Effect of Annealing and Passivation on the Electromigration and Linewidth Dependence

  • R.O. Carnes (a1), C.H. Lee (a1), P.T. Keating (a2), E.M. Barrall II (a3), B.R. York (a3), G.M. Grivna (a4), S.W. Bauguess (a5), M.L. Dreyer (a5) and S.R. Edwards (a5)...

Abstract

Continued miniaturization of conductor geometry below 0.5μm has by a concomitant decrease in Al deposition temperature, typically below 300°C. The degree of reliability exhibited by these films is strongly dependent on the grain size distribution and metallurgical configuration. This investigation focuses on the impact of post-deposition processing on changes in conductor microstructure and electromigration for films deposited at low temperature. AlCu(l%)Si(l%) was deposited at 300°C on PECVD phosphosilicate glass. The impact of post-deposition thermal budget on the as deposited grain size and distribution, preferred orientation and stress/strain states were analyzed using scanning electron microscopy, X-Ray diffraction and bending beam technique, respectively. These characteristics were also measured on unpassivated films subjected to the same thermal budget as SiO2 passivated films so that the geometric confinement and Al-SiO2 surface interaction could be quantified. Electromigration characteristics were measured for linewidths in the range W=1.0μm to W=10μm, for passivated and unpassivated films. A direct correlation between passivation and grain size was observed for both failure modes. This paper will also discuss the relationship between film stress and preferred orientation, the observed failure modes and their linewidth dependence.

Copyright

References

Hide All
1 Kisselgof, L., Baranowski, S.P., Broomfield, M.C., Spooner, T., Elliot, L., Brooke, L., Lloyd, J.R., SPIE V1805, Submicrometer Metallization (1992), 154163.
2 Domenicucci, A., Vook, R.W., J.Vac.Sci.Technol. (1991), 581585.
3 Gardner, D.S., Longworth, H.P., Flinn, P.A., VMIC Conf (1990), 243-253.
4 Dirks, A.G., Augur, R.A., De Veirman, A.E.M., Thin Solid Films, v246 (1994), 164171.
5 Kwok, T., Chan, K.K., Simko, J., J.Vac.Sci.Technol. A, V9,No.4 (1991), 25232526.
6 Akiya, M., Nakamura, H., Arita, Y., J. Electrochem. Soc., V137,No.7, (1990), 22522256.
7 Rodbell, K.P., Knorr, D.B., Mis, J.D., J. of Electronic Materials, V22, No.6, (1993), p 597606.
8 Cho, J., Thompson, C.V., J. of Electronic Materials, V19, No.11, (1990), 12071212
9 Campbell, A.N., Mikawa, R.E., Knorr, D.B., V22, No.6, (1993), 589596.
10 Baerg, W., Wu, K., Davies, P., Dao, G., Fraser, D., IEEE-IRPS, (1990), 119 123.
11 Babcock, S.E. Balluffi, R.W., Acta Metall. V37,No.9,(1989), 23672376.
12 Bauer, C.L., Tang, P.F., Defect and Diffusion Forum, V.66–69, (1989), 11431152.
13 Ho, P.S., Moske, M..A., Hu, C.K., SPIE V1805, Submicrometer Metallization (1992), 116129.
14 Besser, P.R., Ph.D. Dissertation, Stanford University, (1993)
15 Clarke, A.P., Saimoto, S., Ho, P., AIP Conference Proceedings 305, (1994), 126136.
16 Baldini, G.L., Scorzoni, A., IEEE-Trans on Electron Devices, V38, No.3, (1991), 469475.
17 Matsunaga, N., Shibata, H., Hashimoto, K., 1992 Symposium on VLSI Technology Digest of Technical Papers, 7677.
18 Besser, P.R., Bader, S., Venkatraman, R., Bravman, J.C., MRS Symp. Proc. V309, (1993), 255260.
19 Shute, C.J., Cohen, J.B., J. Mater. Res., Vol.6, No.5, (1991), 950956.
20 Chew, H.Z., Fieber, C.A., Kelley, P., Lai, T.T., Ryan, V., SPIE V1805, Submicrometer Metallization (1992), 164168.
21 Anderson, S.G.H., Yeo, I.S., Jawarani, D., and Ho, P.S., SPIE V1805, Multilevel Interconnect (1993), 130137.
22 Anderson, S.G.H., Yeo, I.S., Ho, P.S., Ramaswami, S., Cheung, R., MRS Symp. Proc. V309, (1993), 261268.
23 Grivina, G., Leathersich, C., Shin, H., Cowden, W.G., J. Vac.SCi. Technol. B, V11,No.1, (1993), 5560.
24 Electromigration in Thin Films, by F.M. d’Heurle, P.S. Ho.
25 Agarwala, B.N., Attardo, M.J., Ingraham, A.P., J. Appl. Phys., V41,No.10, (1970), 39543955.
26 Attardo, M.J., Rutledge, R., Jack, R.C., J. Appl. Phys., V42, No.11, (1971), 43434349.
27 Arzt, E., Nix, W.D., J. Mater. Res. V6, No.4, (1991), 731736
28 M.L, Dreyer, Varker, C.J., Appl. Phys. Lett., V60, No.l5, (1992), 18601862.
29 Kardiawarman, . et al. , Applications of a multifiber collimating lens to thin film structure analysis, SPIE proceedings, 1995.

Effect of Annealing and Passivation on the Electromigration and Linewidth Dependence

  • R.O. Carnes (a1), C.H. Lee (a1), P.T. Keating (a2), E.M. Barrall II (a3), B.R. York (a3), G.M. Grivna (a4), S.W. Bauguess (a5), M.L. Dreyer (a5) and S.R. Edwards (a5)...

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed