Discontinuous Dissolution of Spinel Precipitates in the Al2O3-Fe2O3 System

Published online by Cambridge University Press:  15 February 2011

Ho-Yong Lee  and
Suk-Joong L. Kang
Ho-Yong Lee
Affiliation:
Department of Materials Science and Engineering, Sunmoon University, Tangjeong-Myun, Asan-Kun, Chungnam 337-840, Korea
Suk-Joong L. Kang
Affiliation:
Department of Ceramic Science and Engineering, Korea Advanced Institute of Science and Technology, 373-1 Kusong-dong, Yusong-gu, Taejon 305-701, Korea
Get access

Abstract

The discontinuous dissolution of oxide particles has been investigated in the Al2O3 -Fe2O3 system by changing oxygen partial pressure (PO2) and temperature. In PO2 change experiment, 95Al2O3-5Fe2O3 (in wt%) powder compacts were sintered at 1500°C in PO2=0.001 atm and then annealed at 1500°C in air. In temperature change experiment, 85Al2O3-15Fe2O3 (in wt%) powder compacts were sintered at 1600°C in air and then annealed at 1450°C in air. During annealing the sintered specimens, which contained corundum grains and iron aluminate spinel particles, the grain boundaries migrated concomitantly with the dissolution of spinel particles. A discontinuous dissolution of spinel precipitates thus occurred, when the grain boundary migration of alumina in a two phase mixture of corundum and spinel was induced by PO2 or temperature change. The present result would be a distinct observation of the discontinuous dissolution of precipitates in ceramic systems.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 357: Symposium C – Structure and Properties of Interfaces in Ceramics , 1994 , 319
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. King, A. H., Inter. Mater. Rev. 32, 173 (1987).Google Scholar
2. Yoon, D. Y., Annu. Rev. Mater. Sci. 19, 43 (1989).Google Scholar
3. Hillert, M. and Purdy, G. R., Acta Metall. 26, 333 (1978).Google Scholar
4. Cahn, J. W., Pan, J. D., and Balluffi, R. W., Scr. Metall. 13, 503 (1979).Google Scholar
5. Baik, Y. J. and Yoon, D. Y., Acta Metall. 38, 1525 (1990).Google Scholar
6. Sulonen, M. S., Acta Metall. 12, 749 (1964).Google Scholar
7. Sulonen, M. S., Acta Metall. 8, 669 (1960).Google Scholar
8. Pawlowski, A. and Truszkowski, W., Acta Metall. 38, 135 (1990).Google Scholar
9. Baik, Y. J. and Yoon, D. Y., Acta Metall. 33, 1911 (1985).Google Scholar
10. Lee, H. Y. and Kang, S.-J. L., Acta Metall. 38, 1307 (1990).Google Scholar
11. Lee, H. Y., Kang, S.-J. L., and Yoon, D. Y., Acta Metall. Mater. 41, 2497 (1993).Google Scholar
12. Lee, H.-Y., Kang, S.-J. L., and Yoon, D. Y., J. Am. Ceram. Soc. 77, 1301 (1994).Google Scholar
13. Lee, H.-Y., Lee, B.-K., Paek, Y.-K., and Kang, S.-J. L., J. Am. Ceram. Soc. (to appear).Google Scholar
14. Yoon, K. J. and Kang, S.-J. L., J. Am. Ceram. Soc. 76, 1641 (1993).Google Scholar
15. Jeon, J.-H. and Kang, S.-J. L., J. Am. Ceram. Soc. 77, 1688 (1994).Google Scholar
16. Jeong, J. W., Kim, D. Y., and Yoon, D. N., J. Am. Ceram. Soc. 73, 2063 (1990).Google Scholar
17. Choi, K., Cho, E.-S., and Kang, S.-J. L., J. Kor. Ceram. Soc. 29, 888 (1992).Google Scholar
18. Muan, A., in Phase Diagrams for Ceramists, Vol. 1, edited by The American Ceramic Society, Inc. (The American Ceramic Society, Inc., Columbus, 1964). p. 43.Google Scholar