Direct Fabrication of LiCoO2 Film Electrodes Using Soft Solution-Processing in LiOH Solution at 20 - 200°C

  • S.W. Song (a1), K.S. Han (a1), M. Yoshimura (a2), Y. Sato (a3) and A. Tatsuhiro (a3)...

Abstract

Application of Soft Solution-Processing, which is defined by environmentally friendly processing using (aqueous) solution, to the field of rechargeable lithium microbattery has been demonstrated by fabricating LiCoO2 film on the cobalt metal substrate in LiOH solution under hydrothermal condition. The film formation mecahnism could be interpreted in terms of chemical dissolution of cobalt metal plate in LiOH solution at fixed temperature of 20 - 200°C, resulting in the formation of H1−nCoO2 where n value increases with fabrication temperature and precipitation as LiCoO2 by heterogeneous nucleation on the substrate followed by crystal growth. The crystal structure and film properties have been characterized by X-ray diffraction, X-ray photoelectron, micro-Raman spectroscopic and scanning electron microscopic analyses. The films exhibited a good crystallinity despite the low reaction temperature without any postsynthesis annealing. The films prepared under different conditions showed different phase selection such as spinel (Fd3m) or hexagonal (R3-m), surface morphology and film thickness. An electrochemical activity of the LiCoO2 films was evidenced by cyclic voltammogram revealing a good reversibility on Li-intercalation and -deintercalation.

Copyright

References

Hide All
1 Kajiyoshi, K., Tomono, K., Hamaji, Y., Kasanami, T., and Yoshimura, M., J. Am. Ceram. Soc. 77, 2889 (1994).
2 Cho, W. S., Yashima, M., Kakihana, M., Kudo, A., Sakata, T., and Yoshimura, M., Appl. Phys. Lett. 66, 1027 (1995).
3 Yoshimura, M., J. Mater. Res. 13, 796 (1998).
4 Lee, S. J., Lee, J. K., Kim, D. W., and Baik, H. K., J. Electrochem. Soc. 143, L268 (1996).
5 Wang, C. B., Bates, J. B., Hart, F. X., Sales, B. C., Zhur, R. A., and Robertson, J. D., ibid., 143, 3203 (1996).
6 Striebel, K. A., Deng, C. Z., Wen, S. J., and Cairns, E. J., ibid., 143, 1821 (1996).
7 Wang, C. B., Bates, J. B., Hart, F. X., Sales, B. C., Zhur, R. A., and Robertson, J. D., ibid., 143, 3203 (1996).
8 Han, K. S., Krtil, P., and Yoshimura, M., J. Mater. Chem. 8, 2043 (1998).
9 Han, K. S., Song, S. W., and Yoshimura, M., Chem. Mater. 10, 2183 (1998).
10 Han, K. S., Song, S. W., and Yoshimura, M., J. Am. Ceram. Soc. 81, 2465 (1998).
11 Song, S. W., Han, K. S., and Yoshimura, M., ibid., submitted (1999).
12 Song, S. W., Han, K. S., Sasagawa, I., Watanabe, T., and Yoshimura, M., Solid State Ionics, submitted (1999).
13 Ohzuku, T., and Ueda, A., J. Electrochem. Soc. 141, 2972 (1994).
14 Gummow, R. J., Liles, D. C., and Thackeray, M. M., Mat. Res. Bull. 28, 235 (1993).
15 Fately, W. G. in Infrared and Raman Selection Rules for Molecular and Lattice Vibrations: The Correlation Method, Wiley-Interscience, New-York, 1972.
16 Huang, W., and Frech, R., Solid State Ionics, 86–88, 395 (1996)

Direct Fabrication of LiCoO2 Film Electrodes Using Soft Solution-Processing in LiOH Solution at 20 - 200°C

  • S.W. Song (a1), K.S. Han (a1), M. Yoshimura (a2), Y. Sato (a3) and A. Tatsuhiro (a3)...

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed