stimmell, J., J. Vac. Sci. Technol. B5, 1736 (1987).Google Scholar
9. Zhang, Q. Y., Chen, B., Li, G. B., Jin, S., Chen, F. X., Yang, D. Z. and Zhu, Y. C., Surf. Coat. Technol., 66, 468 (1994).Google Scholar
10. Ensinger, W., Kiuchi, M. and Satou, M., J. Appl. Phys., 77, 6630 (1995).Google Scholar
11. Zhu, K. Y., Jun, Y. and Qin, O., Surf. Coat. Technol., 66, 326 (1994).Google Scholar
12. Greene, J. E., Shin, C. S., Gall, D., Desjardins, P., Vailionis, A., Kim, H., Petrov, I., Appl. Phys. Lett, 75, 3808 (1999).Google Scholar
13. Zheleva, T., Jagannadham, K., Narayan, J., J. Appl. Phys. 75, 86 (1994).Google Scholar