The Effects of N2 and Ar as the Ambient Gas During Rapid Thermal Annealing of Tungsten Silicide

Published online by Cambridge University Press:  26 February 2011

Paul Martin Smith  and
Michael O. Thompson
Paul Martin Smith
Affiliation:
Department of Materials Science, Cornell University, Ithaca, NY 14853
Michael O. Thompson
Affiliation:
Department of Materials Science, Cornell University, Ithaca, NY 14853
Get access

Abstract

Rapid thermal annealing of amorphous tungsten silicide thin films (W0.62 Si0 38) on Si at 1100°C in Ar and N2 ambient gases was studied. All films annealed in N2 exhibited good adhesion and remained smooth with no large grain growth. Films annealed in Ar showed grain nucleation and growth from the film perimeter until a critical stress was achieved, followed by stress-assisted grain growth. The resulting growth of large columnar grains caused the films to delaminate. Removal of the surface oxide/nitride layer from the silicide prior to annealing resulted in uniform nucleation and growth over the entire film during annealing in Ar, with no stress-assisted grain growth or film delamination. No difference, however, was observed during annealing in N2. These results suggest that a surface film produced during annealing in N2 slows the nucleation and growth and consequently enhances film adhesion.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 100: Symposium – A Fundamentals of Beam-Solid Interactions and Transient Thermal Processing , 1988 , 707
Copyright
Copyright © Materials Research Society 1988

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Chen, John Y. and Roth, Lynette B., Solid State Technology 27 (8), 145, (1984).Google Scholar

2 Mohammadi, F. and Saraswat, K.C., J. Electrachem. Soc. 127 (2), 450 (1980).CrossRefGoogle Scholar

3 Shaw, J.M. and Amick, J.A., RCA Review 31 (2), 306 (1970).Google Scholar

4 Zirinsky, S., Hammer, W., d'Heurle, F., and Baglin, J., Appl. Phys. Lett. 33 (1), 76 (1978).CrossRefGoogle Scholar

5 Silversmith, D.J., Rathman, D.D., and Mountain, R.W., Thin Solid Films 93, 413 (1982).CrossRefGoogle Scholar

6 Bomchil, G., Goeltz, G., and Tortes, J., Thin Solid Films 140, 59 (1986).CrossRefGoogle Scholar

7 Chang, Chuan C. and Quintana, G., Journal of Electron Spectroscopy and Relatul Phenomena 2, 363, (1973).CrossRefGoogle Scholar

8 Nicolet, Marc-A., and Lau, S.S., in VLSI Electronics: Microstructure Science, Vol.6, edited by Einspruch, Norman G. and Larrabee, Graydon B. (Academic Press, New York, 1983) p. 409.Google Scholar

9 Siegal, M. (private communication).Google Scholar

10 Tsaur, B-Y., Chen, C.K., Anderson, C.H. Jr., and Kwong, D.L., J. Appl. Phys. 57 (6), 1890 (1985).CrossRefGoogle Scholar

11 Göltz, G., Torres, J., Lajzerowicz, J. Jr., and Bomchil, G., Thin Solid Films 124, 19 (1985).CrossRefGoogle Scholar

12 Tsai, M.Y., d'Heurle, F.M., Petersson, C.S., and Johnson, R.W., J. AppI. Phys. 52 (8), 5350 (1981).CrossRefGoogle Scholar

13 Sedgwick, T.O., d'Heurle, F.M., and Cohen, S.A., J. Electrachem. Sac. 131 (10), 2446 (1984).CrossRefGoogle Scholar

14 Choi, K.W. and Ahn, K. Y., J. Vac. Sci. and Technol. A 3 (6), 2272 (1985).CrossRefGoogle Scholar

15 Fukumoto, Masanori and Ohzone, Takashi, Appl. Phys. Lett. 50 (14), 894 (1987).CrossRefGoogle Scholar

16 Thomas, R.E. (private communication).Google Scholar

17 Thomas, R.E., Appl. Surface Sci. 26 534 (1986).CrossRefGoogle Scholar