The Decomposition of Trimethylgallium and Trimethylaluminum on Si(100)

  • F. Lee (a1), T. R. Gow (a1), R. Lin (a1), A. L. Backman (a1), D. Lubben (a1) and R. I. Masel (a1)...

Abstract

The decomposition of trimethylgallium (TMG) and trimethylaluminum (TMA) on Si(100) is studied by TPD, XPS, and EELS. It is found that the decomposition of TMG is largely an intramolecular process. First one of the methyl groups in the TMG reacts with a hydrogen in another methyl group liberating methane. This leaves a CH2 group bound to the gallium which is seen clearly in EELS. Subsequently, another hydrogen reacts with a methyl group producing additional methane. This leaves a gallium atom and a CH group on the surface. Hydrogen desorbs, while carbon is incorporated into the growing film. Careful calibration of the peak areas in the TPD data indicates that 2.1 ± 0.3 moles of methane, 0.5 ± 0.03 moles of hydrogen, 1 mole of gallium, and 0.95 ± 0.1 moles of surface carbon are produced for every mole of TMG which decomposes. Since, the decomposition ratio is independent of the state of the surface, the surface orientation, and the level of impurities on the surface, it appears that the surface is not a direct participant in the reaction.

TMA adsorbs as dimers. However, the dimers decompose upon heating to 400 K. Thereafter, the chemistry of TMA decomposition is similar to that for TMG. Nonetheless, the product ratio varies with the TMA coverage, the state of the surface, and the aluminum coverage. Also, silicon-carbon bonds are evident at 600 K in EELS. It is suggested, therefore, that the decomposition of TMA is similar to that of TMG, except that methyl groups in TMA have a tendency to migrate to the support. In both TMA and TMG, carbon incorporation is an intrinsic part of the decomposition process. This suggests that TMA and TMG would not be appropriate source gases when one needs to produce films with very low carbon levels.

Copyright

References

Hide All
1. Lee, F., Gow, T. R., Masel, R. I., J. Electrochem Soc., to appear.
2. Lee, F., Backman, A. L., Lin, R., Gow, T. R., Masel, R. I., unpublished work.
3. Kvisle, S., Ryttle, E., Spectro. Acta, 40, 939 (1984).
4. Youshinobu, J., Tsuda, H., Onchi, M., Nishijima, M., J. Chem. Phys, 87, 7332 (1987).
5. Bellamy, L. J., The Infrared Spectra Of Complex Molecules, 3rd ed. Chapman and Hall, (1975).
6. Stroscio, J. A., Bare, S. R., Ho, W., Surface Scd. 154, 35 (1985).
7. Bourguignon, B., Carleton, K. L., Leone, S. R., Surface Sci. 204, 455 (1988).
8. Squire, D. W., Dulcey, C. S., Lin, M. C., Proc. Materials Research Soc. 54, 709 (1986).
9. Squire, D. W., Dulcey, C. S., Lin, M. C., Chem. Phys. Lett., 131, 112 (1986).
10. Squire, D. W., Dulcey, C. S., Lin, M. C., JVST B, 3, 1513 (1985).
11. Pütz, N., Heinecke, H., Weyers, M., Lüth, H., Balk, P., J. Crystal Growth, 74, 292 (1986).
12. DenBaars, S. P., Maa, B. Y., Dapkus, P. D., Danner, A. D., Lee, H. C., J. Crystal Growth, 77, 188 (1986).

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed